As the technique of fiber-reinforced polymer (FRP) composite material strengthened reinforced concrete structures is widely used in the field of civil engineering, durability of the strengthened structures has attracted more attention in recent years. Hygrothermal environment has an adverse effect on the bond behavior of the interface between FRP and concrete. This paper focuses on the bond durability of carbon fiber laminate- (CFL-) concrete interface in hygrothermal condition which simulates the climate characteristic in South China. Twenty 100 mm × 100 mm × 720 mm specimens were divided into 6 groups based on different temperature and humidity. After pretreatment in hygrothermal environment, the specimens were tested using double shear method. Strain gauges bonded along the CFL surface and linear variation displacement transducers (LVDTs) were used to measure longitudinal strains and slip of the interface. Failure mode, ultimate capacity, load-deflection relationship, and relative slip were analyzed. The bond behavior of FRP-concrete interface under hygrothermal environment was studied. Results show that the ultimate bearing capacity of the interface reduced after exposure to hygrothermal environments. The decreasing ranges were up to 27.9% after exposure at high temperature and humidity (60°C, 95% RH). The maximum strains (εmax) of the specimens pretreated decreased obviously which indicated decay of the bond behavior after exposure to the hygrothermal environment.

With the prestressed carbon fiber reinforced polymer (CFRP) strengthening technique widely used in reinforced concrete (RC) structures, it is more and more important to study the fatigue performance of RC structures. Since the fracture of a tensile steel bar at the main cracked section is the leading reason for the failure of RC beams reinforced by prestressed CFRP, a fatigue life prediction model of RC beams reinforced by prestressed CFRP was developed based on an accumulative damage model. Moreover, gradual degradation of the performance of the concrete was considered in the fatigue life prediction model. An experimental study was also conducted to research the fatigue behavior of RC beams reinforced by prestressed or non-prestressed carbon fiber laminate (CFL). During the tests, fatigue crack patterns were captured using a digital image correlation (DIC) technique, and the fatigue lives of a total of 30 beams were recorded. The results showed that the predicted main crack propagation curves and the fatigue lives were close to the experimental data. This study also exhibited that the prestressed CFRP could reduce the stress of main steel bars in RC beams and effectively improve the fatigue performance of the RC beams.

Vehicle overload is detrimental to bridges and traffic safety. This paper presents a study on the fatigue performance of typical reinforced concrete (RC) beams of highway bridges under vehicle overload. A definition method of vehicle overload and a construction method of overload ladder spectrum were first proposed based on traffic data acquisition, statistical analysis and structural calculation of the highway bridges in Guangzhou. A fatigue experimental method was also proposed with the three-ladder vehicle overload spectrum, and the fatigue tests of 15 RC beams strengthened with carbon fiber reinforced polymer (CFRP) under three loading levels were then carried out. The fatigue performance and the failure mechanism of the strengthened beams were presented and discussed, and two fatigue life prediction methods were proposed with the established modified Palmgren-Miner rule and the loading level equivalent method respectively. The results showed that the fatigue performance of the strengthened RC beams was severely degraded under overload ladder spectrum compared with that under constant amplitude cyclic load, and the life prediction methods were proved effective.

Numerical and experimental methods were applied to investigate fatigue crack propagation behavior of reinforced concrete (RC) beams strengthened with a new type carbon fiber reinforced polymer (CFRP) named as carbon fiber laminate (CFL) subjected to hot-wet environment. J-integral of a central crack in the strengthened beam under three-point bending load was calculated by ABAQUS. In finite element model, simulation of CFL-concrete interface was based on the bilinear cohesive zone model under hot-wet environment and indoor atmosphere. And, then, fatigue crack propagation tests were carried out under high temperature and high humidity (50°C, 95% R · H) environment pretreatment and indoor atmosphere (23°C, 78% R · H) to obtain a-N curves and crack propagation rate, da/dN, of the strengthened beams. Paris-Erdogan formula was developed based on the numerical analysis and environmental fatigue tests.

A prestressing system was designed to strengthen reinforced concrete (RC) beams with prestressed carbon fiber laminate (CFL). During different prestressing processes, prestress loss was measured using strain gauges attached on the surface of CFL along the length direction. The prestress loss was 50–68% of the whole prestress loss, which is typically associated with CFL slipping between the grip anchors. Approximately 20–27% of the prestress loss was caused by the elastic shortening of the RC beam. An analytical model using linear-elastic theory was constructed to calculate the prestress loss caused by CFL slipping between the anchors and the elastic shortening of the strengthened beams. The compared results showed that the analytical model of prestress loss can describe the experimental data well. Methods of reducing the prestress loss were also suggested. Compared to other experiments, the prestressing system proposed by this research group was effective because the maximum percentage of prestress loss was 14.9% and the average prestress loss was 12.5%.

In recent years, numerous studies have explored the benefits of utilizing prestressed carbon fiber-reinforced polymer (CFRP) for strengthening concrete structures. However, research on the reinforcement of prestressed CFRP on full-scale hollow RC box girders, particularly damaged bridges, remains limited. In this study, both experiments and finite element analysis (FEA) were performed to investigate the flexural behavior of full-scale hollow RC box girders with varying degrees of damage, which were strengthened using CFRP with different levels of prestress. The adhesive behavior of the CFRP–concrete interface was considered in the FEA. Numerical simulations were conducted to assess the flexural behaviors of the girders, including failure modes, yield and ultimate loads, and deflections. The results revealed that the application of prestressed CFRP efficiently increased the yield and ultimate loads of the box girders. Specifically, when the degree of damage of the hollow box girder was less than 23%, the flexural bearing capacity of the repaired girder could be recovered after being strengthened with two prestressed CFRP strips measuring 50 mm in width and 3 mm in thickness. However, the risk of premature debonding at the CFRP–concrete interface increased when the prestressing level of CFRP and degree of damage of hollow RC box girders exceeded 35% and 40%, respectively. These findings suggest that the use of prestressed CFRP may be a promising method for repairing damaged hollow RC box girders, but careful consideration of the degree of damage and prestressing level would be necessary to ensure the effectiveness and safety of the repair.