Results from the international cooperative programme on effects on materials including historic and cultural monuments are presented from the period 1987–2014 and include pollution data (SO₂, NO₂, O₃, HNO₃ and PM₁₀), corrosion data (carbon steel, weathering steel, zinc, copper, aluminium and limestone) and data on the soiling of modern glass for nineteen industrial, urban and rural test sites in Europe. Both one-year and four-year corrosion data are presented. Corrosion and pollution have decreased significantly and a shift in the magnitude is generally observed around 1997: from a sharp decrease to a more modest decrease or to a constant level without any decrease. SO₂ levels, carbon steel and copper corrosion have decreased even after 1997, which is more pronounced in urban areas, while corrosion of the other materials shows no decrease after 1997, when looking at one-year values. When looking at four-year values, however, there is a significant decrease after 1997 for zinc, which is not evident when looking at the one-year values. This paper also presents results on corrosion kinetics by comparison of one- and four-year values. For carbon steel and copper, kinetics is relatively independent of sites while other materials, especially zinc, show substantial variation in kinetics for the first four years, which needs to be considered when producing new and possibly improved models for corrosion.

Malta is known for its limestone megalithic temples of which many are inscribed on the UNESCO World Heritage List. A variation of this limestone was historically, and until very few years ago, a primary building material in Malta. The temples are subject to various environmental influences which until recently have led to several collapses due in part to serious stone surface and infill loss. As a protection measure, open-sided shelters have been built over three of these temples. This work assesses the degrading influence of air pollution (nitrogen dioxide, ozone, particle matter, sulfur dioxide, and acidity in rain) on the temples, in combination and comparison with the influence of other environmental factors (relative humidity, temperature, precipitation, moisture, sea salt, wind) and in this respect evaluates the potential protective effect of the shelters. The variation in air pollution weathering of limestone exposed outdoor in Malta was calculated by exposure–response functions from the ICP-materials programme and compared with measured values, and its contribution to the deterioration of the temples was evaluated. The difference between urban and rural locations in Malta, in the first year of atmospheric chemical weathering of limestone due to air pollution, was found to be about one micrometer loss of stone surface. This is probably less than the annual variations due to the influence of natural climatic factors, and small compared to the present annual variations in continental Europe. The deposition of sea salt and presence of salts on and in the limestone megaliths and changes in salt-crystallization events due to relative humidity fluctuations, inside and outside the shelters, will account for more of the variations in the first year of weathering of Globigerina limestone than variations in air pollution. The deterioration will also be related to temperature (including condensation events), wind parameters and rainfall, as well as ground water replenished from areas beyond the shelter.

Air pollution is one of the environmental influences that degrade cultural heritage objects situated indoors. Other essential influences, such as temperature, relative humidity, and light are often well monitored. The presence of air pollutants is less often measured or included in risk assessment. The MEMORI^® technology presented in this paper was developed as a tool for easy measurement and assessment of the general risk of degradation of heritage objects situated indoors due to indoor exposure to air pollutants. MEMORI dosimetry was performed in locations belonging to English Heritage and Tate (both located in London) and the National Archives of Norway in Oslo, to assess air quality. The related damage risk for collection objects and the protection offered by display and storage designs was assessed. A high level of acidic effect was observed inside a number of showcases, and a high level of oxidizing effect was observed in some room locations. Relatively simple mitigation measures, such as constructing tightly sealed showcases using low emitting materials, installing active carbon absorbing media inside a ‘microclimate’ frame, and using cardboard storage boxes for paper, significantly improved air quality. Overall, implementation of such measures is likely to improve the preservation of objects and reduce conservation costs.

Assessment was performed of the air quality related risk to the conservation of cultural heritage objects in one urban and one rural indoor location in Romania, with expected different air quality related conservation challenges: the National military museum in Bucharest and the Tismana monastery in Gorj County. The work was performed within and subsequent to the EU-Memori project by applying Memori methodology, Memori^®-EWO (Early warning organic) dosimeters and passive pollution badge samplers for acetic and formic acids. The measurements in the National military museum were performed in three rooms with different exposure situations, and inside protective enclosures in the rooms. The rooms had organic and inorganic objects on exhibition and in store. The observed risks were associated with photo-oxidizing impact probably due to traffic pollutants entering from outdoor, and/or light exposure and temperature. The risks were found to be moderate, generally comparable to typical European purpose built museum locations. The highest risk was observed in a more open exhibition room in the main museum building. It was indicated that some observable change might happen to sensitive pigments and paper within 3 years, and to lead, copper and sensitive glass within 30 years in this location. Risk for observable change to sensitive pigments, paper, lead and sensitive glass within 30 years, was indicated in the other locations. The lowest risk was observed in a warehouse. A reduction in photo-oxidizing risk was measured in two of the enclosures, but a slightly higher acidic impact was measured in all the three enclosures, as compared to the respective rooms. In the Tismana monastery, a high level of acetic plus formic acid was observed in the air in the storerooms for icons and textiles, and books. Damage risk within 3 years was indicated for lead objects and sensitive glass, and within 30 years for iron and varnish (Laropal A81, resin mastic and dammar). As organic acid attack increases significantly at higher air humidity (> ~ 60%), this would be especially important to avoid. Risk for photo-oxidizing damage to paper and sensitive pigments within 30 years was indicated.