The effect of heat treatment at various temperatures (650, 850, 1050, and 1100°C) and dwell times (10 min and 1 h) on the metallurgical and microstructural evolution as well as on the related tensile properties of stainless steel 316L processed by selective laser melting (SLM) has been systematically evaluated. The metallurgical and microstructural features such as defects, stability of the columnar–cellular structure and substructure, second phase particles, and phase transformation imparted by SLM and heat treatment have been discussed. It has been shown that the processing conditions specific to SLM significantly alter the kinetics of phase evolution compared to standard welding techniques which affects the accuracy of the prediction. The influence of these characteristics on tensile properties and hardness was elucidated. It was disclosed that with increasing heat treatment temperature there was a gradual increase in elongation but a decrease in strength related to the dislocation density and the development of the microstructure.

Intermetallic Fe₃Al-based alloys reinforced with Laves-phase precipitates are emerging as potential replacements for conventional high-alloy steels and possibly polycrystalline Ni-based superalloys in structural applications up to 700 °C. Their impressive mechanical properties, however, are offset by limited fabricability and poor machinability due to their severe brittleness. High tool wear during finish-machining, which is still required for components such as turbine blades, remains a key barrier to their broader adoption. In contrast to conventional manufacturing routes, additive manufacturing offers a viable solution by enabling near-net-shape manufacturing of difficult-to-machine iron aluminides. In the present study, laser powder bed fusion was used to produce an Fe-25Al-1.5Ta intermetallic containing strengthening Laves-phase precipitates, and the porosity, microstructure and phase composition were characterized as a function of the process parameters. The results showed that preheating the build plate to 650 °C effectively suppressed delamination and macrocrack formation, even though noticeable cracking still occurred at the high scan speed of 1000 mm/s. X-ray tomography revealed that samples fabricated with a lower scan speed (500 mm/s) and a higher layer thickness (0.1 mm) contained larger, irregularly shaped pores, whereas specimens printed at the same volumetric energy density (40 J/mm³) but with different parameter sets exhibited smaller fractions of predominantly spherical pores. All samples contained mostly elongated grains that were either oriented close to relative to the build direction or largely texture-free. X-ray diffraction confirmed the presence of Fe₃Al and C14-type (Fe, Al)₂Ta Laves phase in all samples. Hardness values fell within a narrow range (378–398 HV10), with only a slight reduction in the specimen exhibiting higher porosity.

For over two decades, vascular stents have been widely used to treat clogged vessels, serving as a scaffold to enlarge the narrowed lumen and recover the arterial flow area. High-purity oligocrystalline austenitic steel is usually applied for the production of stents. Despite the popularity and benefit of stenting, it still may cause serious clinical adverse issues, such as in-stent restenosis and stent fracture. Therefore, the study of the mechanical properties of stents and in particular the prediction of their life cycles are in the focus of materials research. In our contribution, within the finite element method, a two-scale model of crack initiation in the microstructure of stents is elaborated. The approach is developed on the basis of the physically based Tanaka–Mura model (TMM), considering the evolution of shear bands during the crack initiation phase. The model allows for the analysis of the microstructure with respect to the life cycles of real materials. The effects of different loading conditions, grain orientation, and thickness of the specimen on Wöhler curves were analysed. It was found that the microstructural features of oligocrystals are very sensitive to different loading conditions with respect to their fatigue behaviour and play a major role in fatigue crack initiation. Different grain-orientation distributions result in qualitative and quantitative differences in stress distribution and in the number of cycles for crack initiation. It was found that presence of a neutral zone in the cut-out of the microstructure under three-point-bending loading conditions changes the qualitative and quantitative patterns of stress distribution and affects the number of cycles for crack initiation. It was found that under both tensile and bending loading conditions, thicker specimens require more cycles for crack initiation. The Wöhler curves for crack initiation in oligocrystalline microstructures of stents could be compared with the ones in the experiment, taking into account that for high cyclic fatigue (HCF), typically, more than 70% of the cycles refer to crack initiation. The developed numerical tools could be used for the material design of stents.