Increasing demands in minimization of fire risks and meeting fire safety requirements by polymers require advances in knowledge of flame-retardant materials suitable for use in fire-retardancy applications. The present work represents the seminal review of alginate/polymer-based materials as flame retardants. Alginates are suitable for this application as they represent alternatives to petroleum-based polymer feedstocks. The content of the present work is structured into four sections: synthesis and structure, including alginate synthesis and modification by polymeric conjugation; properties, including four-stage mechanism of thermal degradation; applications, including commercial information on alginates and polymers; and flame retardancy, including comprehensive summaries of test methods and published data, discussion of key parameters, eight fire retardancy mechanisms, four char generation mechanisms, and extensive quantitative analysis of polymer char formation. The final section culminates in a first-principles approach to the prediction of quantitative polymer char formation. The goal of the review is to provide guidance for the application of alginates and alginates conjugated with fire-retardant polymers as a new generation flame retardant material.

Room temperature vulcanized (RTV) silicone rubber filled with aluminum trihydrate (ATH) is substantially engaged in electrical outdoor insulation applications. The pristine silicone rubber is highly combustible. ATH filled silicone rubber offers excellent electrical insulation but lacks in providing adequate flame retardancy. This short communication reports the novel results on improved flame retardancy of pristine and ATH filled silicone rubber whilst retaining the electrical insulation properties to a great extent. Results suggest that the presence of only one percent of graphene nanoplatelets with ATH sharply reduces the heat release rate and rate of smoke release. A minor reduction in dielectric breakdown strength and volume resistivity is noticed. Furthermore, permittivity and dielectric loss at power frequency suggest that a marginal 1% concentration of nanoplatelet with ATH is an excellent approach to fabricate flame retardant silicone rubber with an acceptable electrical insulation level.

Building polymers are highly flammable and produce a vast amount of toxic chemical compounds in the event of a fire which can lead to potential incapacitation and death. To gain an in-depth understanding of this issue, smoke toxicity and thermal characteristics of seven commonly used building polymers were analysed through a systematic fire performance evaluation system using a Thermogravimetric Analyzer and a Cone Calorimeter coupled with an FTIR arrangement. Four Fractional Effective Dose (FED) expressions were compared to assess the smoke toxicity of the fire effluents based on different assumptions. It was found that FED_N2, calculated using Purser’s equation, reported the highest values of FED with the following order of potential smoke toxicity at 50 kW/m² radiative heat flux: LDPU > HDPU > PE > HDEPS > XPS > EVA > LDEPS. Furthermore, fire performance evaluation of the polymers was carried out by considering three key fire risk parameters, i.e., flashover propensity, total heat released, and toxic hazard. At 50 kW/m² radiative heat flux, HDPU exhibited 11.7 times flashover propensity compared to the least flammable polymer (HDEPS), EVA exhibited 5 times total heat release compared to the polymer with the lowest total heat release (LDEPS) and, LDPU exhibited 6.7 potential times toxic hazard compared to the least toxic polymer (EVA).