In recent years, China is increasingly dependent on imported wood. Afrormosia and Newtonia are some of the imported species with good utilization potential. However, both of them also have problems with poor dimensional stability. In order to make better use of these two types of wood, the influence of heat treatment under air and palm oil conditions on the color, dimensional stability, and hygroscopicity of Afrormosia and Newtonia was investigated. The Afrormosia and Newtonia wood samples were heated in air or palm oil medium for two hours at 160 °C, 180 °C and 200 °C, respectively. Then, the color, weight changes, swelling, moisture absorption and chemical structure were evaluated for each case. As results, the heat treatments with air or palm oil increased the dark color of Newtonia and Afrormosia wood and this increase was proportional to the treatment temperature. The tangential and radial swelling coefficient for air heat treatment of Afrormosia wood at 200 °C were, respectively, reduced by 24.59% and 19.58%, while this reduction for Newtonia was 21.32% and 14.80%. The heat treatment in palm oil further improved the stability and hygroscopicity of the wood, showing that the Afrormosia samples treated by palm oil at 200 °C underwent a decrease of its tangential and radial swelling coefficient, respectively, by 49.34% and 45.88%, whereas the tangential and radial swelling coefficient of Newtonia treated under the same conditions were reduced by 42.85% and 33.63%, respectively. The heat treatments of Afrormosia and Newtonia samples under air at 200 °C diminished the water absorption by 21.67% and 22.12%. The water absorption of Afrormosia and Newtonia heat-treated under palm oil at 200 °C was reduced, respectively, by 39.40% and 37.49%. Moreover, the FTIR analysis showed the decrease of hydroxyl groups in proportion to the wood treatment temperature.

With China's increasing dependence on foreign wood, African wood has gradually become a potential imported species, but its use is seriously affected by problems such as unpleasant odors. In this study, we investigate the effect of heat treatment medium on odor-causing VOCs, decomposition of structural polymers, Modulus of Rupture (MOR) and Modulus of Elasticity (MOE) of hardwood. Samples of “Afrormosia” and “Newtonia” wood were heated under air and palm oil for two hours at 160 °C, 180 °C, and 200 °C, respectively. Then, the nature of the odor of each VOC emitted by the wood before and after heat treatment was identified using the GCMS method. The decomposition of hemicelluloses, cellulose and lignin in wood samples was examined using a ThermoGravimetric Analyzer coupled to Fourier Transform InfraRed spectrometry (TGA-FTIR). The 3-point bending test was used to evaluate MOR and MOE. The results indicate that the main VOCs responsible for unpleasant smells are acetic acid and hexanal; the reduction in hexanal emissions after heat treatment is mainly due to the treatment temperature, while the reduction in acetic acid emissions depends on the heat treatment medium and is due to the chemical interactions between palm oil and acetic acid; thus, the heat treatment under palm oil reduces the percentage area of VOCs with unpleasant odors in Afrormosia and Newtonia wood better than the heat treatment under air. Based on TGA-3D FTIR analysis and mechanical results, the reduction in MOR is greater in heat treatment under air because the said treatment induces a greater loss of woody matter, which was characterized by higher H₂O and CO emissions during heat treatment of wood under palm oil than during heat treatment of wood under air. On the other hand, palm oil more than air, promotes lignin deacetylation, which is characterized by the fact that the 1050 cm⁻¹ wavelength peak was far higher in samples treated with palm oil than in those treated under air; and this might explain why heat treatment under palm oil reduces MOE more than heat treatment under air.

