Compounding natural additives with synthetic polymers allows developing more eco-friendly materials with enhanced biodegradability. The composite films based on low-density polyethylene (PE) with different content of natural rubber (NR) (10–30 wt%) were investigated. The influence of NR content on structural features, water absorption and mechanical properties of the composites were studied. The 70PE/30NR composite is characterized by the uniform distribution and the smallest size of NR domains (45 ± 5 μm). A tensile test was satisfied by the mechanical properties of the biocomposites, caused by elasticity of NR domains. The tensile strength of 70PE/30NR composite film is 5 ± 0.25 MPa. Higher water absorption of PE/NR composites (1.5–3.7 wt%) compared to neat PE facilitates penetrating vital activity products of microorganisms. Mycological test with mold fungi and full-scale soil test detected the composite with 30 wt% of NR as the most biodegradable (mass loss was 7.2 wt% for 90 days). According to infrared spectroscopy and differential scanning calorimetry analysis, NR consumption and PE structural changes in the biocomposites after exposure to soil occurred. The PE/NR composites with enhanced biodegradability as well as satisfied mechanical and technological properties have potential applications in packaging and agricultural films.

Due to the current environmental situation, biopolymers are replacing the usual synthetic polymers, and special attention is being paid to poly-3-hydroxybutyrate (PHB), which is a biodegradable polymer of natural origin. In this paper, the rate of biodegradation of films and fibers based on PHB was compared. The influence of exposure to soil on the structure and properties of materials was evaluated using methods of mechanical analysis, the DSC method and FTIR spectroscopy. The results showed rapid decomposition of the fibrous material and also showed how the surface of the material affects the rate of biodegradation and the mechanical properties of the material. It was found that maximum strength decreased by 91% in the fibrous material and by 49% in the film. Additionally, the DSC method showed that the crystallinity of the fiber after exposure to the soil decreased. It was established that the rate of degradation is influenced by different factors, including the surface area of the material and its susceptibility to soil microorganisms. The results obtained are of great importance for planning the structure of features in the manufacture of biopolymer consumer products in areas such as medicine, packaging, filters, protective layers and coatings, etc. Therefore, an understanding of the biodegradation mechanisms of PHB could lead to the development of effective medical devices, packaging materials and different objects with a short working lifespan.

Recently, environmental problems caused by the overproduction and consumption of synthetic polymer materials led to an urgent need to develop efficient methods for processing plastics. The accumulation of polymer waste for their subsequent incineration does not solve the problem due to the limited areas of landfills for waste storage. In addition, the incineration of polymer waste can cause toxic air pollution, which, in turn, does not contribute to an improvement in the environmental situation. Recycling plastics, although a more environmentally friendly waste disposal method, requires significant labor and energy costs and can be performed a limited number of times. Thus, the most promising solution to this problem is the creation of biodegradable polymers capable of degradation with the formation of simpler chemical structures (water, carbon dioxide, biomass, etc.), which are easily included in the metabolic processes of natural biological systems. The article provides an overview of the main trends in the creation of biodegradable composites for the needs of agriculture. Also, the article proposes a new composition based on polyethylene with natural rubber that surpasses existing biodegradable materials in a number of physical and mechanical characteristics and has the ability to complete biodegradation in 60 months. It is shown that the studies carried out to date indicate that these composites are highly promising for the creation of biodegradable packaging materials with good performance characteristics. Thus, it was concluded that further research on composites based on polyethylene and natural rubber is important.

The purpose of this study was to assess the potential for biocomposite films to biodegrade in diverse climatic environments. Biocomposite films based on polyethylene and 30 wt.% of two lignocellulosic fillers (wood flour or flax straw) of different size fractions were prepared and studied. The developed composite films were characterized by satisfactory mechanical properties that allows the use of these materials for various applications. The biodegradability was evaluated in soil across three environments: laboratory conditions, an open field in Russia, and an open field in Costa Rica. All the samples lost weight and tensile strength during biodegradation tests, which was associated with the physicochemical degradation of both the natural filler and the polymer matrix. The spectral density of the band at 1463 cm⁻¹ related to CH₂-groups in polyethylene chains decreased in the process of soil burial, which is evidence of polymer chain breakage with formation of CH₃ end groups. The degradation rate of most biocomposites after 20 months of the soil assays was greatest in Costa Rica (20.8–30.9%), followed by laboratory conditions (16.0–23.3%), and lowest in Russia (13.2–22.0%). The biocomposites with flax straw were more prone to biodegradation than those with wood flour, which can be explained by the chemical composition of fillers and the shape of filler particles. As the size fraction of filler particles increased, the biodegradation rate increased. Large particles had higher bioavailability than small spherical ones, encapsulated by a polymer. The prepared biocomposites have potential as an ecofriendly replacement for traditional polyolefins, especially in warmer climates.

Nowadays, the development and research of nonwoven medical fibrous materials based on biopolymers is an area of a great practical interest. One of the most promising methods for producing nonwoven materials with a highly developed surface is electrospinning (ES). In this article, the possibility of efficient sterilization of ultrathin fibers based on polyhydroxybutyrate (PHB) by ozone treatment was considered. The purpose of this work was to select the most optimal morphology of nonwoven materials for medical purposes and to establish the correlation between the supramolecular structure and the physical properties of fibrous materials while under the influence of an ozone sterilization process.