Organic-inorganic halide perovskite solar cells (PSCs) have attracted much attention in recent years due to their simple manufacturing process, low cost, and high efficiency. So far, all efficient organic-inorganic halide PSCs are mainly made of polycrystalline perovskite films. There are transmission barriers and high-density defects on the surface, interface, and grain boundary of the films. Among them, the deep-level traps caused by specific charged defects are the main non-radiative recombination centers, which is the most important factor in limiting the photoelectric conversion efficiency of PSCs devices to the Shockley-Queisser (S-Q) theoretical efficiency limit. Therefore, it is imperative to select appropriate passivation materials and passivation strategies to effectively eliminate defects in perovskite films to improve their photovoltaic performance and stability. There are various passivation strategies for different components of PSCs, including interface engineering, additive engineering, antisolvent engineering, dopant engineering, etc. In this review, we summarize a large number of defect passivation work to illustrate the latest progress of different types of passivators in regulating the morphology, grain boundary, grain size, charge recombination, and defect density of states of perovskite films. In addition, we discuss the inherent defects of key materials in carrier transporting layers and the corresponding passivation strategies to further optimize PSCs components. Finally, some perspectives on the opportunities and challenges of PSCs in future development are highlighted.

Some photosensitive resins have poor mechanical properties after 3D printing. To overcome these limitations, a polyurethane acrylate oligomer (PUA) microsphere was prepared using the Pickering emulsion template method and ultraviolet (UV) curing technology in this paper. The prepared PUA microspheres were added to PUA-1,6-hexanediol diacrylate (HDDA) photosensitive resin system for digital light processing (DLP) 3D printing technology. The preparation process of PUA microspheres was discussed based on micromorphology, and it was found that the oil-water ratio of the Pickering emulsion and the emulsification speed had a certain effect on the microsphere size. As the oil-water ratio and the emulsification speed increased, the microsphere particle size decreased to a certain extent. Adding a suitable proportion of PUA microspheres to the photosensitive resin can improve the mechanical properties and thermal stability. When the modified photosensitive resin microsphere content was 0.5%, the tensile strength, elongation at break, bending strength, and initial thermal decomposition temperature were increased by 79.14%, 47.26%, 26.69%, and 10.65%, respectively, compared with the unmodified photosensitive resin. This study provides a new way to improve the mechanical properties of photosensitive resin 3D printing. The resin materials studied in this work have potential application value in the fields of ceramic 3D printing and dental temporary replacement materials.