In this study, the effects of Cu addition on artificial age hardening behavior and mechanical properties of Al-1.2Mg-1.2Si-(xCu) alloy was investigated quantitatively and qualitatively by Vickers hardness, tensile test, and transmission electron microscope. The results indicated that Cu addition enhanced the aging response of the alloy at 175 °C. With the increase in Cu content, the time for the alloys to reach peak aging decreased from 12 h to 10 h and 8 h. The tensile strength of the alloy was obviously improved with Cu added in which was 421 MPa of 0Cu alloy, 448 MPa of 0.18Cu alloy, and 459 MPa of 0.37Cu alloy. The results of TEM observation revealed that the addition of 0.37Cu changed the aging precipitation sequence of the alloy, in which the precipitation sequence of 0Cu and 0.18Cu alloy was SSSS→GP zones/pre-β″→β″→β″ + β′, 0.37Cu alloy was SSSS→GP zones/pre-β″→β″ + L→β″ + L + Q′. Moreover, with the addition of Cu, the number density and volume fraction of precipitates of the Al-1.2Mg-1.2Si-(xCu) alloy was evidently increased. The number density was increased from 0.23 × 10²³/m³ to 0.73 × 10²³/m³ in the initial aging stage and from 1.9 × 10²³/m³ to 5.5 × 10²³/m³ in the peak aging stage. The volume fraction was increased from 0.27% to 0.59% in the early aging stage and from 4.05% to 5.36% in the peak aging stage. It indicated that Cu addition promoted the precipitation of strengthening precipitates and boosted the mechanical properties of the alloy accordingly.

In the present study, the effects of varying heating and cooling rates during the solution treatment process on the microstructure and properties of AA7050 alloy wires were investigated using tensile tests, metallographic microscopy, electron backscattered diffraction, and transmission electron microscopy. It was found that the recrystallized grain size of the alloy, subjected to method of rapid heating, exhibited a smaller and more uniform distribution in comparison to method of slow heating. The low density of η′ strengthening phases after the artificial aging treatment was formed using air cooling method. Meanwhile, by using the water quenching method sufficient solute atoms and more nucleation sites were provided resulting in a large number of η′ strengthening phases being formed. In addition, the alloy processed using the water quenching method displayed higher strength than that treated using the air cooling method for the T6 and T73 states. Furthermore, coarse precipitates formed and less clusters were observed in the matrix, while high density nanoscale clusters and no continuous precipitation are formed when using the water quenching method.

The effect of trace Sc and Zr on grain refinement of Al-5.0Mg-3.0Zn as-cast alloy was investigated by optical microscopy and scanning electron microscopy with EDS. The results indicated that the critical quantities of Sc and Zr for Al-Mg-Zn alloy to produce a significant refining effect were determined and the total mass fraction of Sc and Zr was not less than 0.27, and the mass fraction of Sc was more than 0.13. The average grain size of the as-cast alloy ranged from 30 to 44 μm. The as-cast microstructure refinement of the alloy was related to the number density of Al₃(Sc, Zr) particles and the critical nucleation work of grains. Furthermore, based on first-principles calculations, the formation enthalpies of different Al₃(Sc, Zr) particles and the interface stabilities have been theoretically discussed. The experimental phenomenon of increasing the particle number by the simultaneous addition of Sc and Zr was well explained. Thus, this investigation presented a better insight into the grain refining mechanism from experiments and theoretical calculations.

In this work, the effects of the Cu/Li ratio on the mechanical properties and corrosion behavior of Sc-containing Al-Cu-Li alloys were systematically investigated by utilizing age-hardening behavior, tensile property, corrosion behavior, and electrochemical behavior, complemented by microstructural characterization through EBSD and TEM. The results show that the peak aging strength of the alloys remained relatively consistent but slightly decreased with the decrease in Cu/Li ratio, and the yield strengths were 585 MPa, 578 MPa, and 573 MPa, respectively. The changes in the Cu/Li ratio caused different matching patterns of precipitates in the peak aging alloys. The cumulative precipitation strengthening by T₁, θ′, δ′, and S′ phases are equal within the alloys with different Cu/Li ratios. However, the strength contribution of the T₁ phase decreases from 81% to 66% with the decrease in the Cu/Li ratio. Concurrently, the precipitates of LAGBs gradually increase in number and are continuously distributed, and the precipitates of HAGBs become larger in size with lower Cu content as the Cu/Li ratio decreases, all of which leads to a weakening of the intergranular corrosion (IGC) resistance within the low Cu/Li ratio alloy.

The 7085 aluminum alloy with a low Cu content is an important lightweight structural material in the aerospace field due to its advantages of low density, high specific strength, and high hardenability. However, like other high-strength Al-Zn-Mg-Cu alloys, this alloy is susceptible to stress corrosion cracking (SCC). Additionally, the lower Cu content may increase its tendency toward SCC, potentially impacting the safe use of this alloy. Therefore, this study investigated the effects of aging treatment processes on the mechanical properties and SCC resistance of 7085 aluminum alloy. And the factors affecting the properties of the alloy were analyzed by optical microscope (OM), scanning transmission electron microscope (STEM), and energy-dispersive X-ray spectroscopy (EDS) analyses. The results indicated that increasing the secondary aging temperature and adding a tertiary aging step can significantly reduce the alloy’s susceptibility to SCC while meeting the mechanical performance requirements. The reduced SCC sensitivity was mainly attributed to the increased spacing of grain boundary precipitates, a wider precipitate-free zone at the grain boundaries, and a higher Cu content in the grain boundary precipitates.