Forecasting the results of hybrid laser-plasma cutting of carbon steel

The object of this study is the formation of intermetallic phases (IMPhs) in the heat-affected zone (HAZ) of joints of steel–titanium bimetal plates produced by arc welding. A titanium layer (2 mm) was welded by the plasma method (PAW), a barrier layer of Cusi3Mn1 bronze was deposited on it by the TIG method, the first steel layer was deposited by CMT, and Puls-MAG was used for filling the groove. Here, heating in the solid phase takes place in the HAZ, which may lead to undesirable formation of brittle IMPhs and further welded joint failure. Mathematical modeling was performed and metallurgical features formed during the processes of heating of the HAZ in bimetal steel–titanium plates were studied to identify the risk of IMPh formation. It was found that at a temperature increase from 900 to 1450 °C, a continuous intermetallic layer formed on the steel–titanium interface, which contained FeTi IMPh, and the width of which increased from 1 to 10 μm. In the temperature range 1300…1430 °C, an intermetallic TiFe₂-type phase additionally formed from the titanium side. In the temperature range 1430…1450 °C, the TiFe₂ phase was replaced by the TiXFe phase, which formed both from the steel side and from the titanium side. This phase consists of intermetallics (73–75% Ti + 27–25% Fe) and (80–85% Ti + 20–15% Fe), and it is close to the Ti₂Fe-type phase. The interlayer of intermetallics, formed at temperatures of 900…1300 °C, has a continuous morphology (HV0.01–650…690). At temperatures rising above 1300 °C, the IMPh interlayer became more ramified (HV0.01–590…610) because of the formation of a larger number of pores and microcracks within it. In the temperature range 900…1450 °C, solid-phase diffusion proceeded in the steel–titanium bimetal near the interface of the two metals. A zone of iron diffusion, 5–10 μm to 40–60 μm in width, formed in titanium. In steel, a zone of titanium diffusion 15–20 μm to 120–150 μm in width formed, starting from 1300 °C and higher. It is recommended to perform industrial welding of steel–titanium bimetal in modes, for which the heat input is equal to 200…400 J/mm. Here, during the period 10–12 s, the heating temperature of the HAZ 1.5–3.5 mm in width is equal to 900–1150 °C. It promotes formation of an intermetallic FeTi-type interlayer of up to 1–2 μm width.

The objective of this study is to investigate the formation of the structure and stress–strain state in the joints of AISI 304 stainless steel with a thickness of 2 mm and produced by welding with laser and plasma energy sources. It is established that the microhardness and parameters of the grain and subgrain structures of the welded joint material differ with respect to the dimensions of crystallites, grains, and subgrains according to the welding process. It is shown that, in terms of structure formation, including substructural features, the most favorable structures of 2 mm AISI 304 welded joints are formed by laser–plasma welding. It is predicted that the residual stressed state is less localized with the application of laser–plasma welding than laser welding, and it is characterized by a lower level of residual stresses compared to plasma welding. In all the cases, the maximal stress values are concentrated in the HAZ, and the value obtained using laser–plasma welding is in an intermediate position (431.7 MPa) between those of the laser (443 MPa) and plasma (413.7 MPa) processes. With laser–plasma and laser welding, displacements (deformations) are minimal and close to 0.2 mm. The method of electron speckle interferometry was used, and the results reveal that the error between the calculated and experimental values of equivalent stresses is no more than 6%, which is acceptable. The results of mechanical testing show that, under uniaxial tension, the strength of the welded joints made of AISI 304 steel using laser–plasma and laser welding is the highest and equal to 97% of that of the base metal.

The objective of this study was the additive microplasma powder deposition of 3D metal products. The regularities of the influence of technological parameters of additive microplasma deposition of spatial objects using the powder filler material of a Fe–Cr–Ni–B–Si system on the formation of the microstructure and stress–strain state of 3D product material were studied in this work. Product walls with a layered metal structure with a deposited layer height of about 650 µm and 3.0–3.5 mm thickness were formed as a result of additive microplasma deposition of the HYF–103 powder of a Fe–Cr–Ni–B–Si system. The deposited metal ensured a high ultimate strength (above 600 MPa). The finite element method was used to derive the solution of the thermomechanical problem of additive deposition of 3D prototypes («cylinder», «triangular prism», «square prism», «reverse cone», «straight cone») with HYF–103 powder. The equivalent stresses of the highest magnitude (565 MPa) were predicted in the model sample of the “reverse cone” type, and the lowest stresses (552 MPa) were present in the sample of the “straight cone” type. For all the models, the maximal values of radial movements corresponded to the range of 0.22–0.28 mm. The respective technological mode of deposition was selected to minimize the stress–strain state of the produced 3D objects.

Automatic Welding, 2024, №02. Journal «AVTOMATICHESKAYA SVARKA» Monthly scientific-technical and production journal. ISSN: 0005-111X, Since 1948. Russian version of «The PATON Welding Journal» Text in Russian, contents and summaries in English. The Journal presents a wide range of scientific-technical and promotion information in the field of technologies, equipment and materials for welding, surfacing, brazing, and deposition of protective coatings.

The Paton Welding Journal, 2024, №04. International Scientific-Technical and Production Journal «The Paton Welding Journal» «The Paton Welding Journal» has been published monthly since 2000 in English, ISSN 0957-798X. «The Paton Welding Journal» is a cover-to-cover English translation of the «Avtomaticheskaya Svarka» (Automatic Welding) journal. The «Avtomaticheskaya Svarka» journal has been published monthly since 1948 in Russian, ISSN 005-111X.