In the present study, we investigated the effect of an anode temperature on current transient process during porous anodic alumina growth and morphology of the anodic layers. Alumina films were formed in a 0.4 M oxalic acid at a constant voltage mode and electrolyte temperature. The temperature of the Al anode was controlled by thermoelectric Peltier element and varied in the range of 5 °C–60 °C. Surface morphology of both sides of anodic films and their cross-sections were analyzed by scanning electron microscopy (SEM) with subsequent statistical analysis of the SEM images by ImageJ software. It was found that when anode temperature was increased from 5 °С to 50 °С the pores diameter and interpore distance has not changed, but the porous structure became more ordered. According to these results, the rate of chemical dissolution of the barrier layer and pore walls did not depend on the anode temperature. At the anode temperature of 60 °С, pores diameter has increased 1.7 times and there was a distortion of the ordering of porous cells. It was concluded that the temperature difference between the aluminum substrate and electrolyte is an important parameter affecting the formation of ordered structure of nanoporous anodic alumina.

Herein, we investigate the potential application of a composite consisting of PEDOT:PSS/Graphene, deposited via spray coating on a flexible substrate, as an autonomous conducting film for applications in wearable biosensor devices. The stability of PEDOT:PSS/Graphene is assessed through electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV) and linear polarization (LP) during exposure to an artificial sweat electrolyte, while scanning electron microscopy (SEM) was employed to investigate the morphological changes in the layer following these. The results indicate that the layers exhibit predominant capacitive behavior in the potential range of −0.3 to 0.7 V vs. Ag/AgCl, with a cut-off frequency of approximately 1 kHz and retain 90% capacity after 500 cycles. Aging under exposure to air for 6 months leads only to a minor increase in impedance, demonstrating potential for storage under non-demanding conditions. However, prolonged exposure (>48 h) to the artificial sweat causes significant degradation, resulting in an impedance increase of over 1 order of magnitude. The observed degradation raises important considerations for the long-term viability of these layers in wearable biosensor applications, prompting the need for additional protective measures during prolonged use. These findings contribute to ongoing efforts to enhance the stability and reliability of conducting materials for biosensors in health care and biotechnology applications.