The removal of lead metals from wastewater was carried out with carbon microspheres (CMs) prepared from date palm leaflets using a hydrothermal carbonization process (HTC). The prepared CMs were subsequently activated with phosphoric acid using the incipient wetness impregnation method. The prepared sample had a low Brunauer–Emmet–Teller (BET) surface area of 2.21 m²·g⁻¹, which increased substantially to 808 m²·g⁻¹ after the activation process. Various characterization techniques, such as scanning electron microscopy, BET analysis, Fourier transform infrared, and elemental analysis (CHNS), were used to evaluate the morphological structure and physico-chemical properties of the CMs before and after activation. The increase in surface area is an indicator of the activation process, which enhances the absorption properties of the material. The results demonstrated that the activated CMs had a notable adsorption capacity, with a maximum adsorption capacity of 136 mg·g⁻¹ for lead (II) ions. This finding suggests that the activated CMs are highly effective in removing lead pollutants from water. This research underscores the promise of utilizing activated carbon materials extracted from palm leaflets as an eco-friendly method with high potential for water purification, specifically in eliminating heavy metal pollutants, particularly lead (II), contributing to sustainability through biomass reuse.

In this work, carbon microspheres (CMs) were prepared by hydrothermal carbonization (HTC) of inedible crystallized date palm molasses. The effects of temperature and reaction time on the prepared materials were studied. Experiments were carried out at different temperatures (180, 200, 230 and 250 °C) with reaction times ranging from 2 to 10 h. It was found that temperature had the greatest influence on the mass yield of the CMs. No solid products were observed at a temperature of 180 °C and a reaction time less than 2 h. The highest yield was found to be 40.4% at 250 °C and a reaction time of 6 h. The results show that the CMs produced were approximately 5–9 μm in diameter. The results also show that the largest diameter of the CMs (8.9 μm) was obtained at a temperature of 250 °C and a reaction time of 6 h. Nonetheless, if the reaction time was extended beyond 6 h at 250 °C, the CMs fused and their shapes were deformed (non-spherical shapes). The synthesized materials were characterized using Scanning Electron Microscopy (SEM), Fourier Transform Infrared (FTIR), Branuer-Emmett-Teller (BET) and thermogravimetric analysis (TGA). BET surface areas for the four samples were found to be less than 1 m²/g. The methylene blue adsorption studies indicated that the equilibrium adsorption capacity was reached after 15 min, with a maximum adsorption capacity of 12 mg/g. The recycling of date palm molasses (a known processed waste) to generate a useable carbon microsphere represents a beneficial step in the application of sustainable processing industries in the Middle East.