Chitosan, a natural polysaccharide sourced from crustaceans and insects, is often used with hydrogels in wound care. Evaluating its cytotoxicity and antimicrobial properties is crucial for its potential use in dentistry. Objective: To investigate the mechanical properties of gelatin hydrogels based on decaethylated chitosan and antimicrobial activity against Streptococcus mutans and their biological effects with stem cells from apical papilla (SCAPs). Material and methods: Gelatin–chitosan hydrogels were synthesized at concentrations of 0%, 0.2% and 0.5%. Enzymatic and hydrolytic degradation, along with swelling capacity, was assessed. Fourier transform infrared spectroscopy (FTIR) analysis was employed to characterize the hydrogels. The interaction between hydrogels and SCAPs was examined through initial adhesion and cell proliferation at 24 and 48 h, using the Thiazolyl Blue Tetrazolium Bromide (MTT assay). The antimicrobial effect was evaluated using agar diffusion and a microdilution test against S. mutans. Uniaxial tensile strength (UTS) was also measured to assess the mechanical properties of the hydrogels. Results: The hydrogels underwent hydrolytic and enzymatic degradation at 30, 220, 300 min and 15, 25, 30 min, respectively. Significantly, (p < 0.01) swelling capacity occurred at 20, 40, 30 min, respectively. Gelatin–chitosan hydrogels’ functional groups were confirmed using vibrational pattern analysis. SCAPs proliferation corresponded to 24 h = 73 ± 2%, 82 ± 2%, 61 ± 6% and 48 h = 83 ± 11%, 86 ± 2%, 44 ± 2%, respectively. The bacterial survival of hydrogel interaction was found to be 96 ± 1%, 17 ± 1.5% (p < 0.01) and 1 ± 0.5% (p < 0.01), respectively. UTS showed enhanced (p < 0.05) mechanical properties with chitosan presence. Conclusion: Gelatin–chitosan hydrogels displayed favorable degradation, swelling capacity, mild dose-dependent cytotoxicity, significant proliferation with stem cells from apical papilla (SCAPs), substantial antimicrobial effects against S. mutans and enhanced mechanical properties. These findings highlight their potential applications as postoperative care dressings.

The (-)-Epigallocatechin-gallate (EGCG) metabolite is a natural polyphenol derived from green tea and is associated with antioxidant, biocompatible, and anti-inflammatory effects. Objective: To evaluate the effects of EGCG to promote the odontoblast-like cells differentiated from human dental pulp stem cells (hDPSCs); the antimicrobial effects on Escherichia coli, Streptococcus mutans, and Staphylococcus aureus; and improve the adhesion on enamel and dentin by shear bond strength (SBS) and the adhesive remnant index (ARI). Material and methods: hDSPCs were isolated from pulp tissue and immunologically characterized. EEGC dose-response viability was calculated by MTT assay. Odontoblast-like cells were differentiated from hDPSCs and tested for mineral deposition activity by alizarin red, Von Kossa, and collagen/vimentin staining. Antimicrobial assays were performed in the microdilution test. Demineralization of enamel and dentin in teeth was performed, and the adhesion was conducted by incorporating EGCG in an adhesive system and testing with SBS-ARI. The data were analyzed with normalized Shapiro–Wilks test and ANOVA post hoc Tukey test. Results: The hDPSCs were positive to CD105, CD90, and vimentin and negative to CD34. EGCG (3.12 µg/mL) accelerated the differentiation of odontoblast-like cells. Streptococcus mutans exhibited the highest susceptibility < Staphylococcus aureus < Escherichia coli. EGCG increased (p < 0.05) the dentin adhesion, and cohesive failure was the most frequent. Conclusion: (-)-Epigallocatechin-gallate is nontoxic, promotes differentiation into odontoblast-like cells, possesses an antibacterial effect, and increases dentin adhesion.

