In this work, Sr_0.3Ba_0.4Pb_0.3Fe₁₂O₁₉/(CuFe₂O₄)_x (x = 2, 3, 4, and 5) as strongly exchange-coupled nanosized ferrites were fabricated using a one-pot sol–gel combustion method (citrate sol-gel method). The X-ray diffraction (XRD) powder patterns of the products confirmed the occurrence of pure, exchange-coupled ferrites. Frequency dependencies of the microwave characteristics (MW) were investigated using a co-axial method. The non-linear behavior of the MW with the composition transformation may be due to different degrees of Fe ion oxidation on the spinel/hexaferrite grain boundaries and strong exchange coupling during the hard and soft phases.

The wet chemical processing opens the way to deposit thin film with the versatility and ease for a variety of materials. Liquid film deposition involves the application of a liquid precursor on a substrate which is then converted to the required coating material in a subsequent post-treatment step. Different non-vacuum solution based deposition techniques have been developed to grow thin films with high efficiency and functionality. Spin coating is one of an effective technique for thin film fabrication due to low cost, uniformity, less hazardous, and capability of easy scaling up. The typical process involves depositing a small amount of a fluid onto the center of a substrate and then spinning the substrate at high speed. Dip coating is another simple, cost effective route with feasibility to scale-up for commercial production. The dip coating process can be divided into three important technical stages, immersion, withdrawal and evaporation. The coating may be subjected to further heat treatment in order to burn out residual compounds and induce crystallization of the functional oxides. Spray coating is a promising technique to grow thin film in research and industry to prepare thin and thick films. It is an easy approach to fabricate thin film with uniform distribution at small scale from a few nanometers to micrometers in thickness. Inkjet printing is the emerging promising technique to develop large-scale, and flexible thin films. The inkjet printing process allow easy customization to grow variety of complex structures.

The growth of multi-walled carbon nanotubes (MWCNTs) has been extensively studied using electron microscopy. The ex situ structural behavior was examined to investigate the growth of the MWCNTs under different environments and pressures using electron microscopy. The arc discharge plasma technique was applied to synthesize the MWCNTs by evaporating carbon through the arc plasma between two cylindrical graphite rods, with a background pressure of 10⁻² to 10² mbar, inside a vacuum chamber under different ambient environments. The results showed that long MWCNT structures were successfully grown. We suggest that the mechanism involves: (i) fullerene formation; (ii) the elongation of fullerenes; and (iii) the growth of MWCNTs. Agglomeration with other structures then forms MWCNT bundles. We note that the pressure and environment in the vacuum chamber can affect the structure of the MWCNTs.

Hydroxyapatite has been extensively used as a potential biocompatible ceramic in many orhtopedic applications. Hydroxyapatite is one of the members of calcium phosphate family and been used extensively as a bone substitute. The mechanical properties of hydroxyapatite itself, ceramics and bone cements prepared from hydroxyapatite vary greatly with slight variation in its Ca/P ratio. At present EDX, XRD, XRF and ICP-OES are being used for the determination of Ca/P ratio in hydroxyapatite. These techniques require special sample preparation, may also use toxic chemicals and usually are not very fast in giving the measurements. We report LIBS as a rapid alternative technique for calculation of Ca/P ratio in hydroxyapatite extracted from bovine bone (BHA). Ca/P ratio in laboratory prepared HA is calculated using LIBS and the results are validated against EDX results Ca/P ratio of the hydroxyapatite was calculated as 1.54±0.19 using LIBS while 1.63±0.03 using EDX. Ca/P ratio calculated by LIBS and EDX and showed comparable results with a difference of 5.5%. Moreover, plasma temperature and the ratio of the calcium (ion) line to calcium (atomic) line did not show significant variation in plasma conditions during measurements. The present study has demonstrated that LIBS can also be used for the determination of Ca/P ratio of hydroxyapatite and other calcium phosphates. At the request of all authors of the paper, and with the agreement of the Proceedings Editor, an updated version of this article was published on 24 May 2017.