This study aimed to compare the shear bond strength (SBS) and adhesive remaining index (ARI) using one conventional and two novel adhesive systems with clinical step reduction and direct and indirect bonding. A sample of 72 human premolars were divided into six groups of 12 samples. The first three groups (G1, G2, G3) were bonded with a direct technique, while the remaining groups (G4, G5, G6) were bonded by the indirect technique. Groups G1 and G4 used conventional acid-etching primer composite (XT); groups G2 and G5 used self-etching bonding (BO), and groups G3 and G6 had an acid-etching treatment followed by a self-adhesive composite (OC). All groups were exposed to thermocycling. Shear bond strength was analyzed with a universal test machine, and the ARI was examined with 4× magnification. The results showed statistically significant differences between the three adhesive systems. The highest strength values were observed in the XT group G1 (13.54 ± 4 MPa), while the lowest were shown in the BO G2 samples (5.05 ± 2 MPa). There was no significant difference between the direct or indirect bonding techniques on the three compared groups. The type of primer and bonding material significantly influenced the SBS. Values with self-etching bonding were below the minimum recommended for clinical use (5.9–7.8 MPa). There was no difference between indirect and direct bonding techniques. The lowest ARI scores (0–1) were observed in both self-etching and BO groups. Further clinical studies are needed to compare in vivo results.

The aim of the present study was to describe and determine changes in the superelastic properties of NiTi archwires after clinical use and sterilization. Ten archwires from five different manufacturers (GAC, 3M, ODS, GC, FOR) were cut into two segments and evaluated using a three-point bending test in accordance with ISO 14841:2006. The center of each segment was deflected to 3.1 mm and then unloaded to 0 N to obtain a load–deflection curve. Deflection at the end of the plateau and forces at 3, 2, 1 and 0.5 mm on the unloading curve were recorded. Plateau slopes were calculated at 2, 1 and 0.5 mm of deflection. Data obtained were statistically analyzed to determine differences (p < 0.001). Results showed that the degree of superelasticity and exerted forces differed significantly among brand groups. After three months of clinical use, FOR released a greater force for a longer activation period. GC, EURO and FOR archwires seemed to lose their mechanical properties. GC wires released more force than other brand wires after clinical use. Regarding superelasticity after sterilization, GAC, 3M and FOR wires recovered their properties, while EURO archwires lost more.

Background: The aim of this study is to determine the prevalence of nocturnal enuresis (NE) in children with obstructive sleep apnea (OSA), the effect of adenotonsillectomy (AT) and the width of the arches, and to compare them with control children without respiratory problems. Methods: Children from 2 to 12 years old were divided into three groups: children with OSA and NE (n = 51), children with OSA without NE (n = 79), and the control group (n = 168). NE was defined as at least one bedwetting incident per month. Arch widths were measured at the baseline and one year after. OSA was diagnosed by means of polysomnography, and the apnea-hypopnea index (AHI) was obtained. Parents completed the Pediatric Sleep Questionnaire (PSQ) to classify their children into those with and without NE. Results: NE was present in 39.2% of children with OSA compared to 28% in the control group (p = 0.04). After AT, 49% of the children with OSA and NE significantly improved. Both OSA groups had narrower arch widths than the control group (p = 0.012), with the NE group having the narrowest widths. NE is more prevalent in children with OSA and should be considered one of the first signs of breathing disorders. Adenotonsillectomy reduces NE in about half of the affected children. Both arch widths are narrower in children with OSA, particularly in those with NE.

Introduction: Several advantages have been established regarding the efficiency of self-ligating brackets (SL). In spite of some controversy surrounding this question in the literature, clinical results confirm that “arch development” requires fewer extractions. Objective: The objective of this study was to compare changes in the transverse and sagittal planes in patients treated with conventional ligating brackets (CL)as well as in patients treated with SL brackets and oversized arches. Methods: A sample was selected from a pool of 300 consecutive cases treated by a single clinician: 51 patients with SL brackets and oversized wires, and 55 with CL brackets. These two groups were compared with a control group of 20 patients. All plaster models were scanned and dental landmarks were measured to identify changes from commencement (T0) to conclusion (T1) of treatment. Lateral cephalograms were analyzed for changes in the lower incisor (IMPA) and the first lower molar distal angulation (MAng). Intraoperator reliability was tested with linear regression analysis. To assure all groups were comparable at T0, an ANOVA test with a 95%confidence interval (CI) was performed for all values. To assess changes from T0 to T1 in all groups, a Student’s t-test with 95% CI was used. Finally, results from the three groups were compared using an ANOVA-test (95% CI) and a post-hoc test. Results: Increases in all the transverse variables were recorded in the two groups treated (SL and CL), except for the lower intercanine distance in the SL group. IMPA difference from T0 to T1 was higher in the CL group, and molar distal angulation (MAng) took place in the SL group. Conclusions: Self-ligating brackets with oversized arches and conventional ligating brackets showed increases in all variables in the transverse plane, except for the SL group at the mandibular intercanine distance. In comparison with the CL group, fewer different IMPA values were observed in the SL group, in which distal molar angulation occurred.

Lack of standardization of the retention phase has led to many studies of stability of movements and characteristic of retainers, disregarding the enamel repercussions of fixed retention on this phase. This study aimed to analyze different methods of enamel polishing after detachment of orthodontic retainers. Forty-five healthy premolars were divided into three groups according to the polishing bur after debonding, and four specimens without intervention were used as control. A 0.038 × 0.015 inches gold chain was bonded between the premolars and then removed. The adhesive remnant was removed with three types of burs according to the study groups (Group 1: white stone at high speed; Group 2: high-speed handpiece with a 30-blade tungsten carbide bur; Group 3: low-speed handpiece and a 30-blade tungsten bur). After debonding and polishing, all samples were analyzed with a confocal microscopy on surface roughness parameters: Sa: Arithmetic mean of the height of the surface. Rq: Square mean of the height of the surface and Sz: Maximum surface height. Mechanical tests were carried out to determine the bonding stress of the retention adhered to the teeth using an electromechanical testing machine. The adhesion stress was 8.23 MPa (±0.87). The quality of the refinement of the enamel after debonding is essential in order to preserve its integrity. The use of the 30-blade tungsten carbide bur provides a smooth enamel surface after polishing.

The aim of the present study was to describe and determine changes in the superelastic properties of NiTi archwires after clinical use and sterilization. Ten archwires from five different manufacturers (GAC, 3M, ODS, GC, FOR) were cut in two segments and evaluated using a three-point bending test in accordance with ISO 14841:2006. The centre of each segment was deflected to 3.1mm and then unloaded to 0 N to obtain a load-deflection curve. Deflection at the end of the plateau and forces at 3, 2, 1 and 0.5mm on the unloading curve were recorded. Plateau slopes were calculated at 2, 1 and 0.5mm of deflection. Data obtained were statistically analysed to determine differences (p<0.001). Results showed that the degree of superelasticity and exerted forces differed significantly among brand groups. After three months of clinical use, FOR released a greater force for a longer activation period. GC, EURO and FOR archwires seemed to lose their mechanical properties. GC wires released more force than other brand wires after clinical use. Regarding superelasticity after sterilization, GAC, 3M and FOR wires recovered their properties, while EURO archwires lost more.