Glass fiber-reinforced polymer (GFRP) reinforcements are superior to traditional steel bars in concrete structures, particularly in vertical elements like columns, and offer significant advantages over conventional steel bars when subjected to axial and eccentric loadings. However, there is limited experimental and numerical research on the behavior of GFRP-reinforced concrete (RC) columns under eccentric loading having different spacing of stirrups. In this study, six specimens were cast under three different values of eccentricities (25 mm, 50 mm, and 75 mm) with two groups of stirrups spacing (50 mm and 100 mm). The experimental results showed that by increasing the eccentricity value, there was a reduction in the load-carrying capacity of the specimens. The finite element ABAQUS software was used for the numerical investigation of this study. The results from the finite element analysis (FEA) were close to the experimental results and within the acceptable range. The maximum difference between the experimental and FEA results was 3.61% for the axial load and 12.06% for the deformation.

Reinforced concrete corbels were examined in this study for the cracking behavior and strength evaluation, focusing on defects typically found in these structures. A total of 11 corbel specimens were tested, including healthy specimens (HS), specimens with lower concrete strength (LC), specimens with less reinforcement ratio (LR), and specimens with more concrete cover than specifications (MC). The HS specimens were designed using the ACI conventional method. The specimens were tested under static loading conditions, and the actual strengths along with the crack patterns were determined. In the experimental tests, the shear capacity of the HS specimens was 28.18% and 57.95% higher than the LR and LC specimens, respectively. Similarly, the moment capacity of the HS specimens was 25% and 57.52% greater than the LR and LC specimens, respectively. However, in the case of the built-up sections, the shear capacity of the HS specimens was 9.91% and 37.51% higher than the LR and LC specimens, respectively. Likewise, the moment capacity of the HS specimens was 39.91% and 14.30% higher than the LR and LC specimens, respectively. Moreover, a detailed nonlinear finite element model (FEM) was developed using ABAQUS, and a more user-friendly strut and tie model (STM) was investigated toward its suitability to assess the strengths of the corbels with construction defects. The results from FEM and STM were compared. It was found that the FEM results were in close agreement with their experimental counterparts.

Contaminated wastewater discharged from tanneries in Pakistan creates a lot of pollution problems. This study presents the treatment of wastewater samples collected from inlet and outlet sections of Kasur Tannery Waste Management Agency (KTWMA) in Kasur, Pakistan. The procedure utilizes hydrogen peroxide (H2O2) in the presence of ultraviolet (UV) radiation for the successful degradation of pollutants present in tannery water. The treatment of polluted water samples with UV/H2O2 for the duration of either 45 minutes or 90 minutes has greatly affected the water quality parameters such as biochemical oxygen demand (BOD), chemical oxygen demand (COD), chlorides, chromium, pH, total dissolved solids (TDS) and total suspended solids (TSS). It was concluded that the contaminants were degraded and changed to a great extent as compared to their original concentrations. This process can be considered to be a clean process as it is an environmentally friendly process and does not produce pollutants and solid wastes like other conventional processes.