The different nature of the effect of hydrogen on the tribological behavior of two carbon steels (st. 45 and st. U8) upon their contact with super solid plasma electrolytic oxidation (PEO) layers synthesized on two light alloys (AMg-6 and D16T alloys as the analogists of the A 95556 UNS USA and AA2024 ANSI USA alloys correspondently) was investigated in the medium of mineral oil of the I-20 type. To compare the effect of hydrogenation on the tribological properties of the analyzed contact pairs, similar tests were also performed on the same mineral oil with clear water or an aqueous solution of glycerine added to its content. A spinel-type film (hercynite) was formed upon friction of two contacting surfaces—the iron-carbon steels and PEO layers synthesized on the AMg-6 alloy. This film was a reliable protection against wear of the surface subjected to the effect of hydrogen. When steels came into contact with the PEO layers synthesized on the D16T alloy, surface protection against wear was ensured by another mechanism. The phenomenon of selective metal transfer in the friction zone (from one to another friction surfaces) was revealed.

The microhardness and abrasive wear resistance of cast Al-Si alloys after plasma-electrolytic oxidation (PEO) in a weakly alkaline basic electrolyte (3 g/L KOH + 2 g/L Na₂SiO₃), as well as with the addition of H₂O₂, were determined. X-ray analysis showed that the PEO layer comprises two oxide phases, namely α-Al₂O₃ and γ-Al₂O₃, as well as sillimanite -Al₂O₃ · SiO₂ and a small percentage of mullite -3 Al₂O₃ · 2SiO₂. Silicon is present in the structure of the oxide layer, and its percentage is greater than that of the alloys in their initial state. It has been shown that the characteristics of PEO layers on AK9 and AK12 silumins synthesized in an electrolyte of basic composition increase (microhardness up to 900–1000 HV and abrasive wear resistance by 14–57 times). The formation of PEO layers in the base electrolyte with the addition of 3 g/L of hydrogen peroxide intensifies the synthesis process and promotes the formation of high-temperature oxide phases (in particular, corundum). The abrasive wear resistance of both silumins with PEO layers synthesized in such an electrolyte increases by 30–70%.