Purpose of Review: Fractures of osteoporotic bone in elderly individuals need special attention. This manuscript reviews the current strategies to provide sufficient fracture fixation stability with a particular focus on fractures that frequently occur in elderly individuals with osteoporosis and require full load-bearing capacity, i.e., pelvis, hip, ankle, and peri-implant fractures. Recent Findings: Elderly individuals benefit immensely from immediate mobilization after fracture and thus require stable fracture fixation that allows immediate post-operative weight-bearing. However, osteoporotic bone has decreased holding capacity for metallic implants and is thus associated with a considerable fracture fixation failure rate both short term and long term. Modern implant technologies with dedicated modifications provide sufficient mechanical stability to allow immediate weight-bearing for elderly individuals. Depending on fracture location and fracture severity, various options are available to reinforce or augment standard fracture fixation systems. Summary: Correct application of the basic principles of fracture fixation and the use of modern implant technologies enables mechanically stable fracture fixation that allows early weight-bearing and results in timely fracture healing even in patients with osteoporosis.

Background: Ipsilateral revision surgeries of total hip or knee arthroplasties due to periprosthetic fractures or implant loosening are becoming more frequent in aging populations. Implants in revision arthroplasty usually require long anchoring stems. Depending on the residual distance between two adjacent knee and hip implants, we assume that the risk of interprosthetic fractures increases with a reduction in the interprosthetic distance. The aim of the current study was to investigate the maximum strain within the femoral shaft between two ipsilateral implants tips. Methods: A simplified physical model consisting of synthetic bone tubes and metallic implant cylinders was constructed and the surface strains were measured using digital image correlation. The strain distribution on the femoral shaft was analyzed in 3-point- and 4-point-bending scenarios. The physical model was transferred to a finite element model to parametrically investigate the effects of the interprosthetic distance and the cortical thickness on maximum strain. Strain patterns for all parametric combinations were compared to the reference strain pattern of the bone without implants. Results: The presence of an implant reduced principal strain values but resulted in distinct strain peaks at the locations of the implant tips. A reduced interprosthetic distance and thinner cortices resulted in strain peaks of up to 180% compared to the reference. At low cortical thicknesses, the strain peaks increased exponentially with a decrease in the interprosthetic distance. An increasing cortical thickness reduced the peak strains at the implant tips. Conclusions: A minimum interprosthetic distance of 10 mm seems to be crucial to avoid the accumulation of strain peaks caused by ipsilateral implant tips. Interprosthetic fracture management is more important in patients with reduced bone quality.

Background: Acromial Levy III fractures after inverse shoulder arthroplasty occur in up to 7% of patients. To date, it is not clear how these fractures should be treated as clinical outcomes remain unsatisfactory. The aim of this study was to evaluate the biomechanical performance of three different plating methods of type III acromion fractures. Methods: Levy III fractures in synthetic scapulae were fixed with three different methods. Angular stable locking plates were placed on the spina scapula to bridge the fracture either dorsally, caudally, or on both aspects by double plating. In a biomechanical experiment, the pull of the deltoid muscle at 40° abduction of the arm was simulated by cyclic loading with increasing load levels until failure. Failure load, cycles to failure, and fragment motions were evaluated. Results: The results showed that double plating (350 ± 63 N) withstood the highest loads until failure, followed by dorsal (292 ± 20 N) and caudal (217 ± 49 N) plating. Similarly, double plating showed significantly smaller fragment movement than the other two groups. Conclusions: Double plating appeared to provide the largest biomechanical stability in type III acromion fracture under arm abduction. Caudal plating in contract resulted in insufficient fracture stability and early failure and can thus not be recommended from a biomechanical point of view.

Vertebral augmentation techniques are used to stabilize impacted vertebrae. To minimize intraoperative risks, a solid education of surgeons is desirable. Thus, to improve education of surgeons as well as patient safety, the development of a high-fidelity simulator for the surgical training of cement augmentation techniques was initiated. The integrated synthetic vertebrae should be able to provide realistic haptics during all procedural steps. Synthetic vertebrae were developed, tested and validated with reference to human vertebrae. As a further reference, commercially available vertebrae surrogates for orthopedic testing were investigated. To validate the new synthetic vertebrae, characteristic mechanical parameters for tool insertion, balloon dilation pressure and volume were analyzed. Fluoroscopy images were taken to evaluate the bone cement distribution. Based on the measurement results, one type of synthetic vertebrae was able to reflect the characteristic parameters in comparison to human vertebrae. The different tool insertion forces (19.7 ± 4.1, 13.1 ± 0.9 N, 1.5 ± 0.2 N) of the human reference were reflected by one bone surrogate (11.9 ± 9.8, 24.3 ± 3.9 N, 2.4 ± 1.0 N, respectively). The balloon dilation pressure (13.0 ± 2.4 bar), volume (2.3 ± 1.5 ml) of the synthetic vertebrae were in good accordance with the human reference (10.7 ± 3.4 bar, 3.1 ± 1.1 ml). Cement application forces were also in good accordance whereas the cement distribution couldn’t be reproduced accurately. Synthetic vertebrae were developed that delivered authentic haptics during transpedicular instrument insertion, balloon tamp dilation and bone cement application. The validated vertebra model will be used within a hybrid simulator for minimally invasive spine surgery to educate and train surgeons.