Basalt-fiber-reinforced plastic-bars-reinforced concrete beams (i.e., BFRP-RC beams) usually possess significant deformations compared to reinforced concrete beams due to the FRP bars having a lower Young’s modulus. This paper investigates the effects of adding steel fibers into BFRP-RC beams to reduce their deflection. Ten BFRP-RC beams were prepared and tested to failure via four-point bending under cyclic loading. The experimental variables investigated include steel-fiber volume fraction and shape, BFRP reinforcement ratio, and concrete strength. The influences of steel fibers on ultimate moment capacity, service load moment, and deformation of the BFRP-RC beams were investigated. The results reveal that steel fibers significantly improved the ultimate moment capacity and service load moment of the BFRP-RC beams. The deflection and residual deflection of the BFRP-RC beams reinforced with 1.5% by volume steel fibers were 48.18% and 30.36% lower than their counterpart of the BFRP-RC beams without fibers. Under the same load, the deflection of the beams increased by 11% after the first stage of three loading and unloading cycles, while the deflection increased by only 8% after three unloading and reloading cycles in the second and third stages. Finally, a new analytical model for the deflection of the BFRP-RC beams with steel fibers under cyclic loading was established and validated by the experiment results from this study. The new model yielded better results than current models in the literature.

Aramid fiber is a high-performance fiber with excellent mechanical properties, heat resistance, and corrosion resistance. Its exceptional shear and fatigue properties make it a promising material for civil engineering applications. This study summarizes the basic properties and current development of aramid fiber, as well as the applications of aramid fiber and its composites in civil engineering, including aramid fiber-reinforced composite (AFRP)-concrete/steel composite structures, AFRP rebars, and AFRP rock anchors. The results indicate that the poor interfacial bonding performance between aramid fibers and the resin matrix is the primary bottleneck restricting the application of AFRP composites in civil engineering. Consequently, developing a continuous surface treatment method suitable for industrial-scale production remains a key challenge for the widespread adoption of these composites. Furthermore, in certain specific working conditions and environments—such as seismic retrofitting of rectangular concrete columns, impact/explosion resistance reinforcement, and rock anchoring—AFRPs show the potential to replace traditional inorganic fiber-reinforced polymer composites. However, systematic investigation into the fundamental mechanical properties and long-term service performance of AFRP is still required prior to their practical application.

Steel fiber-reinforced concrete (SFRC) beams with fiber-reinforced polymer (FRP) bars are promising new composite structures. To investigate the durability of BFRP-SFRC beams, eleven beams were fabricated and conducted via four-point bending tests under cyclic loading. The experimental variables included BFRP reinforcement ratios, pre-cracked widths and environments (Natural or Seawater erosion). Experiment results revealed that the load–deflection curves of BFRP-SFRC beams showed bilinear growth. With the increase in loading and unloading cycles, the peak load and energy consumption of the tested beams decreased, and the impact of loading and unloading cycles on the flexural performances of the BFRP-SFRC beams enhanced with the increase in displacement. Under the same load, as the pre-crack width increases, the deflection of the BFRP-SFRC beam decreases. The deflection of the beam with a pre-crack width of 0.4 mm was 1.34 times than that of the beam without a pre-crack at the load of 100 kN. What is more, the pre-crack width had a bad effect on the energy consumed by the BFRP-SFRC beams. Compared with no pre-crack beam, the energy consumed by the beams with 0.02, 0.2 and 0.4 mm pre-crack width were decreased by 1.5%, 7.8% and 11.0% at the 18 mm displacement, respectively. Significantly, the effect of sea water erosion on the energy consumption of tested beams with high BFRP reinforcement ratios were smaller than that of tested beams with low BFRP reinforcement ratios. Finally, a calculation model of deformation of BFRP-SFRC beams under seawater erosion environments was proposed based on the effective moment of inertia methods. Compared with the existing calculation methods, this model was better correlated with the experimental results.