Results from the international cooperative programme on effects on materials including historic and cultural monuments are presented from the period 1987–2014 and include pollution data (SO₂, NO₂, O₃, HNO₃ and PM₁₀), corrosion data (carbon steel, weathering steel, zinc, copper, aluminium and limestone) and data on the soiling of modern glass for nineteen industrial, urban and rural test sites in Europe. Both one-year and four-year corrosion data are presented. Corrosion and pollution have decreased significantly and a shift in the magnitude is generally observed around 1997: from a sharp decrease to a more modest decrease or to a constant level without any decrease. SO₂ levels, carbon steel and copper corrosion have decreased even after 1997, which is more pronounced in urban areas, while corrosion of the other materials shows no decrease after 1997, when looking at one-year values. When looking at four-year values, however, there is a significant decrease after 1997 for zinc, which is not evident when looking at the one-year values. This paper also presents results on corrosion kinetics by comparison of one- and four-year values. For carbon steel and copper, kinetics is relatively independent of sites while other materials, especially zinc, show substantial variation in kinetics for the first four years, which needs to be considered when producing new and possibly improved models for corrosion.

This paper reports estimated maintenance-cleaning costs, cost savings and cleaning interval increases for structural surfaces and windows in Europe obtainable by reducing the air pollution. Methodology and data from the ICP-materials project were used. The average present (2018) cleaning costs for sheltered white painted steel surfaces and modern glass due to air pollution over background, was estimated to be ~2.5 Euro/m²∙year. Hypothetical 50% reduction in the air pollution was found to give savings in these cleaning costs of ~1.5 Euro/m²∙year. Observed reduction in the air pollution, from 2002–2005 until 2011–2014, have probably increased the cleaning interval for white painted steel with ~100% (from 12 to 24 years), representing reductions in the single intervention cleaning costs from 7 to 4%/year (= % of one cleaning investment, per year during the cleaning interval) and for the modern glass with ~65% (from 0.85 to 1.3 years), representing reductions in the cleaning cost from 124 to 95%/year. The cleaning cost reductions, obtainable by 50% reduction in air pollution, would have been ~3 %/year for white painted steel and ~60%/year for the modern glass, representing ~100 and 50% additional cleaning interval increases. These potential cleaning cost savings are significantly higher than previously reported for the weathering of Portland limestone ornament and zinc monuments.