This study aimed to compare the shear bond strength (SBS) and adhesive remaining index (ARI) using one conventional and two novel adhesive systems with clinical step reduction and direct and indirect bonding. A sample of 72 human premolars were divided into six groups of 12 samples. The first three groups (G1, G2, G3) were bonded with a direct technique, while the remaining groups (G4, G5, G6) were bonded by the indirect technique. Groups G1 and G4 used conventional acid-etching primer composite (XT); groups G2 and G5 used self-etching bonding (BO), and groups G3 and G6 had an acid-etching treatment followed by a self-adhesive composite (OC). All groups were exposed to thermocycling. Shear bond strength was analyzed with a universal test machine, and the ARI was examined with 4× magnification. The results showed statistically significant differences between the three adhesive systems. The highest strength values were observed in the XT group G1 (13.54 ± 4 MPa), while the lowest were shown in the BO G2 samples (5.05 ± 2 MPa). There was no significant difference between the direct or indirect bonding techniques on the three compared groups. The type of primer and bonding material significantly influenced the SBS. Values with self-etching bonding were below the minimum recommended for clinical use (5.9–7.8 MPa). There was no difference between indirect and direct bonding techniques. The lowest ARI scores (0–1) were observed in both self-etching and BO groups. Further clinical studies are needed to compare in vivo results.

A potential new bactericide treatment for NiTi orthodontic archwires based in the electrodeposition of silver nanoparticles on the surface was studied. Twenty-five archwires were treated by electrodeposition, obtaining nanoparticles of silver embedded on the archwire surface. These were evaluated in order to investigate the possible changes on the superelastic characteristics (critical temperatures and stresses), the nickel ion release, and the bacteria culture behavior. The chemical composition was analyzed by Energy Dispersive X-Ray Spectroscopy-microanalysis; the singular temperatures of the martensitic transformation were obtained by a flow calorimeter. Induced martensitic transformation stresses were obtained by mechanical testing apparatus. Nickel ion release was analyzed by inductively coupled plasma-mass spectrometry (ICP-MS) equipment using artificial saliva solution at 37 °C. Bacterial tests were studied with the most used oral bacterial strains: Streptococcus sanguinis and Lactobacillus salivarius. NiTi samples were immersed in bacterial suspensions for 2 h at 37 °C. Adhered bacteria were separated and seeded on agar plates: Tood-Hewitt (TH) and Man-Rogosa-Sharpe (MRS) for S. sanguinis and for L.salivarius, respectively. These were then incubated at 37 °C for 1 day and the colonies were analyzed. The results showed that the transformation temperatures and the critical stresses have not statistically significant differences. Likewise, nickel ion release at different immersion times in saliva at 37 °C does not present changes between the original and treated with silver nanoparticles archwires. Bacteria culture results showed that the reduction of the bacteria due to the presence to the nanoparticles of silver is higher than 90%. Consequently, the new treatment with nanoparticles of silver could be a good candidate as bactericidic orthodontic archwire.

The aim of the present study was to describe and determine changes in the superelastic properties of NiTi archwires after clinical use and sterilization. Ten archwires from five different manufacturers (GAC, 3M, ODS, GC, FOR) were cut into two segments and evaluated using a three-point bending test in accordance with ISO 14841:2006. The center of each segment was deflected to 3.1 mm and then unloaded to 0 N to obtain a load–deflection curve. Deflection at the end of the plateau and forces at 3, 2, 1 and 0.5 mm on the unloading curve were recorded. Plateau slopes were calculated at 2, 1 and 0.5 mm of deflection. Data obtained were statistically analyzed to determine differences (p < 0.001). Results showed that the degree of superelasticity and exerted forces differed significantly among brand groups. After three months of clinical use, FOR released a greater force for a longer activation period. GC, EURO and FOR archwires seemed to lose their mechanical properties. GC wires released more force than other brand wires after clinical use. Regarding superelasticity after sterilization, GAC, 3M and FOR wires recovered their properties, while EURO archwires lost more.

Background: The aim of this study is to determine the prevalence of nocturnal enuresis (NE) in children with obstructive sleep apnea (OSA), the effect of adenotonsillectomy (AT) and the width of the arches, and to compare them with control children without respiratory problems. Methods: Children from 2 to 12 years old were divided into three groups: children with OSA and NE (n = 51), children with OSA without NE (n = 79), and the control group (n = 168). NE was defined as at least one bedwetting incident per month. Arch widths were measured at the baseline and one year after. OSA was diagnosed by means of polysomnography, and the apnea-hypopnea index (AHI) was obtained. Parents completed the Pediatric Sleep Questionnaire (PSQ) to classify their children into those with and without NE. Results: NE was present in 39.2% of children with OSA compared to 28% in the control group (p = 0.04). After AT, 49% of the children with OSA and NE significantly improved. Both OSA groups had narrower arch widths than the control group (p = 0.012), with the NE group having the narrowest widths. NE is more prevalent in children with OSA and should be considered one of the first signs of breathing disorders. Adenotonsillectomy reduces NE in about half of the affected children. Both arch widths are narrower in children with OSA, particularly in those with NE.

Lack of standardization of the retention phase has led to many studies of stability of movements and characteristic of retainers, disregarding the enamel repercussions of fixed retention on this phase. This study aimed to analyze different methods of enamel polishing after detachment of orthodontic retainers. Forty-five healthy premolars were divided into three groups according to the polishing bur after debonding, and four specimens without intervention were used as control. A 0.038 × 0.015 inches gold chain was bonded between the premolars and then removed. The adhesive remnant was removed with three types of burs according to the study groups (Group 1: white stone at high speed; Group 2: high-speed handpiece with a 30-blade tungsten carbide bur; Group 3: low-speed handpiece and a 30-blade tungsten bur). After debonding and polishing, all samples were analyzed with a confocal microscopy on surface roughness parameters: Sa: Arithmetic mean of the height of the surface. Rq: Square mean of the height of the surface and Sz: Maximum surface height. Mechanical tests were carried out to determine the bonding stress of the retention adhered to the teeth using an electromechanical testing machine. The adhesion stress was 8.23 MPa (±0.87). The quality of the refinement of the enamel after debonding is essential in order to preserve its integrity. The use of the 30-blade tungsten carbide bur provides a smooth enamel surface after polishing.

The aim of the present study was to describe and determine changes in the superelastic properties of NiTi archwires after clinical use and sterilization. Ten archwires from five different manufacturers (GAC, 3M, ODS, GC, FOR) were cut in two segments and evaluated using a three-point bending test in accordance with ISO 14841:2006. The centre of each segment was deflected to 3.1mm and then unloaded to 0 N to obtain a load-deflection curve. Deflection at the end of the plateau and forces at 3, 2, 1 and 0.5mm on the unloading curve were recorded. Plateau slopes were calculated at 2, 1 and 0.5mm of deflection. Data obtained were statistically analysed to determine differences (p<0.001). Results showed that the degree of superelasticity and exerted forces differed significantly among brand groups. After three months of clinical use, FOR released a greater force for a longer activation period. GC, EURO and FOR archwires seemed to lose their mechanical properties. GC wires released more force than other brand wires after clinical use. Regarding superelasticity after sterilization, GAC, 3M and FOR wires recovered their properties, while EURO archwires lost more.