In the field of flexible electronics manufacturing, inkjet printing technology is a research hotspot, and it is key to developing low-temperature curing conductive inks that meet printing requirements and have suitable functions. Herein, methylphenylamino silicon oil (N75) and epoxy-modified silicon oil (SE35) were successfully synthesized through functional silicon monomers, and they were used to prepare silicone resin 1030H with nano SiO₂. 1030H silicone resin was used as the resin binder for silver conductive ink. The silver conductive ink we prepared with 1030H has good dispersion performance with a particle size of 50–100 nm, as well as good storage stability and excellent adhesion. Additionally, the printing performance and conductivity of the silver conductive ink prepared with n,n-dimethylformamide (DMF): proprylene glycol monomethyl ether (PM) (1:1) as solvent are better than those of the silver conductive ink prepared by DMF and PM solvent. Cured at a low temperature of 160 °C, the resistivity of 1030H-Ag-82%-3 conductive ink is 6.87 × 10⁻⁶ Ω·m, and that of 1030H-Ag-92%-3 conductive ink is 0.564 × 10⁻⁶ Ω·m, so the low-temperature curing silver conductive ink has high conductivity. The low-temperature curing silver conductive ink we prepared meets the printing requirements and has potential for practical applications.

Biochar is considered as a promising candidate for emerging sustainable energy systems and environmental technology applications. However, the improvement of mechanical properties remains challenges. Herein, we propose a generic strategy to enhance the mechanical properties of bio-based carbon materials through inorganic skeleton reinforcement. As a proof-of-concept, silane, geopolymer, and inorganic gel are selected as precursors. The composites’ structures are characterized and an inorganic skeleton reinforcement mechanism is elucidated. Specifically, two types of reinforcement of the silicon-oxygen skeleton network formed in situ with biomass pyrolysis and the silica-oxy-al-oxy network are constructed to improve the mechanical properties. A significant improvement in mechanical strength was achieved for bio-based carbon materials. The compressive strength of well-balanced porous carbon materials modified by silane can reach up to 88.9 kPa, geopolymer-modified carbon material exhibits an enhanced compressive strength of 36.8 kPa, and that of inorganic-gel-polymer-modified carbon material is 124.6 kPa. Moreover, the prepared carbon materials with enhanced mechanical properties show excellent adsorption performance and high reusability for organic pollutant model compound methylene blue dye. This work demonstrates a promising and universal strategy for enhancing the mechanical properties of biomass-derived porous carbon materials.