In this work, we have obtained colloidal solutions of Si nanocrystals (Si-ncs), starting from free-standing porous silicon (PSi) layers. PSi layers were synthesized using a two-electrode Teflon electrochemical cell; the etching solution contained hydrogen peroxide 30%, hydrofluoric acid 40% (HF), and methanol. The anodizing current density was varied to 250 mA cm-2, 1 A cm-2, and 1.2 A cm-2. Thus obtained, PSi was mechanically pulverized in a mortar agate; then, the PSi powders were poured into different solutions to get the final Si-ncs colloidal solutions. The different optical, morphological, and structural characteristics of the colloidal solutions with Si-ncs were measured and studied. These Si-ncs colloidal solutions, measured by photoluminescence (PL), revealed efficient blue-green or violet emission intensities. The results of X-ray diffraction (XRD) indicate that the colloidal solutions are mainly composed of silicon nanocrystallites. The result of UV–vis transmittance indicates that the optical bandgap energies of the colloidal solutions varied from 2.3 to 3.5 eV for colloids prepared in methanol, ethanol, and acetone. The transmission electron microscopy (TEM) images showed the size of the nanocrystals in the colloidal solutions. Fourier transform infrared spectroscopy (FTIR) spectra showed different types of chemical bonds such as Si-O-Si, Si-CH2, and SiH x , as well as some kind of defects.

Hydroxyapatite (HAp) and hydroxyapatite/multi-walled carbon nanotube (MWCNT) composites were obtained by the co-precipitation method, followed by ultrasound-assisted and microwave radiation and thermal treatment at 250 °C. X-ray diffraction (XRD) confirmed the presence of a hexagonal phase in all the samples, while Fourier-transform infrared (FTIR) spectroscopy elucidated the interaction between HAp and MWCNTs. The photoluminescent technique revealed that HAp and the composite with non-functionalized MWCNTs present a blue luminescence, while the composite with functionalized MWCNTs, under UV-vis radiation shows an intense white emission. These findings allowed presentation of a proposal for the use of HAp and HAp with functionalized MWCNTs as potential materials for optoelectronic and medical applications.

Zinc oxide is one of the most important semiconducting metal oxides and one of the most promising n-type materials, but its practical use is limited because of both its high thermal conductivity and its low electrical conductivity. Numerous studies have shown that doping with metals in ZnO structures leads to the modification of the band gap energy. In this work, Al-doped ZnO, Ni-doped ZnO, and undoped ZnO nanocrystalline powders were prepared by a sol–gel method coupled with ultrasound irradiation, and the results show the influence of Al³⁺ and Ni²⁺ ions in the ZnO network. The doping concentrations in ZnO of 0.99 atom % for ZnO–Al and 0.80 atom % for ZnO–Ni were obtained by X-ray Fluorescence (XRF). X-ray Diffraction (XRD) and Raman Spectroscopy showed a decreased intensity and broadening of main peaks, indicating metallic ions. The crystallite size of the sample was decreased from 24.5 nm (ZnO) to 22.0 nm (ZnO–Al) and 21 nm (ZnO–Ni). The textural and morphological properties were analyzed via Nitrogen Adsorption (BET method) and Field Emission Scanning Electron Microscopy (FESEM).

Bioceramic materials, such as hydroxyapatite, Ca₁₀(PO₄)₆(OH)₂, (HAp), can be chemically bound to bone tissue; since they are bioactive and biocompatible. HAp, titanium oxide (TiO₂), and hydroxyapatite/titanium oxide (HAp/TiO₂) nanocomposite nanoparticles were obtained by ultrasound irradiation assisted by sol-gel and co-precipitation methods at different time intervals, using Ca(NO₃)₂•4H₂O, (NH₄)₂HPO₄, and TiOSO₄•xH₂O as calcium, phosphorus, and titanium sources, respectively. HAp, TiO₂, and HAp/TiO₂ nanocomposite powders were characterized by X-ray Diffraction (XRD) and Raman Spectroscopy. The percentages of anatase phase for TiO₂ and of monoclinic and hexagonal phases for HAp were quantified by Rietveld refinement. Furthermore, sample crystallinity in each material was enhanced by increasing the ultrasound irradiation time. The nanoparticle shape was semi-spherical, agglomerated, and between 17 and 20 nm in size. The agglomeration of particles in the samples was corroborated with a Field Emission Scanning Electron Microscope (FESEM).

In systems in atomic scale and nanoscale such as clusters or agglomerates constituted by particles from a few to less than 100 atoms, quantum confinement effects are very important. Their optical and electronic properties are often dependent on the size of the systems and the way in which the atoms in these clusters are bonded. Generally, these nanostructures display optical and electronic properties significantly different to those found in corresponding bulk materials. Silicon agglomerates embedded in silicon rich oxide (SRO) films have optical properties, which have been reported to be directly dependent on silicon nanocrystal size. Furthermore, the room temperature photoluminescence (PL) of SRO has repeatedly generated a huge interest due to its possible applications in optoelectronic devices. However, a plausible emission mechanism has not been widely accepted in the scientific community. In this work, we present a short review about the experimental results on silicon nanoclusters in SRO considering different techniques of growth. We focus mainly on their size, Raman spectra, and photoluminescence spectra. With this as background, we employed the density functional theory with a functional B3LYP and a basis set 6-31G* to calculate the optical and electronic properties of clusters of silicon (constituted by 15 to 20 silicon atoms). With the theoretical calculation of the structural and optical properties of silicon clusters, it is possible to evaluate the contribution of silicon agglomerates in the luminescent emission mechanism, experimentally found in thin SRO films.