This study investigates the influence of solution treatment temperatures on the microstructure and mechanical properties of LPBF (Laser Powder Bed Fusion)-manufactured Inconel 939 alloy. The primary objectives are to assess the impact of sub-recrystallization (below recrystallization temperature) and recrystallization temperatures during solution treatment on mechanical performance under different conditions. This study validates the hypothesis concerning carbide redistribution and mechanical performance in LPBF-produced Inconel 939 parts through comprehensive analysis, including microstructure studies and tensile tests. The results indicate that higher heat treatment temperatures lead to significant changes in carbide redistribution and mechanical performance. For instance, at room temperature, the specimen with sub-recrystallization solution treatment temperature exhibited superior mechanical properties compared to both the as-built and recrystallization-temperature solution treatment specimens. However, at elevated temperatures (700 °C), a reversal in mechanical anisotropy was observed, with the vertical axis demonstrating higher tensile strength compared to the horizontal axis for all material states. Furthermore, a microstructural analysis revealed distinct changes in grain structure and precipitate distribution, particularly the migration of carbides from grain boundaries to intragranular regions. These findings underscore the importance of precise control over heat treatment parameters to achieve optimal mechanical behavior. This research provides valuable insights into optimizing LPBF processes for the Inconel 939 alloy, highlighting the need for a meticulous control of the solution treatment parameters to ensure mechanical integrity. The findings contribute to a broader understanding of material-specific responses in additive manufacturing, with significant implications for aerospace applications.

The paper investigates the influence of the ion-nitriding process on the microstructure, corrosion resistance, and tensile strength at elevated temperatures of Haynes 282 nickel superalloy specimens produced by the Direct Metal Laser Sintering (DMLS) technique. The study was performed for two conditions, i.e., as-built by DMLS method and as-built by DMLS method + covered by a layer containing CrN + Cr₂N phases. An analysis of the surface morphology revealed that the ion-nitriding process significantly affects the physical and chemical phenomena occurring on the specimen’s surface. The XRD measurement of the specimens showed that preparing them with the DMLS method as well as following a nitriding process produced residual tensile stresses. Based on the measurement of the nanohardness distribution through the layer approximatively of 7 μm in width and the superalloys substrate, the results of the nanohardness showed the maximum values of 27 GPa and 13.5 GPa for the nitrided layer and the substrate, respectively. The surface protection from the nitrided layer proved a positive effect on the corrosion resistance of the DMLS specimens in the solution of 0.1 M Na₂SO₄ + 0.1 M NaCl at room temperature. The results of the tensile tests at 750 °C showed that the ion-nitriding process did not significantly affect the elevated-temperature tensile strength of the superalloy specimens produced with the DMLS technique.

The paper investigates the influence of ion nitriding on the microstructure, corrosion resistance, and tensile strength at elevated temperatures of Haynes 282 nickel superalloy specimens produced by the Direct Metal Laser Sintering-DMLS technique. Analysis of the specimens’ surface morphology revealed that the ion nitriding process significantly affects the physical and chemical phenomena occurring on the surface of the specimens. Phase composition and stress analysis showed that Haynes 282 nickel alloy specimens produced by the DMLS technique and a chromium nitride layer produced in the ion nitriding process have tensile stress. The layer is also characterized by high nanohardness compared to specimens produced using the classical method (wrought) and DMLS technique. The conducted corrosion resistance tests confirmed the positive effect of the nitrided layer on the corrosion resistance of Haynes 282 nickel alloy produced by the DMLS technique. The ion nitriding process did not significantly affect the elevated-temperature tensile strength of Haynes 282 nickel alloy specimens produced by the DMLS technique.