Durable electromagnetic interference (EMI) shielding is highly desired, as electromagnetic pollution is a great concern for electronics’ stable performance and human health. Although a superhydrophobic surface can extend the service lifespan of EMI shielding materials, degradation of its protection capability and insufficient self-healing are troublesome issues due to unavoidable physical/chemical damages under long-term application conditions. Here, we report, for the first time, an instantaneously self-healing approach via microwave heating to achieve durable shielding performance. First, a hydrophobic 1H,1H,2H,2H-perfluorooctyltriethoxysilane (POTS) layer was coated on a polypyrrole (PPy)-modified fabric (PPy@POTS), enabling protection against the invasion of water, salt solution, and corrosive acidic and basic solutions. Moreover, after being damaged, the POTS layer can, for the first time, be instantaneously self-healed via microwave heating for a very short time, i.e., 4 s, benefiting from the intense thermal energy generated by PPy under electromagnetic wave radiation. This self-healing ability is also repeatable even after intentionally severe plasma etching, which highlights the great potential to achieve robust and durable EMI shielding applications. Significantly, this approach can be extended to other EMI shielding materials where heat is a triggering stimulus for healing thin protection layers. We envision that this work could provide insights into fabricating EMI shielding materials with durable performance for portable and wearable devices, as well as for human health care."Image missing"<!-- image only, no MathML or LaTex -->

Organic montmorillonite (MMT) modified by 1,3-dihexadecyl-3H-benzimidazolium bromide (Bz) was used to prepare polyphenylene sulfide (PPS)/MMT composites by melting intercalation. The PPS/MMT composites showed mixed morphology, being comprised of exfoliated and intercalated structures with slight agglomerates. The tensile property of PPS/MMT composites was significantly improved due to the good dispersion of the MMT nanolayers. The test results showed that the tensile strength retention of PPS/MMT composites was higher than that of pure PPS after the oxidation treatment. Moreover, FTIR and XPS analyses were also used to evaluate the oxidation resistance of PPS composites. The FTIR analysis confirmed that adding MMT could better limit the damage of the C–S group and retard the generation of sulfuryl groups (–SO₂–) during the oxidation treatment compared to pure PPS. The XPS analysis also suggested that the addition of MMT could reduce the chemical combination of the elements sulfur (S) and oxygen (O) during oxidation treatment. Furthermore, the MMT nanolayers could also promote the transfer of S from a C–S bond into an –SO₂– group.

To investigate the influences of quaternization/hydroxypropylsulfonation on viscosity stability, adhesion to fibers and film properties of oxidized tapioca starch (OTS) for ameliorating its end-use ability in applications such as warp-sizing and paper-making, a series of quaternized and hydroxypropylsulfonated OTS (QHOTS) samples were synthesized by simultaneous quaternization and hydroxypropylsulfonation of OTS with N-(3-chloro-2-hydroxypropyl) trimethylammonium chloride (CHPTAC) and 3-chloro-2-hydroxy-1-propanesulfonic acid sodium salt (CHPS-Na). The QHOTS granules were characterized by Fourier transform infra-red spectroscopic and scanning electron microscope techniques. Apparent viscosity and viscosity stability were determined, and adhesion was evaluated by measuring the bonding force of starch to the fibers. Film properties were also estimated in terms of tensile strength, breaking elongation, bending endurance, degree of crystallinity, and moisture regain. It was showed that quaternization/hydroxypropylsulfonation was capable of obviously improving viscosity stability of gelatinized OTS paste, enhancing bonding forces of OTS to cotton and polylactic acid (PLA) fibers, increasing breaking elongation, bending endurance and moisture regain of film and decreasing its tensile strength and degree of crystallinity, thereby obviously stabilizing paste viscosity, improving adhesion to fibers and lessening film brittleness. Increasing the level of quaternization/hydroxypropylsulfonation favored improvement in the stability, enhancement in adhesion and decrease in brittleness. The QHOTS showed potential in the applications of cotton and PLA sizing.

High-performance electromagnetic interference (EMI) shielding materials with ultralow density and environment-friendly properties are greatly demanded to address electromagnetic radiation pollution. Herein, carbon nanotube/polylactic acid (CNT/PLA) materials with different CNT contents, which exhibit characteristics of light weight, environmental protection and good chemical stability, are fabricated using 3D printing technology, where CNTs are evenly distributed and bind well with PLA. The performances of 3D-printed CNT/PLA composites are improved compared to pure 3D-printed PLA composites, which include mechanical properties, conductive behaviors and electromagnetic interference (EMI) shielding. The EMI shielding effectiveness (SE) of CNT/PLA composites could be improved when the content of CNTs increase. When it reaches 15 wt%, the EMI SE of 3D-printed CNT/PLA composites could get up to 47.1 dB, which shields 99.998% of electromagnetic energy. Meanwhile, the EMI shielding mechanism of 3D-printed CNT/PLA composites is mainly of absorption loss, and it generally accounts for more than 80% of the total shielding loss. These excellent comprehensive performances endow a 3D-printed CNT/PLA composite with great potential for use in industrial and aerospace areas.