Hydrophobic silica aerogel powder and hollow glass microspheres (HGM) were used as fillers for an epoxy adhesive to improve its thermal insulator properties. At 50 wt% of HGM content, the thermal conductivity of the HGM/epoxy composite decreased from 0.182 W/m·K to 0.104 W/m·K. The aerogel/epoxy composite, on the contrary, showed a slight increase in its thermal conductivity, most probably due to the filling of aerogel pores with the epoxy adhesive. Furthermore, it was shown that adhesion values of epoxy composites increase with the addition of aerogel and decrease when HGM was used as the filler material. Realistic numerical finite element method simulations revealed an increase in thermal isolation properties for both HGM/epoxy and aerogel/epoxy composites.

Pyrolysis is a promising way to reuse of waste tires. However, the carbon black generated in the process is often contaminated with various pyrolysis products. This study aims to recycle low-quality recycled carbon black (rCB) from waste tire pyrolysis, addressing the challenges posed by organic residues (up to 5 wt% bituminous substances, 112.2 mg/kg PAH). This causes the agglomeration of particles and decreases the active specific surface area. Cavitational vortex milling (both wet and dry) emerges as a promising method to valorize contaminated rCB, allowing for a significant reduction in the concentration of contaminants. This novel method allows for the generation of hydrophilic and hydrophobic black pigments. In parallel experiments, low-quality rCB is incorporated into solid biofuel to enhance its calorific value. The addition of 10 wt% rCB) to peat residues significantly elevates the calorific value from 14.5 MJ/kg to 21.0 MJ/kg. However, this improvement is accompanied by notable increases in CO₂ and SO₂ emissions. This dual effect underscores the necessity of considering environmental consequences when utilizing recycled carbon black as a supplement to solid biofuels. The findings provide valuable insights into the potential of cavitational vortex milling for carbon black valorization and highlight the trade-offs associated with enhancing biofuel properties through the addition of rCB.

Construction of road embankments in peatlands commonly involves replacement of the peat with a fill-up soil of an adequate load-bearing capacity. This usually requires a lowering of the water level, turning a peatland from a carbon sink to a source of greenhouse gases. Thus, alternatives are sought that are less costly in both economic and ecological terms. Mass-stabilization technology can provide a cheap substitute for Portland cement. Calcareous ashes (waste materials), supplemented with pozzolanic and alkali additives to facilitate and accelerate the setting and hardening processes, are attractive alternatives to soil excavation or replacement techniques. Silica fume and waterglass were used as pozzolanic agents and KOH as a soil-alkalizing agent. X-ray fluorescence (XRF), Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) analyses and stress–strain tests were performed for the hardened samples. Crystallization of alkali feldspars was observed in all test samples. Comparable hardening of peat soil was achieved for both ashes. It was shown that the ashes of Estonian kukersite (oil shale) from both pulverized firing and a circulating fluidized bed incineration process (produced in energy sector as quantitatively major solid waste in Estonia) can be used as binding agents for peat stabilization, even without the addition of Portland cement. Hardened peat soil samples behaved as a ductile material, and the cellulose fibers naturally present in peat gave the peat–ash composite plasticity, acting mechanically in the same way as the steel or glass fiber in ordinary reinforced concrete. The effect of peat fiber reinforcement was higher in cases of higher load and displacement of the composite, making the material usable in ecological constructions.

HydroThermal Liquefaction (HTL) is a process that involves the reaction of polymer compounds such as cellulose, lignin, synthetic plastics, etc. with near-critical or supercritical water to form low molecular weight liquid compounds, similar to natural oil which is believed to have formed over millions of years. Compared to other biomass recovery methods such as pyrolysis or anaerobic digestion, HTL is highly efficient with an energy efficiency of up to 90%, while the others have an efficiency of only around 30%. However, traditional HTL requires extremely high temperatures (250–450 °C) and pressures (100–350 bar), which are challenging to achieve using large-scale industrial equipment. This study proposes the use of ultrasonic cavitation to induce a supercritical state in water locally, rather than throughout the entire reactor, making it possible to perform HTL reactions using inexpensive and simple devices. The study demonstrates the successful conversion of pure cellulose to low molecular weight liquid compounds using potassium hydroxide as a catalyst.

The reductive pinacol coupling of aldimines was studied in respect to different coupling-mediators such as mischmetall, Zn–Cu couple and Devarda alloy. High diastereoselectivity was achieved for three substrates. A simple procedure for the preparation of 1,2-diamines is described.

Excellent regioselectivity is observed in the addition of diverse organometallic nucleophiles to unsymmetrical azo compounds. Primary/secondary/tertiary alkyl, aryl and heteroaryl substituents were introduced this way in high yields.