Fiber-reinforced polymer (FRP) composites have gained increasing recognition and application in the field of civil engineering in recent decades due to their notable mechanical properties and chemical resistance. However, FRP composites may also be affected by harsh environmental conditions (e.g., water, alkaline solutions, saline solutions, elevated temperature) and exhibit mechanical phenomena (e.g., creep rupture, fatigue, shrinkage) that could affect the performance of the FRP reinforced/strengthened concrete (FRP-RSC) elements. This paper presents the current state-of-the-art on the key environmental and mechanical conditions affecting the durability and mechanical properties of the main FRP composites used in reinforced concrete (RC) structures (i.e., Glass/vinyl-ester FRP bars and Carbon/epoxy FRP fabrics for internal and external application, respectively). The most likely sources and their effects on the physical/mechanical properties of FRP composites are highlighted herein. In general, no more than 20% tensile strength was reported in the literature for the different exposures without combined effects. Additionally, some provisions for the serviceability design of FRP-RSC elements (e.g., environmental factors, creep reduction factor) are examined and commented upon to understand the implications of the durability and mechanical properties. Furthermore, the differences in serviceability criteria for FRP and steel RC elements are highlighted. Through familiarity with their behavior and effects on enhancing the long-term performance of RSC elements, it is expected that the results of this study will help in the proper use of FRP materials for concrete structures.

Fiber-reinforced polymer (FRP) composites offer a corrosion-resistant, lightweight, and durable alternative to traditional steel material in concrete structures. However, the lack of established inspection methods for assessing reinforced concrete elements with externally bonded FRP (EB-FRP) composites hinders industry-wide confidence in their adoption. This study addresses this gap by investigating non-destructive testing (NDT) techniques for detecting damage and defects in EB-FRP concrete elements. As such, this study first identified and categorized potential damage in EB-FRP concrete elements considering where and why they occur. The most promising NDT methods for detecting this damage were then analyzed. And lastly, experiments were carried out to assess the feasibility of the selected NDT methods for detecting these defects. The result of this study introduces infrared thermography (IR) as a proper method for identifying defects underneath the FRP system (wet lay-up). The IR was capable of highlighting defects as small as 625 mm² (1 in.²) whether between layers (debonding) or between the substrate and FRP (delamination). It also indicates the inability of GPR to detect damage below the FRP laminates, while indicating the capability of PAU to detect concrete delamination and qualitatively identify bond damage in the FRP system. The outcome of this research can be used to provide guidance for choosing effective on-site NDT techniques, saving considerable time and cost for inspection. Importantly, this study also paves the way for further innovation in damage detection techniques addressing the current limitations.

Fiber-Reinforced Polymer (FRP) bars/strands are the most promising alternative to their steel counterparts for reinforcing concrete elements due to their resistance to corrosion, lighter weight, higher strength and better durability. However, very limited research has been conducted in relation to non-destructive testing (NDT) methods that are applicable to damage detection in FRP bars or the detection of FRP reinforcements embedded in concrete. The ability to assess the condition of the relatively new and unique FRP reinforcements will increase the confidence of the construction industry in their use as a reliable substitute for steel reinforcements. This paper investigates the ability of two of the most commonly used NDT methods, Ground Penetrating Radar (GPR) and Phased Array Ultrasonic (PAU), in detecting FRP bars/strands embedded in concrete elements. GPR and PAU tests were performed on two slab specimens reinforced with GFRP (Glass-FRP) bars, the most commonly used FRP bar, with variations in their depth, size and configuration, and a slab specimen with different types of available FRP reinforcements. The results show that GPR devices can detect GFRP bars/strands and CFRP (Carbon-FRP) strands to some extent, and their detectability increases with the increase in their antenna center frequency. On the contrary, PAU is only capable of detecting GFRP and CFRP strands. The results of this paper also emphasize the need for further research and developments related to NDT applications to embedded FRP bars.