In order to realize the construction of environmentally friendly potassium sodium niobate ceramic coating on metal surface, potassium sodium niobate ceramic coating was prepared by supersonic plasma spraying technology. The morphology, element extension and phase structure of such coating were investigated. The dielectric and ferroelectric properties were also analyzed. The results show that the coating has good quality and tetragonal phase structure. When test frequency ≥ 2 MHz, the dielectric constant is stable at about 300, and also dielectric loss is stable at about 0.05. The coating exhibits good hysteresis loops under different applied electric fields. When the applied electric field is 16 KV/cm, residual polarization value of as-prepared coating reaches 17.02 μC·cm⁻².

Copper (Cu)-based composite coatings have been widely applied in all kinds of important industry fields due to their outstanding comprehensive properties. The preparation temperature of a composite coating is the key factor affecting the properties, so the cold spray (CS) technology is characterized by low-temperature solid-state deposition, which ensures its emergence as the most promising technology for preparing the Cu-based composite coatings. In this paper, first, the principle of CS technology and the deposition mechanism of the coatings are introduced. On this basis, the deposition mechanism of Cu-based metal/ceramic composite coatings is further explored. Secondly, the effects of key CS process parameters (particle velocity, particle morphology, and substrate state) on the quality of the Cu-based composite coatings are summarized, and the current research status of cold-sprayed Cu-based composite coatings in the fields of corrosion resistance, wear resistance, self-lubricating properties, and electrical conductivity is reviewed. Moreover, the improvement of the performance of Cu-based composite coatings by various post-process treatments of coatings, such as heat treatment (HT) and friction stir processing (FSP), is elaborated. Finally, the future development of Cu-based composite coatings and CS technology is prospected.

Thermal control coating is an important means of ensuring that a spacecraft remains operational at high temperatures. Due to limitations regarding preparation technology and material properties, the mechanical properties of the conventional thermal control coatings still need to be improved. To solve this problem, nanostructured alumina coatings (NCs) and conventional alumina coatings (CCs) were prepared using plasma-spraying technology. The microscopic morphology, phase structure, hardness, and thermal control properties (solar absorptance (α_s) and emissivity (ε)) of the nanostructured alumina coatings were investigated and compared with those of conventional alumina coatings. The results show that the NC has a higher hardness value (1168.8 HV) and that its reflectivity exceeds 75% in the wavelength range of 446–1586 nm, while a high degree of emissivity of 0.863–0.87 is still maintained at 300–393 K. Furthermore, the results show that these highly reflective properties are related to the phase composition and internal micromorphology of the NC, whereby the solar absorption of the coating is reduced due to the increase in the alpha phase content (21.4%), the high porosity (5.21%) and the nanoparticles favoring the internal scattering. All these properties can improve the performance of this CC coating with low solar absorptance (α_s) and high emissivity (ε).

Conventional carburizing has disadvantages, such as high energy consumption, large deformation of parts, and an imperfect structure of the carburizing layer. Hence, a rare earth ion pre-implantation method was used to catalyze and strengthen the carburized layer of 20Cr2Ni4A alloy steel. In this study, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive microanalysis (EDS), transmission electron microscopy (TEM), and Rockwell/Vickers hardness testing were used to analyze the microstructure, phase composition, retained austenite content, hardness, carburized layer thickness, and carbon diffusion. The results showed that lanthanum and yttrium ions implanted into the 20Cr2Ni4A steel formed solid solutions of rare earth ions and a large number of dislocations, which improved the diffusion coefficient of carbon elements on the carburized surface and the uniformity of the carbon distribution. Simultaneously, rare earth ion implantation improved the structure and hardness of the vacuum carburized layer. Compared to the lanthanum ion implantation, yttrium ion implantation caused the structure of the carburized layer to be finer, and the carbon diffusion coefficient increased by 1.17 times; in addition, the surface hardness of the carburized layer was 61.8 HRC.

The current work aims to compare the effects of systematic A-site substitutions on the electrical properties of potassium sodium niobate (KNN)-based coating. The A-site elements were replaced by Li⁺ to form (K_0.4675Na_0.4675Li_0.065) NbO₃ (KNLN). The pure KNN coating and the Li⁺-doped potassium sodium niobate (KNLN) coating with dense morphology and single perovskite structure were successfully prepared by supersonic plasma spraying, and the phase composition, microscopic morphology and electrical properties of the two coatings were compared and analyzed in detail by XRD, XPS, three-dimensional morphology and SEM on an Agilent 4294A (Santa Clara, CA, USA) and FE-5000 wide-range ferroelectric performance tester. The results show that: as the polarization voltage increases, the pure KNN coating is flatter and fuller, but the leakage current is large. The KNLN coating has a relatively long hysteresis loop and is easily polarized. The domain deflection responds faster to the external electric field, and the resistance of the domain wall motion to the external electric field is small. The dielectric constant of KNLN coating is 375, which is much higher than that of the pure KNN coating with 125, and the dielectric loss is stable at 0.01, which is lower than that of pure KNN coating at 0.1–0.35. This is because Li⁺ doping has successfully constructed a polycrystalline phase boundary in which O-T phases coexist, and has higher dielectric properties, piezoelectric properties and ferroelectric properties. At the same time, due to the high-temperature acceleration process in supersonic plasma spraying, the violent volatilization of the alkaline elements Li⁺, Na⁺ and K⁺ leads to the presence of oxygen vacancies and part of Nb⁴⁺ in the coating, which seriously affects the electrical properties of the coating.

Titanium (Ti) materials are highly valued in the medical field for their outstanding biocompatibility and corrosion resistance. However, challenges such as suboptimal wettability and wear resistance can impact the tribological properties of titanium implants, potentially leading to implant failure. This study explores the application of ultrafast pulsed laser processing to create two distinct structures, circular pits and grooves, on the surface of titanium materials. The samples underwent low-surface-energy treatment, after which the wettability and wear resistance of the textured surfaces were evaluated. The findings indicate that the textured surfaces exhibit improved hydrophobic properties and reduced surface wear. Specifically, the textured surfaces demonstrated a remarkable 73.68% reduction in wear compared to the untextured surfaces. These results underscore the potential of etching textured structures onto titanium surfaces to enhance their wear resistance, thereby offering promising implications for the improvement of titanium implant performance.