Aluminum-fly ash particulate-reinforced composites (AA6063-FA) have been used in various engineering fields, such as automotive and aerospace industries, due to their low density and good mechanical properties. There are many fabrication techniques available to manufacture these composites according to matrix and reinforcement materials. The compocasting technique for the fabrication of the AA6063 matrix composite reinforced with fly ash particles is the focus of this research. Fly ash content was in the range of 0–12 wt % in increasing increments of 2%. Fly ash particles were added to the molten AA6063 alloy until they were completely blended and cooled down just below the liquidus to keep the slurry in the semi-solid state. After this, the molten AA6063-FA composites were cast into prepared cast iron molds. Bulk density and apparent porosity measurements, Charpy impact testing, Vickers microhardness measurements, Field Emission Scanning Electron Microscope (FESEM), Variable Pressure Scanning Electron Microscope and Energy Dispersive X-ray spectroscope (EDS) elemental mapping were used to evaluate these materials. The results showed that an increase in the fly ash content in the melted leads results in an increase in the microhardness and porosity in the composites. In contrast, the bulk density and Charpy impact energy of the composites decreased with an increase in the fly ash content.

Fly ash is the main waste as a result of combustion in coal fired power plants. It represents about 40% of the wastes of coal combustion products (fly ash, boiler ash, flue gas desulphurization gypsum and bottom ash). Currently, coal waste is not fully utilized and waste disposal remains a serious concern despite tremendous global efforts in reducing fossil fuel dependency and shifting to sustainable energy sources. Owing to that, employment of fly ash as reinforcement particles in metallic matrix composites are gaining momentum as part of recycling effort and also as a means to improve the specifications of the materials that are added to it to form composite materials. Many studies have been done on fly ash to study composite materials wear characteristics including the effects of fly ash content, applied load, and sliding velocity. Here, particular attention is given to studies carried out on the influence FA content on physical, mechanical, and the thermal behavior of Aluminium-FA composites. Considerable changes in these properties are seen by fly ash refinement with limited size and weight fraction. The advantage of fly ash addition results in low density of composites materials, improvement of strength, and hardness. It further reduces the thermal expansion coefficient and improve wear resistance.

The development of new methods for addition fine ceramic powders to Al aluminium alloy melts, which would lead to more uniform distribution and effective incorporation of the reinforcement particles into the aluminium matrix alloy. Recently the materials engineering research has moved to composite materials from monolithic, adapting to the global need for lightweight, low cost, quality, and high performance advanced materials. Among the different methods, stir casting is one of the simplest ways of making aluminium matrix composites. However, it suffers from poor distribution and combination of the reinforcement ceramic particles in the metal matrix. These problems become significantly effect to reduce reinforcement size, more agglomeration and tendency with less wettability for the ceramic particles in the melt process. Many researchers have carried out different studies on the wettability between the metal matrix and dispersion phase, which includes added wettability agents, fluxes, preheating the reinforcement particles, coating the reinforcement particles, and use composting techniques. The enhancement of wettability of ceramic particles by the molten matrix alloy and the reinforcement particles distribution improvement in the solidified matrix is the main objective for many studies that will be discussed in this paper.

Lightweight, high-strength metal matrix composites have attracted considerable interest because of their attractive physical, mechanical and tribological properties. Moreover, they may offer distinct advantages due to good strength and wear resistance. In this research, AA6063 was reinforced with FA particles using compocasting methods. The effects of fly ash content, load, sliding speed and performance tribology of AA6063 –FA composite were evaluated. Dry sliding wear tests were carried out according to experimental design using the pin-on-disc method with three different loads (24.5, 49 and 73.5 N) and three speeds (150, 200 and 250 rpm) at room temperature. Response surface methodology (RSM) was used to analyze the influence of the process parameters on the tribological behavior of the composites. The surface plot showed that the wear rate increased with increasing load, time and sliding velocity. In contrast, the friction coefficient decreased with increasing these parameters. Optimal models for wear rate and friction coefficient showed appropriate results that can be estimated, hence reducing wear testing time and cost.

The AA6063 alloy reinforced with 0, 2, 4 and 6 wt. % of fly ash (FA) particulate composites were produced by the compocasting technique. In this study, the effect of FA content and sliding speed on the wear behaviour of AA6063-FA composite was investigated. The wear was carried out by using pin on disc apparatus against rough steel counterface. These wear tests were conducted at applied load of 24.5, 49 and 73.5 N respectively with the constant sliding speed (150 rpm) and sliding time (10 minutes). In the results, it has been observed that upon addition of FA particles, the wear resistance of AA6063 -FA composites was enhanced. The wear rate reduced with the increase in the content of FA particles. While the wear rate increased with increase in the applied load.