A novel Al-Mg-Si aluminum alloy with the addition of the micro-alloying element Er and Zr that was promptly quenched after extrusion has been studied. The solid solution and aging treatment of the novel alloy are studied by observing the microstructure, mechanical properties, and strengthening mechanism. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques are employed to examine the changes in the microstructure resulting from various solid solution treatments and aging treatments. The best strengthening effect can be achieved when the solubility of the MgSi phase and precipitate β″ (Mg₂Si phase) is at their maximum. The addition of Er and Zr elements promotes the precipitation of the β″ phase and makes the b″ phase more finely dispersed. The aging strengthening of alloys is a comprehensive effect of the dislocation cutting mechanism and bypass mechanism, the joint effect of diffusion strengthening of Al₃(Er,Zr) particles and the addition of Er and Zr elements promoting the precipitation strengthening of β″ phases. In this paper, by adding Er and Zr elements and exploring the optimal heat treatment system, the yield strength of the alloy reaches 437 MPa and the tensile strength reaches 453 MPa after solid solution treatment at 565 °C/30 min and aging at 175 °C/10 h.

The influence of grain size on the corrosion behavior of pure aluminum and the defect density and diffusion coefficient of surface passive films were investigated using electron backscatter diffraction (EBSD) and electrochemical testing techniques, based on the point defect model (PDM). Samples with three different grain sizes (23 ± 11, 134 ± 52, and 462 ± 203 μm) were obtained by annealing at different temperatures and times. The polarization curves and electrochemical impedance spectroscopy results for the pure aluminum in the 3.5% NaCl solution showed that with decreasing grain size, the corrosion current (i_corr) decreased monotonously, giving rise to a noble corrosion potential and a large polarization resistance. The Motte–Schottky results showed that the passive films that formed on pure aluminum with fine grains of 23 ± 11 μm had a low density (3.82 × 10²⁰ cm⁻³) of point defects, such as oxygen vacancies and/or metal interstitials, and a small diffusion coefficient (1.94 × 10⁻¹⁷ cm²/s). The influence of grain size on corrosion resistance was discussed. This work demonstrated that grain refinement could be an effective approach to achieving high corrosion resistance of passive metals.

The nucleation and growth processes of pure Fe/pure Al intermetallic compounds (IMCs) during heat treatment at 380 °C and 520 °C were observed through in situ scanning electron microscopy (SEM). The size of the IMCs were statistically analyzed using image analysis software. The types and distribution of IMCs were characterized using transmission electron microscopy (TEM) and electron backscattering diffraction (EBSD). The results showed that: at 380 °C, the primary phase of the Fe/Al composite intermetallic compounds was Fe₄Al₁₃, formed on the Fe side and habituated with Fe. The IMC was completely transformed from the initial Fe₄Al₁₃ to the most stable Fe₂Al₅, and the Fe₂Al₅ was the habitus with Fe during the process of holding at 380 °C for 15 min to 60 min. At 380 °C, the initial growth rate of the IMC was controlled by reaction, and the growth rate of the thickness and horizontal dimensions was basically the same as 0.02–0.17 μm/min. When the IMC layer thickness reached 4.5 μm, the growth rate of the thickness changed from reaction control to diffusion control and decreased to 0.007 μm/min. After heat treatment at 520 °C (≤20 min), the growth of IMC was still controlled by the reaction, the horizontal growth rate was 0.53 μm/min, the thickness growth rate was 0.23 μm/min, and the main phase of the IMC was the Fe₂Al₅ phase at 520 °C/20 min.