Ru catalysts supported on activated carbon obtained by hydrothermal treatment of rice husk were evaluated in the hydrogenation reaction of levulinic acid to γ-valerolactone. The hydrothermally treated carbon was characterized by nitrogen physisorption, elemental analysis, and thermogravimetric analysis, and the catalysts were characterized by FTIR spectroscopy, X-ray photoelectron spectroscopy, temperature-programmed reduction, and temperature-programmed desorption of pyridine (acidic properties). Prior to the reaction, the catalysts were reduced at different temperatures in the range of 100–350 °C to evaluate the effect of the reduction temperature on the performance in the hydrogenation of levulinic acid. The reaction was carried out in a batch reactor at 70 °C and 1.5 MPa. The results of conversion and selectivity to γ-valerolactone showed that the catalyst with the best performance was the sample reduced at 200 °C. After 2 h of reaction, a γ-valerolactone yield of 74% was achieved. This catalyst presented the lowest acidity value, and the ruthenium-containing phase consisted mainly of RuO₂, with a small portion of Ru⁰. The solid catalyst can be recovered and successfully reused for three runs with the GVL yield at 56%.

Ruthenium (1 wt%) catalysts supported on alumina doped with alkaline (Na and K) and alkaline earth metals (Ba, Ca, and Mg) of different concentrations (1, 5, and 10 wt%) were tested in the dry reforming of methane. All catalysts were prepared by the successive impregnation method. Supports were characterized by X-ray diffraction, BET surface area, temperature-programmed desorption of CO_2, and 2-propanol dehydration. Additionally, catalysts were characterized by temperature-programmed reduction (TPR), temperature-programmed oxidation (TPO), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). Stability tests to study coke deposition were performed using long-time dry reforming reactions. All the catalysts showed good catalytic activity, and activity falls were never detected. Ru metallic phase seemed to be resistant to coke formation even though its particles are sintered during a long-term reaction.