Components produced by additive manufacturing (AM) via direct metal laser sintering (DMLS) have typical as-fabricated surface defects. As a result, surface properties of AM products should be modified to increase their strength, anti-wear behaviour, and at the same time to ensure their high corrosion resistance. Surface modification via shot peening is considered suitable for additive manufacturing of medical devices made of 17-4PH stainless steel. The objective of this study was to determine the effect of shot peening pressures (0.3 MPa and 0.6 MPa) and three types of blasting media (CrNi steel shot, nutshell granules and ceramic beads) on the tribological characteristics and corrosion resistance of specimens of DMLS 17-4PH stainless steel. Results demonstrated that shot peening caused steel microstructure refinement and—except for the nutshell shot-peened specimens—induced both martensite (α) formation and retained austenite (γ) reduction. 17-4PH specimens peened with steel and ceramic shots showed the highest increase in surface hardening by approx. ~ 119% (from 247 to 542 HV), which significantly improved their wear resistance. The highest mechanical properties (hardness and wear resistance) and corrosion resistance were obtained for the surfaces modified using the following media: ceramic beads > CrNi steel shot > nutshell granules. Adhesive and fatigue wear were two predominant mechanisms of tribological deterioration. Results demonstrated that the application of shot peening using ceramic beads led to grain size refinement from 22.0 to 14.6 nm and surface roughness reduction, which in turn resulted in higher corrosion resistance of the material. DMLS 17-4PH specimens modified by shot peening using ceramic beads and a pressure of 0.6 MPa exhibited the optimum surface morphology, hardness and microstructure, and thus improved wear and corrosion performance.

Shot peening is a dynamically developing surface treatment used to improve the surface properties modified by tool, impact, microblasting, or shot action. This paper reviews the basic information regarding shot peening methods. The peening processes and effects of the shot peening and cavitation peening treatments on the surface layer properties of metallic components are analysed. Moreover, the effects of peening on the operational performance of metallic materials are summarized. Shot peening is generally applied to reduce the surface roughness, increase the hardness, and densify the surface layer microstructure, which leads to work hardening effects. In addition, the residual compressive stresses introduced into the material have a beneficial effect on the performance of the surface layer. Therefore, peening can be beneficial for metallic structures prone to fatigue, corrosion, and wear. Recently, cavitation peening has been increasingly developed. This review paper suggests that most research on cavitation peening omits the treatment of additively manufactured metallic materials. Furthermore, no published studies combine shot peening and cavitation peening in one hybrid process, which could synthesize the benefits of both peening processes. Moreover, there is a need to investigate the effects of peening, especially cavitation peening and hybrid peening, on the anti-wear and corrosion performance of additively manufactured metallic materials. Therefore, the literature gap leading to the scope of future work is also included.

The paper investigates the cavitation erosion (CE) and sliding wear (SW) resistance of cold-sprayed Al/Al₂O₃ and Cu/Al₂O₃ composites and studies them in relation to a set of metallic materials such as aluminium alloy (AlCu4Mg1), pure copper (Cu110), brass (CuZn40Pb2) and stainless steel (AISI 304). The coatings were deposited on stainless steel by low-pressure cold spray (LPCS) using Al (40 wt.%) and Cu (50 wt.%) blended with Al₂O₃ (60 and 50 wt.%, respectively) feedstocks. CE resistance was estimated by the stationary sample method according to the ASTM G32 standard. The SW test was conducted using a ball-on-disc tester with compliance to the ASTM G99 standard. Results obtained for the LPCS coatings show that the Cu/Al₂O₃ coating exhibits a denser structure but lower adhesion and microhardness than Al/Al₂O₃. The Al/Al₂O₃ and Cu/Al₂O₃ resistance to cavitation is lower than for bulk alloys; however, composites present higher sliding wear resistance to that of AlCu4Mg1, CuZn40Pb2 and stainless steel. The CE wear mechanisms of LPCS composites start at the structural discontinuities and non-uniformities. The cavitation erosion degradation mechanism of Al/Al₂O₃ relies on chunk material detachment while that of Cu/Al₂O₃ initiates by alumina removal and continues as layer-like Cu-metallic material removal. CE damage of metal alloys relies on the fatigue-induced removal of deformed material. The SW mechanism of bulk alloys has a dominant adhesive mode. The addition of Al₂O₃ successfully reduces the material loss of LPCS composites but increases the friction coefficient. Coatings’ wear mechanism has an adhesive-abrasive mode. In both CE and SW environment, the behaviour of the cold-sprayed Cu/Al₂O₃ composite is much more promising than that of the Al/Al₂O₃.

The resistance to cavitation erosion and sliding wear of stainless steel grade AISI 304 can be improved by using physical vapor deposited (PVD) coatings. The aim of this study was to investigate the cavitation erosion and sliding wear mechanisms of magnetron-sputtered AlTiN and TiAlN films deposited with different contents of chemical elements onto a stainless steel SS304 substrate. The surface morphology and structure of samples were examined by optical profilometry, light optical microscopy (LOM) and scanning electron microscopy (SEM-EDS). Mechanical properties (hardness, elastic modulus) were tested using a nanoindentation tester. Adhesion of the deposited coatings was determined by the scratch test and Rockwell adhesion tests. Cavitation erosion tests were performed according to ASTM G32 (vibratory apparatus) in compliance with the stationary specimen procedure. Sliding wear tests were conducted with the use of a nano-tribo tester, i.e., ball-on-disc apparatus. Results demonstrate that the cavitation erosion mechanism of the TiAlN and AlTiN coatings rely on embrittlement, which can be attributed to fatigue processes causing film rupture and internal decohesion in flake spallation, and thus leading to coating detachment and substrate exposition. At moderate loads, the sliding wear of thin films takes the form of grooving, micro-scratching, micro-ploughing and smearing of the columnar grain top hills. Compared to the SS reference sample, the PVD films exhibit superior resistance to sliding wear and cavitation erosion.

The study presents the effect of annealing process parameters on the microstructure, hardness, and strain-hardening coefficients, that is, the strength coefficient c and the strain-hardening exponent n, of 42CrMo4 steel. Seven selected annealing time–temperature schemes are examined for superior steel formability in cold metal forming conditions. The c and n coefficients are first determined in experimental upsetting of annealed samples and then used in FEM (finite element method) simulations of the upsetting process. The results demonstrate that the strain-hardening coefficients (c and n) depend on the employed annealing scheme. Compared with the as-received sample, the annealing process reduces the true stress and effectively decrease the hardness of 42CrMo4 steel; improves microstructural spheroidization; and, consequently, facilitates deformability of this material. The annealing schemes, relying on heating the material to 750 °C and its subsequent slow cooling, lead to the highest decrease in hardness ranging from 162 to 168 HV. The results obtained with the SEM-EDS (scanning electron microscopy-energy dispersive spectrometer), LOM (light optical microscopy), and XRD (X-ray diffraction) methods lead to the conclusion that the employed heat treatment schemes cause the initial ferritic-pearlitic microstructure to develop granular and semi-lamellar precipitation of cementite enriched with Mo and Cr in the ferrite matrix. In addition, the annealing process affects the growth of α-Fe grains. The highest cold hardening rate, and thus formability, is obtained for the annealing scheme producing the lowest hardness. The results of FEM simulations are positively validated by experimental results. The obtained results are crucial for further numerical simulations and experimental research connected with developing new cold metal forming methods for producing parts made of 42CrMo4 steel.