The combination of layered double hydroxides (LDH) with graphene oxide (GO) enables the formation of nanohybrids with improved properties. This work focuses on the structural and catalytic properties of Ce-containing MgAl LDH-GO composites bearing different concentrations of GO in the range of 5–25 wt.%. The synthesis of the composites was performed by co-precipitating the LDH phase in the presence of GO, while their characterization was performed using XRF, XRD, DRIFT, Raman, SEM, nitrogen adsorption-desorption, and acidity-basicity measurements. The LDH-GO composites, showing redox, basic, and acid catalytic functions, were tested in two different types of organic transformations: (i) Knoevenagel condensation and (ii) one-pot cascade oxidation-Knoevenagel condensation. (i) The cinnamic acid was synthesized by the Knoevenagel condensation of benzaldehyde with diethylmalonate. The composites showed catalytic performances in strong contrast to neat LDH or GO, suggesting a synergistic interaction between the two components. During Knoevenagel condensation, the catalytic activity increased with the GO content in the hybrids up to 15 wt.% and decreased afterwards. (ii) 2-Benzoyl-3-phenylacrylonitrile was synthesized by the aerobic oxidation of benzyl alcohol followed by the Knoevenagel condensation with benzoyl acetonitrile using three different non-polar solvents, i.e., toluene, benzene, and mesitylene. The conversion of benzyl alcohol was higher for the hybrid materials compared to the individual components but decreased with the increase of the graphene oxide concentration.

A series of M(x)CoCeMgAlO mixed oxides with different transition metals (M = Cu, Fe, Mn, and Ni) with an M content x = 3 at. %, and another series of Fe(x)CoCeMgAlO mixed oxides with Fe contents x ranging from 1 to 9 at. % with respect to cations, while keeping constant in both cases 40 at. % Co, 10 at. % Ce and Mg/Al atomic ratio of 3 were prepared via thermal decomposition at 750 °C in air of their corresponding layered double hydroxide (LDH) precursors obtained by coprecipitation. They were tested in a fixed bed reactor for complete methane oxidation with a gas feed of 1 vol.% methane in air to evaluate their catalytic performance. The physico-structural properties of the mixed oxide samples were investigated with several techniques, such as powder X-ray diffraction (XRD), scanning electron microscopy (SEM) coupled with energy dispersive X-ray spectroscopy (EDX), elemental mappings, inductively coupled plasma optical emission spectroscopy (ICP-OES), X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction under hydrogen (H₂-TPR) and nitrogen adsorption–desorption at −196 °C. XRD analysis revealed in all the samples the presence of Co₃O₄ crystallites together with periclase-like and CeO₂ phases, with no separate M-based oxide phase. All the cations were distributed homogeneously, as suggested by EDX measurements and elemental mappings of the samples. The metal contents, determined by EDX and ICP-OES, were in accordance with the theoretical values set for the catalysts’ preparation. The redox properties studied by H₂-TPR, along with the surface composition determined by XPS, provided information to elucidate the catalytic combustion properties of the studied mixed oxide materials. The methane combustion tests showed that all the M-promoted CoCeMgAlO mixed oxides were more active than the M-free counterpart, the highest promoting effect being observed for Fe as the doping transition metal. The Fe(x)CoCeMgAlO mixed oxide sample, with x = 3 at. % Fe displayed the highest catalytic activity for methane combustion with a temperature corresponding to 50% methane conversion, T₅₀, of 489 °C, which is ca. 40 °C lower than that of the unpromoted catalyst. This was attributed to its superior redox properties and lowest activation energy among the studied catalysts, likely due to a Fe–Co–Ce synergistic interaction. In addition, long-term tests of Fe(3)CoCeMgAlO mixed oxide were performed, showing good stability over 60 h on-stream. On the other hand, the addition of water vapors in the feed led to textural and structural changes in the Fe(3)CoCeMgAlO system, affecting its catalytic performance in methane complete oxidation. At the same time, the catalyst showed relatively good recovery of its catalytic activity as soon as the water vapors were removed from the feed.

The synthesis and characterization of sol-gel-derived cornhusk support for low-temperature catalytic methane combustion (LTCMC) were investigated in this study. The prepared cornhusk support was impregnated with palladium and cerium oxide (Pd/CeO₂) via the classical incipient wetness method. The resulting catalyst was characterized using various techniques, including X-ray diffraction (XRD), N₂ physisorption (BET), transmission electron microscopy (TEM), and hydrogen temperature-programmed reduction (H₂-TPR). The catalytic performance of the Pd/CeO₂/CHSiO₂ catalyst was evaluated for methane combustion in the temperature range of 150–600 °C using a temperature-controlled catalytic flow reactor, and its performance was compared with a commercial catalyst. The results showed that the Pd/CeO₂ dispersed on SiO₂ from the cornhusk ash support (Pd/CeO₂/CHSiO₂) catalyst exhibited excellent catalytic activity for methane combustion, with a conversion of 50% at 394 °C compared with 593 °C for the commercial silica catalyst (Pd/CeO₂/commercial). Moreover, the Pd/CeO₂/CHSiO₂ catalyst displayed better catalytic stability after 10 h on stream, with a 7% marginal loss in catalytic activity compared with 11% recorded for the Pd/CeO₂/commercial catalyst. The N₂ physisorption and H₂-TPR results indicated that the cornhusk SiO₂ support possessed a higher surface area and strong reducibility than the synthesized commercial catalyst, contributing to the enhanced catalytic activity of the Pd/CeO₂/SiO₂ catalyst. Overall, the SiO₂ generated from cornhusk ash exhibited promising potential as a low-cost and environmentally friendly support for LTCMC catalysts.

The oxidative C-C cleavage of a C₁₈ substrate is an important transformation in synthetic organic chemistry, facilitating the synthesis of valuable C₈-C₉ acids widely used in many industries. Through a comparative analysis of the catalytic and physicochemical properties of catalysts, comprising mono- (Pd or Au) and bimetallic (PdAu) nanoparticles deposited on oxides, oxyhydroxides and graphite-like carbon material Sibunit (Cp), it was shown that the efficiency of the catalyst in the oxidative cleavage of 9,10-dihydroxystearic acid relies on the nature of the active component, the support and the average size of metal nanoparticles (NPs). The dependency of 9,10-DSA conversion on the average size of metal NPs shows the structural sensitivity of the oxidative cleavage reaction. Notably, catalysts with an average size of gold particles less than 3 nm exhibit the highest activity. The nature of the active component and the support material are crucial factors determining the process selectivity. Among the catalysts studied, the most effective for the oxidative cleavage of 9,10-DSA is a material based on Au NPs deposited on Cp.