In order to improve the properties of biodegradable polylactide (PLA), mixtures with polybutylene adipate-co-terephthalate (PBAT) were prepared. PLA is a bio-based and renewable biodegradable material, made from starch. PBAT is a biodegradable polyester for compostable film. In order to improve the composite properties, two types of additives were implemented via melt mixing, a chain extender (CE) and montmorillonite (MMT). CE was used as an interfacial modifier to enhance the adhesion between components. Montmorillonite is a widely studied clay added to polymer nanocomposites. Due to the lamellar structure, it improves the barrier properties of materials. PLA/PBAT films were oriented in the extrusion process and the amounts of filler introduced into the PLA/PBAT nanocomposites were 1.0, 3.0, and 5.0%. The improvement in the PLA barrier properties by the addition of PBAT and 5% of MMT was confirmed as the oxygen permeability decreased almost by a factor of 3. The addition of the biodegradable polymer, chain extender, montmorillonite, and the implemented orientation process resulted in a decrease in composite viscosity and an increase in the PLA crystallinity percentage (up to 25%), and the wettability tests confirmed the synergic behavior of the selected polymer blend.

There has been a growing interest in poly(ethylene terephthalate) PET degradation studies in the last few years due to its widespread use and large-scale plastic waste accumulation in the environment. One of the most promising enzymatic methods in the context of PET degradation is the use of PETase from Ideonella sakaiensis, which has been reported to be an efficient enzyme for hydrolysing ester bonds in PET. In our study, we expressed a codon-optimized PETase gene in the yeast Yarrowia lipolytica. The obtained strain was tested for its ability to degrade PET directly in culture, and a screening of different supplements that might raise the level of PET hydrolysis was performed. We also carried out long-term cultures with PET film, the surface of which was examined by scanning electron microscopy. The efficiency of PET degradation was tested based on the concentration of degradation products released, and the results showed that supplementation of the culture with olive oil resulted in 66 % higher release of terephthalic acid into the medium compared to the mutant culture without supplementation. The results indicate the possibility of ethylene glycol uptake by both strains, and, additionally, the PETase produced by the newly engineered strain hydrolyses MHET. The structure of the PET film after culture with the modified strain, meanwhile, had numerous surface defects, cracks, and deformations.

Recently, biocomposites have emerged as materials of great interest to the scientists and industry around the globe. Among various polymers, polylactic acid (PLA) is a popular matrix material with high potential for advanced applications. Various particulate materials and nanoparticles have been used as the filler in PLA based matrix. One of the extensively studied filler is cellulose. However, cellulose fibres, due to their hydrophilic nature, are difficult to blend with a hydrophobic polymer matrix. This leads to agglomeration and creates voids, reducing the mechanical strength of the resulting composite. Moreover, the role of the various forms of pure cellulose and its particle shape factors has not been analyzed in most of the current literature. Therefore, in this work, materials of various shapes and shape factors were selected as fillers for the production of polymer composites using Polylactic acid as a matrix to fill this knowledge gap. In particular, pure cellulose fibres (three types with different elongation coefficient) and two mineral nanocomponents: precipitated calcium carbonate and montmorillonite were used. The composites were prepared by a melt blending process using two different levels of fillers: 5% and 30%. Then, the analysis of their thermomechanical and physico-chemical properties was carried out. The obtained results were presented graphically and discussed in terms of their shape and degree of filling.

The modification of carbon fibers for improving adhesion between fibers and an epoxy resin in composite materials has become the focus of attention. In this work the carbon fiber coating process has been devised in a way preventing the stiffening and clumping of fibers. To improve interactions between coated fibers and a resin in composites, four types of silica coatings with different organic functional groups (3-aminopropyl–coating 1, 3-mercaptopropyl–coating 2, 2-(3,4-epoxycyclohexyl) ethyl–coating 3, methyl–coating 4) were obtained. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used to distinguish the changes of a carbon fibers surface after coating deposition. The thickness of the obtained coatings, including the diversity of thickness, was determined by transmission electron microscopy (TEM). The increase in surface free energy (SFE) of modified fibers, including the distinction between the polar and dispersive parts, was examined by wettability measurements using a tensometric test. The developed coating preparation process allowed to cover fibers separately with nanoscale silica layers, which changed their morphology. The introduction of organic functional groups resulted in surface free energy changes, especially an increase in specific polar surface energy components.

The paper analyses the influence of binary solvent systems on the electrospinning process and gelation effect. The characteristics of the electrospinning process are presented, considering the physicochemical properties of polymer solutions and the role of different solvents: chloroform, dimethylformamide (DMF), dimethyl sulfoxide (DMSO) and d -limonene. The shift in transition temperatures between the liquid and the gel phase were analyzed, and the obtained fiber structures were assessed using scanning electron microscopy (SEM). The optimization of solvent systems allows for the control of electrospinning process parameters, opening new possibilities for design advanced polymeric materials.

Effect of hemp shives (30–90 v/v %; size 0.5 and 0.8 mm) on the structure (SEM), mechanical properties (tensile properties, impact strength) and thermal properties (thermal conductivity, Vicat softening temperature) and water absorption of PBS composites was investigated. With the increase in filler content, the mechanical and insulating properties of the composites deteriorated due to weak interactions at the filler-polymer matrix interface. Water absorption also increased. Better properties were obtained with a smaller filler size.