Using kukersite oil shale ash for the stabilization of organic-rich soils has been extensively studied but without much success. The main reason for this is the retarding effect of humic acids present in organic-rich soils on the formation of the C–S–H (calcium–silicate–hydrate) phase, which effectively prevents the solidification of cementitious materials in peat soils. Based on the studies performed at the University of Tartu, we have developed a novel method for the in situ mass stabilization of peat soils using waste materials (calcareous fly ash and silica fume). In this manner, the perfect hardening of peat–ash mixtures (to each 1 m³ of soil, 150–400 kg ash, 25–50 L pozzolanic additives, and 2.5–5 kaNaOH were added) can be achieved. A test road embankment was constructed under extremely hard conditions in a peat quarry that is currently in use.

Construction of road embankments in peatlands commonly involves replacement of the peat with a fill-up soil of an adequate load-bearing capacity. This usually requires a lowering of the water level, turning a peatland from a carbon sink to a source of greenhouse gases. Thus, alternatives are sought that are less costly in both economic and ecological terms. Mass-stabilization technology can provide a cheap substitute for Portland cement. Calcareous ashes (waste materials), supplemented with pozzolanic and alkali additives to facilitate and accelerate the setting and hardening processes, are attractive alternatives to soil excavation or replacement techniques. Silica fume and waterglass were used as pozzolanic agents and KOH as a soil-alkalizing agent. X-ray fluorescence (XRF), Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) analyses and stress–strain tests were performed for the hardened samples. Crystallization of alkali feldspars was observed in all test samples. Comparable hardening of peat soil was achieved for both ashes. It was shown that the ashes of Estonian kukersite (oil shale) from both pulverized firing and a circulating fluidized bed incineration process (produced in energy sector as quantitatively major solid waste in Estonia) can be used as binding agents for peat stabilization, even without the addition of Portland cement. Hardened peat soil samples behaved as a ductile material, and the cellulose fibers naturally present in peat gave the peat–ash composite plasticity, acting mechanically in the same way as the steel or glass fiber in ordinary reinforced concrete. The effect of peat fiber reinforcement was higher in cases of higher load and displacement of the composite, making the material usable in ecological constructions.

During roof renovations, large quantities of waste BBRM (bitumen-based roofing materials) are generated, and the possibilities for recycling these materials have so far been very limited. In general, they can be crushed and mixed with asphalt to pave roads or can be burned for energy. While waste plastic materials are often recycled, the remelting process significantly degrades their durability and mechanical properties. Unlike conventional methods, our recycling process results in a material with properties that are in many ways superior to the original materials. It is durable, weather resistant, and has exceptionally high mechanical strength. This material can be used to produce various construction components, including replacing quickly degradable wooden parts in structures. The composite material demonstrates increased flexibility, enhanced tensile strength, and improved resistance to ultraviolet (UV) radiation and environmental degradation compared to standard bitumen. The process is simple and can be carried out directly at the renovation site using a portable device.