The objective of this work was to study the influence of palm oil on the VOCs emitted during the heat treatment of Afromosia (Pericopsis Elata Van Meeuwen) and Newtonia (Newtonia paucijuga Harms) wood by comparing to the VOCs emitted during the heat treatment under air. Two batches of Afrormosia and Newtonia wood samples were heated under air and palm oil at temperatures of 160 °C, 180 °C, and 200 °C for 2 h. Then, the VOCs were collected by Solid Phase Micro Extraction (SPME) and measured using a Gas Chromatograph and Mass Spectrometer (GC-MS). The results showed that the temperature, the wood species, and the treatment medium have a great influence on the categories and percentages of VOCs emitted. In the air heat treatment, ethers were the most emitted VOCs from Afrormosia and Newtonia when these woods were thermally treated at 160 °C. Newtonia treated under air at 180 °C emitted more esters, while Afrormosia continued to emit more ethers under the same conditions. Moreover, Afrormosia and Newtonia treated at 200 °C emitted more ketones and aldehydes, respectively. Regarding the heat treatment of Afrormosia and Newtonia wood under palm oil, a similarity of the VOCs emitted from Newtonia with those emitted from Afrormosia under the same conditions was observed. Furthermore, palm oil was the main factor conditioning the nature of the VOCs emitted during the heat treatment. In general, for the treatment of Afrormoshia wood with palm oil, the VOCs emitted, such as alcohols, alkanes, and ethers, decreased with the treatment temperature. Ethers and ketones increased with the processing temperature. At 160 °C and 180 °C, the percentage of aldehydes was highest, while, at 200 °C, the percentage of esters was highest. Similarly, for Newtonia treated under palm oil, adehydes, ethers, and alcohols were the most abundant VOCs emitted at 160 °C. However, their percentages decreased with the increase in the treatment temperature; on the contrary, esters and ketones were weakly emitted at 160 °C and became abundant with the increase in temperature. Additionally, the ethers formed during the heat treatment of Afrormosia and Newtonia wood treated under air carry acetyl groups, while those formed during the treatment of the said wood under palm oil carry hydroxyl groups.

This study investigates the synergistic effect of phenolic resin impregnation on the mechanical and adhesive properties of hydrothermally treated bamboo composites further reinforced with a silica nanoparticle sol–gel catalyzed by Fe₃O₄ (SiO₂/Fe₃O₄). The hydrothermal pre-treatment was found to enhance cellulose crystallinity, as confirmed through XRD analysis. Dynamic mechanical analysis (DMA) and nanoindentation tests revealed that the hybrid treatment significantly influences the viscoelastic response. Composites treated only with hot water and resin (GB-W) exhibited superior short-term creep resistance and higher elasticity, attributed to their optimized crystalline structure. In contrast, the silica-reinforced composites (GB-M) demonstrated the most viscous behavior and lowest stress relaxation, making them most effective at minimizing elastic springback. Nanoindentation further showed that GB-W had the highest nano-adherence at the fiber cell wall level. FTIR analysis indicated a stronger interaction between the phenolic resin and the hydroxyl groups of the bamboo matrix in GB-0 and GB-W compared to GB-M, where the silica layer potentially altered this interface. Microscopy confirmed a resin penetration depth of at least 1 mm, primarily into porous tissues. The results demonstrate that while silica reinforcement enhances relaxation properties, the hydrothermal pre-treatment combined with phenolic resin creates a more favorable interface, leading to better overall creep resistance and adherence.

As a promising construction material combining high strength with renewability, bamboo’s natural form restricts its applications. While thermal bending enhances versatility, it alters mechanical performance. This study examines how liquid-water heating and temperature influence rheological and mechanical behavior, particularly creep, relaxation, and flexural properties. Key insights reveal: immersion heating reduces Tg to 38°C via aqueous plasticization; density increases up to 45% through hydrothermal absorption; temperature-dependent MOR reductions (≤ 30%); 40% stiffness loss coupled with 70% ductility gain, optimizing bendability; water-heated bamboo exhibited lower creep than control samples; The relaxation modulus decreases with heating temperature, asymptotically around 90°C. The fractional Maxwell model effectively quantified creep and relaxation behavior. Model parameter analysis revealed that water heating enhances ductility at the expense of strength. This approach provides an alternative framework for analyzing and optimizing bamboo bending parameters.