The aim of this study was to investigate the ecotoxicity of polyvinylidene difluoride (PVDF) and polylactic acid (PLA) microplastics (MPs) in two marine zooplankton: the crustacean Artemia franciscana and the cnidarian Aurelia sp. (common jellyfish). To achieve this goal, (i) MP uptake, (ii) immobility, and (iii) behavior (swimming speed, pulsation mode) of crustacean larval stages and jellyfish ephyrae exposed to MPs concentrations (1, 10, 100 mg/L) were assessed for 24 h. Using traditional and novel techniques, i.e., epifluorescence microscopy and 3D holotomography (HT), PVDF and PLA MPs were found in the digestive systems of the crustaceans and in the gelatinous tissue of jellyfish. Immobility was not affected in either organism, while a significant behavioral alteration in terms of pulsation mode was found in jellyfish after exposure to both PVDF and PLA MPs. Moreover, PLA MPs exposure in jellyfish induced a toxic effect (EC50: 77.43 mg/L) on the behavioral response. This study provides new insights into PLA and PVDF toxicity with the potential for a large impact on the marine ecosystem, since jellyfish play a key role in the marine food chain. However, further investigations incorporating additional species belonging to other trophic levels are paramount to better understand and clarify the impact of such polymers at micro scale in the marine environment. These findings suggest that although PVDF and PLA have been recently proposed as innovative and, in the case of PLA, biodegradable polymers, their effects on marine biota should not be underestimated.

In this work, novel composites based on poly(ε-caprolactone) (PCL) were prepared and characterized in terms of morphological, thermal, rheological and mechanical properties. Hollow glass microspheres (HGM), alone or surface modified by treatment with (3-aminopropyl)triethoxysilane (APTES) in order to enhance the compatibility between the inorganic particles and the polymer matrix, were used to obtain lightweight composites with improved properties. The silanization treatment implies a good dispersion of filler particles in the matrix and an enhanced filler–polymer adhesion. The addition of HGM to PCL has relevant implications on the rheological and mechanical properties enhancing the stiffness of the material. Furthermore, the presence of HGM strongly interferes with the crystallization behavior and thermo-oxidative degradation of PCL. The increase of PCL crystallization rate was observed as a function of the HGM amount in the composites. Finally, rotational molding tests demonstrated the possibility of successfully producing manufactured goods in PCL and PCL-based composites on both a laboratory and industrial scale.

In an effort to reduce greenhouse gas emission, reduce the consumption of natural resources, and increase the sustainability of biocomposite foams, the present study focuses on the recycling of cork processing waste for the production of lightweight, non-structural, fireproof thermal and acoustic insulating panels. Egg white proteins (EWP) were used as a matrix model to introduce an open cell structure via a simple and energy-efficient microwave foaming process. Samples with different compositions (ratio of EWP and cork) and additives (eggshells and inorganic intumescent fillers) were prepared with the aim of correlating composition, cellular structures, flame resistance, and mechanical properties.