This study analyzes the behavior under the static delamination and mode-I fracture stress of adhesive joints made on the same composite material with an epoxy matrix and unidirectional carbon fiber reinforcement and two types of adhesives, one epoxy and the other acrylic. Standard DCB tests (for mode-I fracture) were used to quantify the influence on the interlaminar fracture toughness of the type of adhesive used. Both materials were subjected to two different degradation processes, one hygrothermal and the other in a salt-fog chamber. After aging, the mode-I fracture has been evaluated for both materials. From the experimental results obtained, it can be deduced for the epoxy adhesive that exposure to the hygrothermal environment used moderately modifies its behavior against delamination, while its exposure to the saline environment produces a significant loss of its resistance to delamination. For the acrylic adhesive, the hygrothermal exposure causes an improvement in its delamination behavior for all the exposure periods considered, while the saline environment slightly modifies its behavior. There is, therefore, a clear influence of the type of aging on the fracture behavior of both adhesives.

It is well known that the cold-forming process used to manufacture tubes causes an increase in both the yielding stress and the ultimate strength of the corner material in rectangular steel hollow sections. This may have a significant effect on the resistance of any structure built with those profiles. However, the mentioned material hardening can be difficult to take into account in the calculations for member design or to evaluate the connection resistance through the design formulation or when using numerical simulation models. As an attempt to face the above-mentioned problem, the present paper presents a comparison among simplified approaches that consider homogeneous material properties for the whole section. It has been carried out by comparing the results obtained from the finite element modelling of stub column tests in which the material properties based on the flat faces were considered for the whole profile.

Eurocode 3 establishes the component method to analytically characterize the structural joints between beam and columns. When one of the members involved in the joint is a hollow section (i.e., a tube) there is a lack of information for the specific components present in the joint. There are two different ways to bridge the gap: experimental testing on the actual beam column joints involving tubular sections; or numerical modelization, typically by means of finite element analysis. For this second option, it is necessary to know the actual mechanical properties of the material. As long as the joint implies a welding process, there is a concern related to how the mechanical properties in the heat-affected zone (HAZ) influence the behavior of the joint. In this work, some coupons were extracted from the HAZ of the beam-column joint. The coupons were tested and the results were implemented in the numerical model of the joint, in an attempt to bring it closer to the experimental results of the tested joints.

This study analyzes the delamination behavior of adhesive joints after exposure to a saline environment for zero, one, and twelve weeks. Delamination was assessed under static and fatigue loading conditions in fracture Modes I and II, with a detailed analysis of fracture surfaces using Scanning Electron Microscopy (SEM) and Backscattered Electron (BSE) detection. The 3D images reveal significant morphological differences in fracture surfaces, showing variations in fatigue lines and the presence of impurities depending on the fracture mode. A probabilistic fatigue life analysis was performed using a Weibull regression model, showing notable changes, especially in Mode I at a high number of cycles. A chemical analysis using EDX and FTIR-ATR complemented the mechanical study, revealing an increase in sodium and chlorine concentrations with prolonged saline exposure. Oxidative degradation was also observed, with carbonyl groups increasing significantly over time, particularly in areas most exposed to the saline mist.

This study investigates the fatigue delamination behavior of adhesive joints in epoxy carbon composite materials under Mode II fracture loading. The joints were characterized using the End-Notched Flexure (ENF) test, comprising adhesive joints formed by bonding two unidirectional carbon fiber epoxy matrix laminates with epoxy adhesive. These joints were subjected to different exposure periods (1, 2, 4, and 12 weeks) in a saline environment. Prior to dynamic fatigue testing, critical Mode II energy release rate values were determined through quasi-static tests, serving as a reference for subsequent fatigue characterization. This study aimed to comprehend how exposure duration to a saline environment affected the initial stage of fatigue delamination growth and employed a probabilistic model based on the Weibull distribution to analyze the experimental data. The results, gathered over a two-year experimental program, revealed varying behaviors in adhesive joint resistance to delamination based on exposure duration. A noteworthy reduction in fatigue strength capacity was observed, with fracture energies for infinite fatigue life reaching approximately 20% of their static loading capacity. This study sheds light on the deterioration of adhesive joints when exposed to a saline environment.

The determination of plywood bonding quality by shear testing is one of the most commonly used and informative tests, alongside bending strength, to characterise this compound material. Two types of birch plywood were studied: indoor use (class 1), thickness 18 mm, urea-formaldehyde glue; and exposed outdoor use (class 3), thickness 15 mm, phenolic formaldehyde glue. The corresponding pre-treatments indicated in standards UNE-EN 314-1 and -2 were applied to each type. To test the suitability of the method, the technique of digital image correlation (DIC) was used to obtain information about the complex modes of fracture present in compound materials such as plywood. Assessing the results based on the statistical extreme value theory provided more reliable and robust information about the failure strength values for low failure probabilities. The results confirm that DIC can be used to determine the true distribution of the deformations during the fracture process and, therefore, it provides greater knowledge of the details of the failure process. Statistical evaluation of the experimental data obtained with DIC indicates that test results exceeding the time limit of 30 ± 10 s should be evaluated, contrary to the operating procedure in standard UNE-EN 314-1, which states that they are invalid.