The electrochemical behavior of polycrystalline TiO₂ anatase coatings prepared by a one-step hydrothermal synthesis on commercially pure (CP) Ti grade 2 and a Ti13Nb13Zr alloy for bone implants was investigated in Hank’s solution at 37.5 °C. The aim was to verify to what extent the in-situ-grown anatase improved the behavior of the substrate in comparison to the bare substrates. Tafel-plot extrapolations from the potentiodynamic curves revealed a substantial improvement in the corrosion potentials for the anatase coatings. Moreover, the coatings grown on titanium also exhibited lower corrosion-current densities, indicating a longer survival of the implant. The results were explained by considering the effects of crystal morphology, coating thickness and porosity. Evidence for the existing porosity was obtained from corrosion and nano-indentation tests. The overall results indicated that the hydrothermally prepared anatase coatings, with the appropriate morphology and surface properties, have attractive prospects for use in medical devices, since better corrosion protection of the implant can be expected.

The influence of the flooding gas during ToF-SIMS depth profiling was studied to reduce the matrix effect and improve the quality of the depth profiles. The profiles were measured on three multilayered samples prepared by PVD. They were composed of metal, metal oxide, and alloy layers. Dual-beam depth profiling was performed with 1 keV Cs⁺ and 1 keV O₂⁺ sputter beams and analyzed with a Bi⁺ primary beam. The novelty of this work was the application of H₂, C₂H₂, CO, and O₂ atmospheres during SIMS depth profiling. Negative cluster secondary ions, formed from sputtered metals/metal oxides and the flooding gases, were analyzed. A systematic comparison and evaluation of the ToF-SIMS depth profiles were performed regarding the matrix effect, ionization probability, chemical sensitivity, sputtering rate, and depth resolution. We found that depth profiling in the C₂H₂, CO, and O₂ atmospheres has some advantages over UHV depth profiling, but it still lacks some of the information needed for an unambiguous determination of multilayered structures. The ToF-SIMS depth profiles were significantly improved during H₂ flooding in terms of matrix-effect reduction. The structures of all the samples were clearly resolved while measuring the intensity of the M_nH_m^–, M_nO_m^–, M_nO_mH^–, and M_n^– cluster secondary ions. A further decrease in the matrix effect was obtained by normalization of the measured signals. The use of H₂ is proposed for the depth profiling of metal/metal oxide multilayers and alloys.

This study investigated polysiloxane hybrid sol-gel coatings synthesized from tetraethyl orthosilicate (TEOS), 3-(trimethoxysilyl)propyl methacrylate (MAPTMS) and two different precursors, i.e., methyl- or ethyl- methacrylate (MMA or EMA), as corrosion protection of aluminium alloy 7075-T6. The hypothesis was that the additional alkyl group might affect the chemical properties and, consequently, the corrosion properties. Synthesis of the sols proceeded in two steps, each involving either MMA or EMA in the same molar ratio. The resulting sols, siloxane-(poly(methyl methacrylate-co-MAPTMS)) or siloxane-(poly(ethyl methacrylate-co-MAPTMS)), were applied on aluminium alloy followed by characterization in terms of chemical structure and composition, topography, wettability, adhesion and corrosion resistance in 0.1 M sodium chloride solution. The chemical properties of sols, monoliths and coatings were investigated using Fourier transform infrared spectrometry, solid state nuclear magnetic resonance spectrometry, X-ray photoelectron spectroscopy and time-of-flight secondary ion mass spectrometry. Coatings were similar in terms of surface topography, while the wettability of the coating with EMA showed 6° greater water contact angle compared to the coating with MMA. Both coatings were shown, by electrochemical impedance spectroscopy in 0.1 M NaCl solution, to act as barriers to protect the underlying substrate in which coating with EMA exhibits better protection properties after 2 months of immersion. Adhesion tests confirmed the highest grade of adhesion to the substrate for both coatings. Testing in a salt-spray chamber demonstrated excellent corrosion protection, where coatings remaining intact after more than 600 h of exposure.

Nanostructured Fe₂TiO₅ (pseudobrookite), a mixed metal oxide material holds significant promise for utilization in energy and environmental applications.