Opuntia Ficus-indica, or nopal, is traditionally used for its medicinal properties in Mexico. This study aims to decellularize and characterize nopal (Opuntia Ficus-indica) scaffolds, assess their degradation and the proliferation of hDPSC, and determine potential pro-inflammatory effects by assessing the expression of cyclooxygenase 1 and 2 (COX-1 and 2). The scaffolds were decellularized using a 0.5% sodium dodecyl sulfate (SDS) solution and confirmed by color, optical microscopy, and SEM. The degradation rates and mechanical properties of the scaffolds were determined by weight and solution absorbances using trypsin and PBS and tensile strength testing. Human dental pulp stem cells (hDPSCs) primary cells were used for scaffold–cell interaction and proliferation assays, as well as an MTT assay to determine proliferation. Proinflammatory protein expression of COX-I and -II was discovered by Western blot assay, and the cultures were induced into a pro-inflammatory state with interleukin 1-β. The nopal scaffolds exhibited a porous structure with an average pore size of 252 ± 77 μm. The decellularized scaffolds showed a 57% reduction in weight loss during hydrolytic degradation and a 70% reduction during enzymatic degradation. There was no difference in tensile strengths between native and decellularized scaffolds (12.5 ± 1 and 11.8 ± 0.5 MPa). Furthermore, hDPSCs showed a significant increase in cell viability of 95% and 106% at 168 h for native and decellularized scaffolds, respectively. The combination of the scaffold and hDPSCs did not cause an increase in the expression of COX-1 and COX-2 proteins. However, when the combination was exposed to IL-1β, there was an increase in the expression of COX-2. This study demonstrates the potential application of nopal scaffolds in tissue engineering and regenerative medicine or dentistry, owing to their structural characteristics, degradation properties, mechanical properties, ability to induce cell proliferation, and lack of enhancement of pro-inflammatory cytokines.

The incorporation of silver nanoparticles (AgNPs) into alginate–gelatin (Alg-Gel) hydrogels can enhance the properties of these materials for bone regeneration applications, due to the antimicrobial properties of AgNPs and non-cytotoxic concentrations, osteoinductive properties, and regulation of stem cell proliferation and differentiation. Here, the hydrogel formulation included 2% (w/v) sodium alginate, 4 µg/mL AgNPs, and 2.5% (w/v) gelatin. AgNPs were synthesized using a 2% (w/v) aqueous extract of roasted green tea with silver nitrate. The aqueous extract of roasted green tea for AgNP synthesis was characterized using HPLC and UHPLC-ESI-QTOF-MS/MS, and antioxidant capacity was measured in Trolox equivalents (TE) from 4 to 20 nmol/well concentrations. Stem cells from human exfoliated deciduous tooth cells were used for differentiation assays including positive (SHEDs/hydrogel with AgNPs) and negative controls (hydrogel without AgNPs). FTIR was used for hydrogel chemical characterization. Statistical analysis (p < 0.05, ANOVA) confirmed significant findings. Roasted green tea extract contained caffeine (most abundant), (−)-Gallocatechin, gallic acid, and various catechins. XRD analysis revealed FCC structure, TEM showed quasispheroidal AgNPs (19.85 ± 3 nm), and UV–Vis indicated a plasmon surface of 418 nm. This integration of nanotechnology and biomaterials shows promise for addressing bone tissue loss in clinical and surgical settings.

El polimetilmetacrilato (PMMA) es uno de los materiales más conocidos en la fabricación de prótesis e implantes dentales, con propiedades óptimas para su aplicación odontológica debido a las características favorecedoras como son: buena estética, biocompatibilidad, bajo nivel de absorción en agua, ser transparente, ligero y fuerte. Pese a todas estas beneficiosas propiedades, se considera que posee desventajas que se verían mejoradas con la adición de nanopartículas de distintos materiales. En la presente revisión sistemática, se identifica como problema principal la adhesión microbiana al PMMA cuando este se encuentra en cavidad oral. El objetivo se centró en comparar el uso de las nanopartículas (NPs) de diferentes metales (plata – Ag y cobre – Cu) así como de fosfato de magnesio – MgP, con el PMMA. Dentro de los principales resultados, la mayoría de los artículos mostraron efectos antimicrobianos positivos o mejorados en comparación con el PMMA convencional.

Biotechnology and artificial intelligence have sparked a revolution in dentistry, with a focus on restoring natural tissue functions. This transformation has given rise to bioactive materials, inspired by biomimetics, aimed at replicating the processes found in nature. As synthetic biology advances, there is a heightened focus on signaling systems crucial for bio-based diagnostics and therapeutics. Dentistry now harnesses synthetic proteins for tissue regeneration and dental material enhancement. A current research priority is bacterial biofilm inhibition, vital for dental health. Given the role of Streptococcus mutans in dental caries, the development of synthetic antimicrobial peptides targeting this bacterium is underway. The balance of dental enamel between demineralization and remineralization impacts caries formation. Factors such as the presence of hydroxyapatite and salivary peptides influence enamel health. Recent studies have spotlighted salivary protein-inspired peptides for enhanced remineralization. In the realm of bone regeneration, synthetic proteins like bone morphogenetic proteins (BMP) have been spotlighted, earning FDA approval. Research is currently delving into peptides such as cementum protein 1 peptide (CEMP-1-p1) and parathyroid hormone variants like PTH (1-34), underscoring their potential in advancing dental and bone health.