The bonding interface between the CFRP and the steel plate is the weak link of CFRP-strengthened steel structures. This paper studies the bond–slip relationship of the CFRP–steel interface by experiments and numerical tests. First, a series of double-strap experiments on a CFRP-strengthened steel plate are carried out. The results show that the maximum shear stress of the bonding interface of the Q345B specimen is larger than that of the X100 specimen. The initial slip and maximum slip become larger as the thickness of the bonding interface becomes larger. Finite element analysis of the above tests is carried out; we introduce the maximum stress criterion to simulate the bonding interface, which assumes that when the nominal stress of the material reaches the maximum nominal stress of damage, the material begins to damage. The FE model established has proved very effective for analyzing the bond characteristics of CFRP-strengthened steel plates. Finally, a verification test was carried out, using an FE analysis to verify the accuracy of the modified equations; the results prove that the results of the modified equations are in good agreement with the numerical results and experiment results, which verifies the effectiveness of the equations.

With the prestressed carbon fiber reinforced polymer (CFRP) strengthening technique widely used in reinforced concrete (RC) structures, it is more and more important to study the fatigue performance of RC structures. Since the fracture of a tensile steel bar at the main cracked section is the leading reason for the failure of RC beams reinforced by prestressed CFRP, a fatigue life prediction model of RC beams reinforced by prestressed CFRP was developed based on an accumulative damage model. Moreover, gradual degradation of the performance of the concrete was considered in the fatigue life prediction model. An experimental study was also conducted to research the fatigue behavior of RC beams reinforced by prestressed or non-prestressed carbon fiber laminate (CFL). During the tests, fatigue crack patterns were captured using a digital image correlation (DIC) technique, and the fatigue lives of a total of 30 beams were recorded. The results showed that the predicted main crack propagation curves and the fatigue lives were close to the experimental data. This study also exhibited that the prestressed CFRP could reduce the stress of main steel bars in RC beams and effectively improve the fatigue performance of the RC beams.

Vehicle overload is detrimental to bridges and traffic safety. This paper presents a study on the fatigue performance of typical reinforced concrete (RC) beams of highway bridges under vehicle overload. A definition method of vehicle overload and a construction method of overload ladder spectrum were first proposed based on traffic data acquisition, statistical analysis and structural calculation of the highway bridges in Guangzhou. A fatigue experimental method was also proposed with the three-ladder vehicle overload spectrum, and the fatigue tests of 15 RC beams strengthened with carbon fiber reinforced polymer (CFRP) under three loading levels were then carried out. The fatigue performance and the failure mechanism of the strengthened beams were presented and discussed, and two fatigue life prediction methods were proposed with the established modified Palmgren-Miner rule and the loading level equivalent method respectively. The results showed that the fatigue performance of the strengthened RC beams was severely degraded under overload ladder spectrum compared with that under constant amplitude cyclic load, and the life prediction methods were proved effective.

Self-compacting lightweight concrete is a kind of high-performance concrete developed from self-compacting concrete and lightweight aggregate concrete. Describing the crack propagation accurately is important in studying the fracture performance of this concrete structure. This paper presents a simulation study on the fracture process for self-compacting lightweight concrete (SCLC) by the extended finite element method (XFEM). Following an introduction of the basic principle of XFEM, a fracture model of self-compacting lightweight concrete beam with initial crack is established based on XFEM. The beam is subjected to three-point bending load and the criterion of maximum tensile stress for traction damage is used as the Crack criterion. The bending results of crack mouth opening displacements (CMOD) and stresses under different loading levels are calculated and compared with some existing theoretical and experimental results. Furthermore, influences of secondary cracks, crack-depth and crack-distance on the fracture process are discussed. The research results indicate that the beam's fracture is controlled by the main crack located in the mid-span when the crack-depths of the secondary cracks smaller than the main cracks.