Modification of titania with copper is a promising way to enhance the photocatalytic performance of TiO₂. The enhancement means the significant retardation of charge carriers’ recombination ratio and the introduction of visible light activity. This review focuses on two main ways of performance enhancement by copper species—i.e., originated from plasmonic properties of zero-valent copper (plasmonic photocatalysis) and heterojunctions between semiconductors (titania and copper oxides). The photocatalytic performance of copper-modified titania is discussed for oxidative reaction systems due to their importance for prospective applications in environmental purification. The review consists of the correlation between copper species and corresponding variants of photocatalytic mechanisms including novel systems of cascade heterojunctions. The problem of stability of copper species on titania, and the methods of its improvement are also discussed as important factors for future applications. As a new trend in the preparation of copper-modified titania photocatalyst, the role of particle morphology (faceted particles, core-shell structures) is also described. Finally, in the conclusion section, perspectives, challenges and recommendations for future research on copper-modified titania are formulated.

In this study, titania nanoparticles were obtained using the microwave-assisted technique. Moreover, different surfactants (PEG (M_n = 400), Pluronic P123 and Triton X−100) were used during the synthesis in order to determine their impact on the crystallinity and morphology of the final products. Subsequently, techniques such as XRD, SEM and TEM (performed in high contrast and high-resolution mode), diffuse reflectance spectroscopy (DRS), low temperature N₂ sorption (BET model), FTIR and TGA were carried out. Based on the crystallinity analysis of the obtained materials, it was established that the addition of surfactants results in greater (PEG and Triton X−100) or smaller (Pluronic P123) average crystallite size. The main purpose of this study was to use the synthesized nanomaterials in the photodegradation process (in the UV light range) of the model organic pollutants – phenol (20 mg/L) and etodolac (15 mg/L). Furthermore, it was also pointed out that the dye-sensitized solar cells can be a second application for the synthesized titania nanomaterials. The photo-oxidation and photovoltaic tests have shown that the titanium dioxide obtained using the surfactant-assisted microwave method is characterized not only by better photodegradation efficiency of phenol and etodolac, but also by higher photocurrent density compared to the reference titania samples—the pristine TiO₂ and commercial P25.

Pristine and modified/doped titania are still some of the most widely investigated photocatalysts due to its high activity, stability, abundance and proper redox properties to carry out various reactions. However, modifiers and/or dopants resulting in visible-light activity might be expensive or work as recombination centers under UV irradiation. It seems that defective titania, known as “self-doped” TiO₂, might be the best solution since it can be obtained under mild conditions without the addition of expensive materials and methods. This review discusses various methods of defective titania preparation, characterization of defect types, their localization (surface vs. bulk) and their function, as well as proposed mechanisms of photocatalytic reactions in the presence of self-doped titania. Although many kinds of defective titania samples have already been prepared with different colors, color intensities and defect kinds (mainly Ti³⁺ and oxygen vacancies), it is difficult to conclude which of them are the most recommended as the preparation conditions and activity testing used by authors differ. Furthermore, activity testing under solar radiation and for dyes does not clarify the mechanism since bare titania can also be excited and sensitized, respectively, in these conditions. In many reports, authors have not considered the possible influence of some impurities originated from the synthesis method (e.g., H, Al, Zn, Cl, F) that could co-participate in the overall mechanism of photocatalytic reactions. Moreover, some reports indicate that defective titania, especially black ones, might decrease activity since the defects might work as recombination centers. Despite some unproven/unclear findings and unanswered questions, there are many well-conducted studies confirmed by both experimental and theoretical studies that defective titania might be a promising material for various photocatalytic reactions under both UV and visible-light irradiation. Based on available literature, it could be proposed that optimal defects’ concentration, the preferential role of surface defects, a higher surface-to-bulk ratio of defects in rutile than in anatase, and the beneficial impact of disordered surface are the most important aspects to be considered during the preparation of defective titania.