Activated carbon fibers (ACFs) are known as an excellent adsorbent material due to their particular characteristics such as their high speed adsorption rate and for being easy to handle. The ACFs are commercially manufactured from carbon fibers (CF) which receive an additional activation process and can be produced from celluloses, phenolic resin, pitch and Polyacrylonitrile (PAN). In the present work, the oxidized 5.0 dtex textile PAN fiber was carbonized to CFs formation. During the carbonization process in different heating rates, the topographic features changes on fibers were monitored in order to determine the best carbonization condition for CFs production to be used as raw material for ACF. Different heating rates and maximum temperature of treatment were tested and the results indicated that it is possible to produce poorly activated carbon fiber, directly from oxidized textile PAN fiber, by one single step production process

An electrical double-layer capacitor (EDLC) is based on the physical adsorption/desorption of electrolyte ions onto the surface of electrodes. Due to its high surface area and other properties, such as electrochemical stability and high electrical conductivity, carbon materials are the most widely used materials for EDLC electrodes. In this work, we study an activated carbon felt obtained from sheep wool felt (ACF’f) as a supercapacitor electrode. The ACF’f was characterized by elemental analysis, scanning electron microscopy (SEM), textural analysis, and X-ray photoelectron spectroscopy (XPS). The electrochemical behaviour of the ACF’f was tested in a two-electrode Swagelok^®-type, using acidic and basic aqueous electrolytes. At low current densities, the maximum specific capacitance determined from the charge-discharge curves were 163 F·g⁻¹ and 152 F·g⁻¹, in acidic and basic electrolytes, respectively. The capacitance retention at higher current densities was better in acidic electrolyte while, for both electrolytes, the voltammogram of the sample presents a typical capacitive behaviour, being in accordance with the electrochemical results.

Carbonaceous materials have been widely applied as adsorbents, but there are some factors that affect their efficiency. In this context, advances in nanotechnology provide new and more efficient methodologies for water treatment. This study evaluated the efficiency of a novel carbon-based adsorbent developed from Brazilian polyacrylonitrile textile fiber and functionalized with iron oxide magnetic nanoparticles for the removal of 2,4-dichlorophenoxyacetic acid (2,4-D) from the aqueous medium. The synthesized adsorbent (ACF-Fe₃O₄) was characterized by FTIR, XRD, VSM, Zeta potential, SEM, EDX, and TEM. The characterization techniques showed that the adsorbent has peaks characteristic of its precursors and superparamagnetic characteristics, confirming the efficiency of the synthesis method. The adsorption tests evaluated the influence of adsorbent dosage, pH of the contaminant solution, contact time and temperature on the removal of 2,4-D. The experimental data were better adjusted by the pseudo-second order kinetic model and by the Langmuir isothermal model. The thermodynamic parameters revealed that the process is exothermic, spontaneous and thermodynamically favorable. Under the best experimental conditions, the maximum adsorption capacity obtained was 51.10 mg g⁻¹ with an adsorbent concentration of 0.33 g L⁻¹, natural pH of the solution, temperature of 288 K at the equilibrium time of six hours. Adsorbent reusage was studied in four desorption cycles. The adsorption mechanism can be explained through π-π bonds, hydrogen bonds and electrostatic interactions. The prepared material presented high-efficiency adsorption capacity of 2,4-D compared to other carbonaceous materials present in the literature, demonstrating its viability for the removal of this contaminant from the aqueous medium. GRAPHICAL ABSTRACT

Rechargeable sodium seawater batteries (SWBs) are gaining the world leadership of high voltage energy storage devices for marine environments. With natural seawater as the source of active material, SWBs can be supplied infinitely with Na cations. Because of their open-structured cathode, the cathode material’s specific surface area, porosity and wettability need to be optimized to achieve a high-performance cell. In this work, activated textile polyacrylonitrile (PAN) fibers were used to produce an activated carbon felt with a facile manufacturing process. The easy and low-cost production of these fibers makes them excellent candidates for energy storage applications involving oxygen evolution and reduction reactions. The electrochemical performance results of the fabricated activated PAN fibers and of commercial carbon felts were measured and compared, being characterized through galvanostic charge discharge cycles, electrochemical impedance spectroscopy and cyclic voltammetries. A performance improvement was observed with PAN activated carbon felt as half cell with a capacitance increase (about 9000%), and as full cell with a smaller voltage gap (about 10%) and increased gravimetric capacitance (about 260%) when compared to the commercial carbon felt. The successful implementation of PAN activated carbon felts in an aqueous environment opens new paths toward high performance seawater battery’s cathodes.