Radio frequency (RF) breakdown in the slow-wave structures (SWSs) is a crucial bottleneck restricting relativistic backward wave oscillator (RBWO) to pursuing higher output power and longer pulse width. This paper has experimentally studied the influence of thermal accumulation during repetitive operation on RF breakdown in an X-band RBWO. A method for cooling the SWSs using water flow has been proposed to restrain the temperature rise to some extent. Under different heat dissipation conditions, the operating states of the RBWOs exhibit great differences. The greater the distance between the water-cooling heat transfer channel and the SWSs, the more serious the pulse shortening of high-power microwave. Moreover, the breakdown traces appearing in the SWSs become more obvious with the worse convective heat transfer capacity. The observed experimental phenomena provide a new guideline that helps to enrich the mechanism of RF breakdown and to explore corresponding suppression methods in RBWO.

Field electron emission (FEE) is generally considered to be closely correlated with radio frequency (RF) breakdown in accelerating structures and high-power microwave (HPM) devices. In this study, the field emission characteristics of titanium are investigated by using a field emission test system. With the increase of the number of field emission tests and stability tests, the repeatability of the field emission characteristic curve of titanium tends to be better, and the amplitude of the current oscillation in the stability tests gradually decreases, indicating that the field emission performance of titanium gradually becomes stable. Subsequently, the field emission characteristic curve of titanium is analyzed by adopting the field emission theory of metal microprotrusions. Combined with the analysis of the electric field enhancement effects caused by the surface morphology, the dominant effect of the metal microprotrusions on the FEE of titanium is excluded from the two aspects of the electric field enhancement factor and local maximum emission current density. At last, the field emission theory of dielectric micropoints is introduced to analyze the field emission characteristics of titanium. The electric field enhancement factor of 10² ∼ 10³ are explained theoretically. Simultaneously, the reasonable effective emission area and local emission current density are given, which can better explain the field emission phenomena of titanium, such as the sharp decrease in emission current and repeatability of the field emission curve. Hence, it is revealed that the key factor that dominates the FEE of titanium is the dielectric impurities on the surface, rather than the metal microprotrusions.

Radio frequency (RF) breakdown can result in pulse shortening and severely limits the performance of the relativistic backward wave oscillator (RBWO). In this study, segmented slow-wave structure (SWS) rings, which can be observed directly using a scanning electron microscope without any post-processing, are used to study the breakdown in a RBWO. After undergoing high-power microwave experiments, the working surface of the SWS rings was found to exhibit corrugated morphologies at the sub-mm to mm scale, and a large number of craters in the vicinity of the corrugated morphologies and a mass of scattered droplets were visible on the surface. It was deduced that the unusual morphologies resulted from electron bombardment of the working surface. The observed structures and droplets provide new evidence that helps to explain the mechanism for RF breakdown in the RBWO.

In this paper, two kinds of Be/2024Al composites were prepared by the pressure infiltration method using two different beryllium powders as reinforcements and 2024Al as a matrix. The effect of interfacial strength on the mechanical behavior of Be/2024Al composites was studied. Firstly, the microstructure and mechanical properties of the two composites were characterized, and then the finite element analysis (FEA) simulation was used to further illustrate the influence of interfacial strength on the mechanical properties of the two Be/2024Al composites. The mechanical tensile test results show that the tensile strength and elongation of the beryllium/2024Al composite prepared by the blocky impact grinding beryllium powder (blocky-Be/2024Al composite) are 405 MPa and 1.58%, respectively, which is superior to that of the beryllium/2024Al composite prepared by the spherical atomization beryllium powder (spherical-Be/2024Al composite), as its strength and elongation are 331 MPa and 0.38%, respectively. Meanwhile, the fracture of the former shows brittle fracture of beryllium particles and ductile fracture of aluminum, while the latter shows interface debonding. Further FEA simulation illustrates that the interfacial strength of the blocky-Be/2024Al composite is 600 MPa, which is higher than that of the spherical-Be/2024Al composite (330 MPa). Therefore, it can be concluded that the better mechanical properties of the blocky-Be/2024Al composite contribute to its stronger beryllium/aluminum interfacial strength, and the better interfacial strength might be due to the rough surface and microcrack morphology of blocky beryllium particles. These research results provide effective experimental and simulation support for the selection of beryllium powder and the design and preparation of high-performance beryllium/aluminum composites.

An $\textit{X}$ -band superradiant relativistic backward-wave oscillator (RBWO) operating at a low magnetic field with power conversion efficiency exceeding unity is proposed. The device efficiency is improved from two aspects: beam transmission stability focused by a low guiding magnetic field and microwave transmission efficiency. First, a gradually decaying axial magnetic field is applied. It could not only suppress the initial radial oscillation amplitude of the electron beam envelope but also transform the high transverse momentum of electrons into the axial momentum, which is beneficial to the beam–wave interaction Second, a novel structure with a front extractor is introduced. The backward wave is extracted into a coaxial channel outside the slow wave structure (SWS) and transmitted in TEM mode to avoid the power loss of the reflected microwave in the SWS caused by the dispersion effects. Particle-in-cell (PIC) simulation results reveal that when the intense relativistic electron beam (IREB) propagating in a 36-period superradiance-RBWO (SR-RBWO) is confined with a magnetic induction intensity that decreases from 0.81 T in cathode region to 0.43 T in interaction region, the output power of 1.04 GW corresponding to conversion factor $\textit{K}$ $=$ 1.55 can be obtained. The merits of low-magnetic-field operation and high efficiency make this tube a promising device used for the miniaturization of high-power SR systems.

The change in material dimensional will lead to the decline of instrument accuracy and reliability. In this paper, the characterization and analysis of the lattice constant, precipitates, and dislocation density of the material by X-ray diffraction (XRD) and transmission electron microscopy (TEM) reveals the reason why the relative dimensional change in the rolled 2024Al is one order of magnitude lower than that of the as-cast 2024Al during isothermal aging. Compared with as-cast 2024Al, the dislocation density of rolled 2024Al is higher, the lattice constant decreases less before and after aging, and the precipitates have orientation and more content, resulting in the dimensional change in rolled 2024Al being smaller than that of as-cast 2024Al. In addition, two main reasons for decreasing the dimensional change in rolled 2024Al are discussed: the decrease in lattice constant, the formation and growth of the S phase before and after aging.