The paper briefly describes major thermal spray techniques used to spray functionally graded coatings such as atmospheric plasma spraying, high velocity oxy-fuel spraying, suspension and solution precursor plasma spraying, and finally low and high pressure cold gas spray method. The examples of combined spray processes as well as some examples of post spray treatment including laser and high temperature treatments or mechanical one, are described. Then, the solid and liquid feedstocks used to spray and their properties are shortly discussed. The reviewed properties of functional coatings include: (i) mechanical (adhesion, toughness, hardness); (ii) physical (porosity, thermal conductivity and diffusivity, thermal expansion, photo-catalytic activity), and; (iii) bioactivity and simulated body fluid (SBF) corrosion. These properties are useful in present applications of functionally graded coatings as thermal barriers, the bioactive coatings in prostheses, photo-catalytic coatings in water treatment, coatings used in printing industry (anilox and corona rolls). Finally, some of the future possible fields of functional thermal sprayed coatings applications are discussed, e.g., to coat polymer substrates or to use the cheap technology of low pressure cold gas spray method instead of expensive technology of vacuum plasma spraying to obtain bond coatings.

The paper investigates the cavitation erosion (CE) and sliding wear (SW) resistance of cold-sprayed Al/Al₂O₃ and Cu/Al₂O₃ composites and studies them in relation to a set of metallic materials such as aluminium alloy (AlCu4Mg1), pure copper (Cu110), brass (CuZn40Pb2) and stainless steel (AISI 304). The coatings were deposited on stainless steel by low-pressure cold spray (LPCS) using Al (40 wt.%) and Cu (50 wt.%) blended with Al₂O₃ (60 and 50 wt.%, respectively) feedstocks. CE resistance was estimated by the stationary sample method according to the ASTM G32 standard. The SW test was conducted using a ball-on-disc tester with compliance to the ASTM G99 standard. Results obtained for the LPCS coatings show that the Cu/Al₂O₃ coating exhibits a denser structure but lower adhesion and microhardness than Al/Al₂O₃. The Al/Al₂O₃ and Cu/Al₂O₃ resistance to cavitation is lower than for bulk alloys; however, composites present higher sliding wear resistance to that of AlCu4Mg1, CuZn40Pb2 and stainless steel. The CE wear mechanisms of LPCS composites start at the structural discontinuities and non-uniformities. The cavitation erosion degradation mechanism of Al/Al₂O₃ relies on chunk material detachment while that of Cu/Al₂O₃ initiates by alumina removal and continues as layer-like Cu-metallic material removal. CE damage of metal alloys relies on the fatigue-induced removal of deformed material. The SW mechanism of bulk alloys has a dominant adhesive mode. The addition of Al₂O₃ successfully reduces the material loss of LPCS composites but increases the friction coefficient. Coatings’ wear mechanism has an adhesive-abrasive mode. In both CE and SW environment, the behaviour of the cold-sprayed Cu/Al₂O₃ composite is much more promising than that of the Al/Al₂O₃.

Thermally sprayed ceramic coatings are applied for the protection of surfaces that are exposed mainly to wear, high temperatures, and corrosion. In recent years, great interest has been garnered by spray processes with submicrometric and nanometric feedstock materials, due to the refinement of the structure and improved coating properties. This paper compares the microstructure and tribological properties of alumina coatings sprayed using conventional atmospheric plasma spraying (APS), and various methods that use finely grained suspension feedstocks, namely, suspension plasma spraying (SPS) and suspension high-velocity oxy-fuel spraying (S-HVOF). Furthermore, the suspension plasma-sprayed Al₂O₃ coatings have been deposited with radial (SPS) and axial (A-SPS) feedstock injection. The results showed that all suspension-based coatings demonstrated much better wear resistance than the powder-sprayed ones. S-HVOF and axial suspension plasma spraying (A-SPS) allowed for the deposition of the most dense and homogeneous coatings. Dense-structured coatings with low porosity (4 vol.%) and good cohesion to the metallic substrate, containing a high content of α–Al₂O₃ phase (56 vol.%) and a very low wear rate (0.2 ± 0.04 mm³ × 10⁻⁶/(N∙m)), were produced with the S-HVOF method. The wear mechanism of ceramic coatings included the adhesive wear mode supported by the fatigue-induced material delamination. Moreover, the presence of wear debris and tribofilm was confirmed. Finally, the coefficient of friction for the coatings was in the range between 0.44 and 0.68, with the highest values being recorded for APS sprayed coatings.

Thermal barrier coatings (TBC) is one of the most intensively studied of coatings’ applications area. From 1970’s TBC are developed in two independent ways: (i) development in new materials, with lower thermal conductivity, better erosion resistance and better thermal shock resistance or (ii) development in new deposition techniques. On this field besides conventional atmospheric plasma spraying (APS) and almost conventional (because of very common use) EB-PVD method, in the past 20 years two new techniques have been developed, namely suspension plasma spraying (SPS) and solution precursor plasma spraying (SPPS). In this paper only SPS method was described, as well as, new materials, which could be used in industrial applications of TBC. Moreover, the key issues, like suspension preparation, type of suspension injection, interaction between liquid droplets and plasma jet and deposition mechanism were described.

The study aims to elaborate a neural model and algorithm for optimizing hardness and porosity of coatings and thus ensure that they have superior cavitation erosion resistance. Al₂O₃-13 wt% TiO₂ ceramic coatings were deposited onto 316L stainless steel by atmospheric plasma spray (ASP). The coatings were prepared with different values of two spray process parameters: the stand-off distance and torch velocity. Microstructure, porosity and microhardness of the coatings were examined. Cavitation erosion tests were conducted in compliance with the ASTM G32 standard. Artificial neural networks (ANN) were employed to elaborate the model, and the multi-objectives genetic algorithm (MOGA) was used to optimize both properties and cavitation erosion resistance of the coatings. Results were analyzed with MATLAB software by Neural Network Toolbox and Global Optimization Toolbox. The fusion of artificial intelligence methods (ANN + MOGA) is essential for future selection of thermal spray process parameters, especially for the design of ceramic coatings with specified functional properties. Selection of these parameters is a multicriteria decision problem. The proposed method made it possible to find a Pareto front, i.e., trade-offs between several conflicting objectives—maximizing the hardness and cavitation erosion resistance of Al₂O₃-13 wt% TiO₂ coatings and, at the same time, minimizing their porosity.

In present work the Cr₃C₂–NiCr coating was deposited on magnesium alloy substrate with high velocity oxygen fuel (HVOF) spraying. The microstructure of the samples has been characterized by means of electron microscopy, SEM and phase composition analysis carried out. The porosity of coatings has been also estimated. Finally, tests of selected mechanical properties, such as instrumented indentation, abrasive erosion have been performed. The results of the investigations confirmed that dense, homogeneous and well-adhered Cr₃C₂–NiCr cermet coating is possible to obtain onto the magnesium AZ31 alloy substrate. Moreover, the coatings exhibit high resistance to erosion.