Fabricating high-performance MXene-based polymer nanocomposites is a huge challenge because of the poor dispersion and interfacial interaction of MXene nanosheets in the polymer matrix. To address the issue, MXene nanosheets were successfully exfoliated and subsequently modified by long-chain cationic agents with different chain lengths, i.e., decyltrimethylammonium bromide (DTAB), octadecyltrimethylammonium bromide (OTAB), and dihexadecyldimethylammonium bromide (DDAB). With the long-chain groups on their surface, modified Ti₃C₂ (MXene) nanosheets were well dispersed in N,N-dimethylformamide (DMF), resulting in the formation of uniform dispersion and strong interfacial adhesion within a polystyrene (PS) matrix. The thermal stability properties of cationic modified Ti₃C₂/PS nanocomposites were improved considerably with the temperatures at 5% weight loss increasing by 20 °C for DTAB-Ti₃C₂/PS, 25 °C for OTAB-Ti₃C₂/PS and 23 °C for DDAB-Ti₃C₂/PS, respectively. The modified MXene nanosheets also enhanced the flame-retardant properties of PS. Compared to neat PS, the peak heat release rate (PHRR) was reduced by approximately 26.4%, 21.5% and 20.8% for PS/OTAB-Ti₃C₂, PS/DDAB-Ti₃C₂ and PS/DTAB-Ti₃C₂, respectively. Significant reductions in CO and CO₂ productions were also obtained in the cone calorimeter test and generally lower pyrolysis volatile products were recorded by PS/OTAB-Ti₃C₂ compared to pristine PS. These property enhancements of PS nanocomposites are attributed to the superior dispersion, catalytic and barrier effects of Ti₃C₂ nanosheets.

In recent years, the applications of lithium-ion batteries have emerged promptly owing to its widespread use in portable electronics and electric vehicles. Nevertheless, the safety of the battery systems has always been a global concern for the end-users. The separator is an indispensable part of lithium-ion batteries since it functions as a physical barrier for the electrode as well as an electrolyte reservoir for ionic transport. The properties of separators have direct influences on the performance of lithium-ion batteries, therefore the separators play an important role in the battery safety issue. With the rapid developments of applied materials, there have been extensive efforts to utilize these new materials as battery separators with enhanced electrical, fire, and explosion prevention performances. In this review, we aim to deliver an overview of recent advancements in numerical models on battery separators. Moreover, we summarize the physical properties of separators and benchmark selective key performance indicators. A broad picture of recent simulation studies on separators is given and a brief outlook for the future directions is also proposed.

Room temperature vulcanized (RTV) silicone rubber filled with aluminum trihydrate (ATH) is substantially engaged in electrical outdoor insulation applications. The pristine silicone rubber is highly combustible. ATH filled silicone rubber offers excellent electrical insulation but lacks in providing adequate flame retardancy. This short communication reports the novel results on improved flame retardancy of pristine and ATH filled silicone rubber whilst retaining the electrical insulation properties to a great extent. Results suggest that the presence of only one percent of graphene nanoplatelets with ATH sharply reduces the heat release rate and rate of smoke release. A minor reduction in dielectric breakdown strength and volume resistivity is noticed. Furthermore, permittivity and dielectric loss at power frequency suggest that a marginal 1% concentration of nanoplatelet with ATH is an excellent approach to fabricate flame retardant silicone rubber with an acceptable electrical insulation level.