High-performance electromagnetic interference (EMI) shielding materials with ultralow density and environment-friendly properties are greatly demanded to address electromagnetic radiation pollution. Herein, carbon nanotube/polylactic acid (CNT/PLA) materials with different CNT contents, which exhibit characteristics of light weight, environmental protection and good chemical stability, are fabricated using 3D printing technology, where CNTs are evenly distributed and bind well with PLA. The performances of 3D-printed CNT/PLA composites are improved compared to pure 3D-printed PLA composites, which include mechanical properties, conductive behaviors and electromagnetic interference (EMI) shielding. The EMI shielding effectiveness (SE) of CNT/PLA composites could be improved when the content of CNTs increase. When it reaches 15 wt%, the EMI SE of 3D-printed CNT/PLA composites could get up to 47.1 dB, which shields 99.998% of electromagnetic energy. Meanwhile, the EMI shielding mechanism of 3D-printed CNT/PLA composites is mainly of absorption loss, and it generally accounts for more than 80% of the total shielding loss. These excellent comprehensive performances endow a 3D-printed CNT/PLA composite with great potential for use in industrial and aerospace areas.

Composites with excellent thermomechanical and thermochemical properties are urgently needed in the aerospace field, especially for structural applications under high-temperature conditions. Carbon fiber-reinforced Si-based composites are considered the most promising potential high-temperature materials due to their excellent oxidation resistance and ablative behaviors, good structural designability, and excellent mechanical properties. The reinforcement of the relevant composites mainly involves carbon fiber, which possesses good mechanical and temperature resistance abilities. In this paper, the ablation behaviors and mechanisms of related composites are reviewed. For carbon fiber-reinforced pure Si-based composites (C/SiM composites), the anti-ablation mechanism is mainly attributed to the continuous glassy SiO₂, which inhibits the damage of the substrate. For C/SiM composite doping with refractory metal compounds, the oxides of Si and refractory metal together protect the main substrate from ablation and oxidation. Moreover, in addition to thermochemical damage, thermophysical and thermomechanical behavior severely destroy the surface coating of the substrate.

Porous carbon nanofibers (PCNFs) with excellent physical and chemical properties have been considered candidate materials for electrodes used in supercapacitors. Herein, we report a facile procedure to fabricate PCNFs through electrospinning blended polymers into nanofibers followed by pre-oxidation and carbonization. Polysulfone (PSF), high amylose starch (HAS), and phenolic resin (PR) are used as three different kinds of template pore-forming agents. The effects of pore-forming agents on the structure and properties of PCNFs have been systematically studied. The surface morphology, chemical components, graphitized crystallization, and pore characteristics of PCNFs are analyzed by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and nitrogen adsorption and desorption test, respectively. The pore-forming mechanism of PCNFs is analyzed by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Fabricated PCNF-R have a specific surface area as high as ~994 m²/g, a total pore volume as high as ~0.75 cm³/g, and a good graphitization degree. When PCNF-R are used as active materials to fabricate into electrodes, the PCNF-R electrodes show a high specific capacitance ~350 F/g, a good rate capability ~72.6%, a low internal resistance ~0.55 Ω, and an excellent cycling stability ~100% after 10,000 charging and discharging cycles. The design of low-cost PCNFs is expected to be widely applicable for the development of high-performance electrodes for an energy storage field.

Recently, short-fiber-reinforced thermoplastic composites (SFRTPCs) have been playing a more and more crucial role in the application of automotive interior materials due to their advantages of low density and environmental resistance properties. However, their relevant mechanical properties need to be optimized. Previous investigations revealed that the surface modification of fibers is useful to improve their mechanical properties. In this work, carbon fiber (CF)-reinforced polylactic acid (PLA) composites modified with MXene and graphene oxide (GO) were prepared by twin-screw extrusion and injection molding methods. Short CF was firstly modified with polyetherimide (PEI), then different weight ratios of MXene-GO (1:1) were subsequently modified on PEI-CF. Finally, the flexural properties and failure mechanisms were analyzed. The results showed that MXene-GO was successfully coated on CF surface, and the flexural strength and modulus of CF-PEI-MXene-GO-reinforced PLA (CF-PEI-MG/PLA) composite were improved compared to that of CF/PLA composite. In addition, the fracture sections of the composites were flat and white, and the fibers bonded well with PLA for CF-PEI-0.1MG/PLA composite compared to CF/PLA composite. The present study could provide a reference for further improving the mechanical performance of PLA-related composites.