Understanding the interaction behaviors between sessile droplets under imposed high voltages is very important in many practical situations, e.g., microfluidic devices and the degradation/aging problems of outdoor high-power applications. In the present work, the droplet coalescence, the discharge activity and the surface thermal distribution response between sessile multidroplets and chloride salt droplets under high tangential electric fields have been investigated with infrared thermography, high-speed photography and pulse current measurement. Obvious polarity effects on the discharge path direction and the temperature change in the droplets in the initial stage after discharge initiation were observed due to the anodic dissolution of metal ions from the electrode. In the case of sessile aligned multidroplets, the discharge path direction could affect the location of initial droplet coalescence. The smaller unmerged droplet would be drained into the merged large droplet as a result from the pressure difference inside the droplets rather than the asymmetric temperature change due to discharge. The discharge inception voltages and the temperature variations for two salt droplets closely correlated with the ionization degree of the salt, as well as the interfacial electrochemical reactions near the electrodes. Mechanisms of these observed phenomena were discussed.

A deterministic adhesive model for the contact between an elastic layered medium with surface roughness and a smooth elastic microsphere was developed on the basis of the Lennard–Jones surface force law. Through numerical simulations, the adhesive contact behavior of the layered medium with the measured three-dimensional (3D) surface topography was comparatively analyzed with that of the homogeneous medium. Furthermore, the contact characteristics of the layered medium with pre-assigned roughness parameters were investigated with the aid of a computer-generated technique for simulating surface roughness. Results showed that the pull-off force for the contact problem involving rough surfaces was influenced by the contact location, and the average value for the contact between an alumina (SiO2) microsphere and a diamond-like carbon/silicon (DLC/Si)-layered medium was smaller than that for the contact between a SiO2 microsphere and a Si homogeneous half-space. In addition, the effect of the diamond-like carbon (DLC) layer on reducing adhesion was smaller than that of the surface roughness. Finally, the average pull-off force for a DLC/Si-layered medium with computer-generated surface roughness rapidly decreased; however, it eventually became almost unchangeable with the increase in the root-mean-square (RMS) deviation.

Purpose: This paper aims to clarify the effects of metallic nanoparticles (NPs) additives and room temperature ionic liquids (ILs) on the tribological performance of electric contacts. Design/methodology/approach: Tribological properties of copper (Cu) and silver (Ag) NPs as lubricant additives in different lubricants of ILs or polyalphaolefin (PAO) oils under applied electric currents were investigated. After tribological tests, morphologies of worn surfaces were observed; meanwhile, lubrication and anti-wear properties were analyzed. Findings: The mixture solution of the IL and Cu NPs showed desirable lubrication and anti-wear properties due to the reduction of electrocorrosion and the enhancement of rolling effects of particles in the contact region. The anti-wear performance of Cu NPs is better than that of Ag NPs due to the difference in the particle size. The PAO oil with the Cu NPs additives showed poor lubrication properties due to the low solubility of the particles in the oil. When the direction of applied current was changed, the friction of the lubricant with better conductivity was more stable in the variation trend. Originality/value: This paper begins with a study of tribological properties of Cu and Ag NPs as lubricant additives in different lubricants of IL or PAO oils under applied electric currents. The authors then propose several methods and possible solutions which could be implemented to improve the tribological performance of electric contacts.

Purpose: This paper aims to introduce a series of experimental results which are the extension of our previous novel observations (Xie et al., Soft Matter, 2011), which could be helpful for revealing the lubrication failure mechanism in bearings when they are exposed to an electrical environment. Design/methodology/approach: An experimental apparatus where a ball was in contact with a glass disk coated with a semi-reflective chromium layer. A small volume of oil droplet was put into the microgap of the ball-disk contact. Then, a potential was applied onto the oil micropool formed by the droplet surrounding the contact region. Findings: It has been found that destabilization of the low-conducting oil micropool around the contact region could be induced after applying a potential. Thin oil films could be drained out of the oil pool and spread on the tribopair surfaces, resulting in the depletion of the oil pool. When the applied potential was increased, the occurrence of spreading would be easier and its development would be more obvious. In contrast, the electrospreading behavior would be suppressed when the oil viscosity, contact load and oil pool size were increased. Thermocapillary force due to thermal effect as a result of the current flow near the oil pool border has been proposed as the main driving force for the spreading behavior. The influences of the operating parameters have been ascribed to the change of the electric current near the oil pool border as well as the corresponding variations in the temperature rise and the surface tension of the oil pool. Originality/value: This is the first study to directly observe that the lubricant oil micropool around the contact region could deplete after applying a potential, potentially resulting in oil starvation in the contact region.