Room temperature vulcanized (RTV) silicone rubber filled with aluminum trihydrate (ATH) is substantially engaged in electrical outdoor insulation applications. The pristine silicone rubber is highly combustible. ATH filled silicone rubber offers excellent electrical insulation but lacks in providing adequate flame retardancy. This short communication reports the novel results on improved flame retardancy of pristine and ATH filled silicone rubber whilst retaining the electrical insulation properties to a great extent. Results suggest that the presence of only one percent of graphene nanoplatelets with ATH sharply reduces the heat release rate and rate of smoke release. A minor reduction in dielectric breakdown strength and volume resistivity is noticed. Furthermore, permittivity and dielectric loss at power frequency suggest that a marginal 1% concentration of nanoplatelet with ATH is an excellent approach to fabricate flame retardant silicone rubber with an acceptable electrical insulation level.

The effect of varying the weight percentage composition (wt.%) of low-cost expandable graphite (EG), ammonium polyphosphate (APP), fibreglass (FG), and vermiculite (VMT) in polyurethane (PU) polymer was studied using a traditional intumescent flame retardant (IFR) system. The synergistic effect between EG, APP, FG, and VMT on the flame retardant properties of the PU composites was investigated using SEM, TGA, tensile strength tests, and cone calorimetry. The IFR that contained PU composites with 40 wt.% EG displayed superior flame retardant performance compared with the composites containing only 20 w.t.% or 10 w.t.% EG. The peak heat release rate, total smoke release, and carbon dioxide production from the 40 wt.% EG sample along with APP, FG, and VMT in the PU composite were 88%, 93%, and 92% less than the PU control sample, respectively. As a result, the synergistic effect was greatly influenced by the compactness of the united protective layer. The PU composite suppressed smoke emission and inhibited air penetrating the composite, thus reducing reactions with the gas volatiles of the material. SEM images and TGA results provided positive evidence for the combustion tests. Further, the mechanical properties of PU composites were also investigated. As expected, compared with control PU, the addition of flame-retardant additives decreased the tensile strength, but this was ameliorated with the addition of FG. These new PU composite materials provide a promising strategy for producing polymer composites with flame retardation and smoke suppression for construction materials.