Electropolishing at high current densities without agitation of the electrolyte results in a pitting phenomenon that produces dimple-like surface features. Although pitting is unfavorable in the electropolishing process, its effect on surface modification, such as surface texturing, has not been thoroughly investigated. Surface topography and chemical composition analyses of electropolished steel revealed surface pits and an oxide surface layer, indicating the presence of surface texture and coating. The resulting surface is characterized by negative skewness and high kurtosis values. The tribological behavior of the electropolished steel-bronze pair is investigated by evaluating coefficients of friction and bronze wear using sliding tests conducted in mixed and boundary lubrication regimes. The results are compared to those of the ground steel-bronze pair. In the mixed and upper range of the boundary lubrication regime, coefficients of friction reduction up to 30% and shorter running-in phases are observed for electropolished steel (electropolished steel μ_avg = 0.019 vs. ground steel μ_avg = 0.028). In contrast, the coefficient of friction increased in the lower range of boundary lubrication regime by 50% (electropolished steel μ_avg = 0.098 vs. ground steel μ_avg = 0.065). Electropolishing, as a cost- and time-effective method applicable to complex geometries, presents an alternative method for achieving surface modifications aimed at friction reduction and improved tribological behavior for non-conformal contacts in the boundary and mixed lubrication regimes.

Electropolishing using a high-current density results in a pitting phenomenon, producing a surface texture distinguished by many pits. Apart from the change in surface topography, electropolishing forms an oxide surface layer characterized by beneficial tribological properties. This paper introduces surface texturing in worm gear pairs by electropolishing a 16MnCr5 steel worm surface. Electropolishing produces surface pits 1 μm to 5 μm deep and 20 to 100 μm in diameter. The material characterization of 16MnCr5 steel is compared against the electropolished 16MnCr5 steel based on microstructure, hardness, surface topography and chemical composition. Experimental tests with worm pairs employing electropolished worms are conducted, and the results are compared to conventional worm pairs with ground steel worms. Electropolished worms show up to 5.2% higher efficiency ratings than ground ones and contribute to better running-in of worm gear pairs. Moreover, electropolished worms can reliably support full contact patterns and prevent scuffing due to improved lubrication conditions resulting from the produced surface texture and oxide surface layer. Based on the obtained results, electropolishing presents a promising method for surface texturing and modification in machine elements characterized by highly loaded non-conformal contacts and complex geometry.