In this study, titania nanoparticles were obtained using the microwave-assisted technique. Moreover, different surfactants (PEG (M_n = 400), Pluronic P123 and Triton X−100) were used during the synthesis in order to determine their impact on the crystallinity and morphology of the final products. Subsequently, techniques such as XRD, SEM and TEM (performed in high contrast and high-resolution mode), diffuse reflectance spectroscopy (DRS), low temperature N₂ sorption (BET model), FTIR and TGA were carried out. Based on the crystallinity analysis of the obtained materials, it was established that the addition of surfactants results in greater (PEG and Triton X−100) or smaller (Pluronic P123) average crystallite size. The main purpose of this study was to use the synthesized nanomaterials in the photodegradation process (in the UV light range) of the model organic pollutants – phenol (20 mg/L) and etodolac (15 mg/L). Furthermore, it was also pointed out that the dye-sensitized solar cells can be a second application for the synthesized titania nanomaterials. The photo-oxidation and photovoltaic tests have shown that the titanium dioxide obtained using the surfactant-assisted microwave method is characterized not only by better photodegradation efficiency of phenol and etodolac, but also by higher photocurrent density compared to the reference titania samples—the pristine TiO₂ and commercial P25.

The main goal of the study was the hydrothermal-assisted synthesis of TiO₂-ZnO systems and their subsequent use in photoactive processes. Additionally, an important objective was to propose a method for synthesizing TiO₂-ZnO systems enabling the control of crystallinity and morphology through epitaxial growth of ZnO nanowires. Based on the results of X-ray diffraction analysis, in the case of materials containing a small addition of ZnO (≥5 wt.%), no crystalline phase of wurtzite was observed, proving that a high amount of modified titanium dioxide can inhibit the crystallization of ZnO. The transmission electron microscopy (TEM) results confirmed the formation of ZnO nanowires for systems containing ≥ 5% ZnO. Moreover, for the synthesized systems, there were no significant changes in the band gap energy. One of the primary purposes of this study was to test the TiO₂-ZnO system in the photodegradation process of 4-chlorophenol using low-power UV-LED lamps. The results of photo-oxidation studies showed that the obtained binary systems exhibit good photodegradation and mineralization efficiency. Additionally, it was also pointed out that the dye-sensitized solar cells can be a second application for the synthesized TiO₂-ZnO binary systems.

TiO₂-MoO₃ composite systems were successfully prepared using a template-assisted microwave method at molar ratios TiO₂:MoO₃ = 8:2, 5:5 and 2:8. The synthesized material systems were comprehensively characterized, in terms of their crystalline structure (XRD and Raman spectroscopy), morphology (SEM, TEM and HRTEM analysis) and parameters of the porous structure (low-temperature N₂ sorption). The materials exhibited highly crystalline phases: anatase and hexagonal molybdenum trioxide. Moreover, TEM analysis revealed hexagonal prism particles of MoO₃ and nanocrystalline particles of TiO₂. The proposed template-assisted microwave synthesis enabled the incorporation of TiO₂ particles on the surface of hexagonal particles of MoO₃, which resulted in a stable junction between titania and molybdenum trioxide. The values of BET surface area were 57, 29 and 11 m²/g for samples obtained at molar ratios TiO₂:MoO₃ = 8:2, 5:5 and 2:8 respectively. In electrochemical applications, titanium dioxide plays a crucial role as an intercalation intensifier, in which MoO₃ is responsible for current conduction. Taking account of the potential electrochemical applications, the best system was obtained at the molar ratio TiO₂:MoO₃ = 5:5. The anode could maintain a capacity of 400 mAh/g at current densities in the range 100–1000 mA/g at potential values ranging from 1.00 to 3.30 V vs. Li/Li⁺. X-ray photoelectron spectroscopy (XPS) confirmed the effective intercalation of lithium ions into the TiO₂-MoO₃ composite materials.

The TiO₂-Fe₃O₄ composite materials were fabricated via the hydrothermal-assisted technique. It was determined how the molar ratio of TiO₂ to Fe₃O₄ influences the crystalline structure and morphology of the synthesized composite materials. The effect of the molar ratio of components on the antibacterial activity was also analyzed. On the basis of XRD patterns for the obtained titanium(IV) oxide-iron(II, III) oxide composites, the two separate crystalline forms—anatase and magnetite —were observed. Transmission electron microscopy revealed particles of cubic and tetragonal shape for TiO₂ and spherical for Fe₃O₄. The results of low-temperature nitrogen sorption analysis indicated that an increase in the iron(II, III) oxide content leads to a decrease in the BET surface area. Moreover, the superparamagnetic properties of titanium(IV) oxide-iron(II, III) oxide composites should be noted. An important aim of the work was to determine the antibacterial activity of selected TiO₂-Fe₃O₄ materials. For this purpose, two representative strains of bacteria, the Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus, were used. The titanium(IV) oxide-iron(II, III) oxide composites demonstrated a large zone of growth inhibition for both Gram-positive and Gram-negative bacteria. Moreover, it was found that the analyzed materials can be reused as antibacterial agents in three consecutive cycles with good results.

Background: The injection of Neb-colloostatin into T. molitor females causes gonadoinhibitory effects on ovarian development. This peptide inhibits intercellular space formation (patency) in follicular epithelium and results in slowed vitellogenesis, delayed ovulation, reduced number of eggs laid and presumably cell death in the terminal follicles. However, as does the form of cell death in the terminal follicle, the mode of action of Neb-colloostatin remains unknown. Results: We tested Neb-colloostatin for a sterilizing effect on females of Tenebrio molitor. We report that injection of nanomolar doses of Neb-colloostatin induce ovarian follicle atresia in 4-day old females during their first gonadotropic cycle. Light microscope observations revealed morphological changes in the ovary: after Neb-colloostatin injection the terminal oocytes are significantly smaller and elicit massive follicle resorption, but the control terminal follicles possess translucent ooplasm in oocytes at different stages of vitellogenesis. A patency is visible in follicular epithelium of the control vitellogenic oocytes, whereas peptide injection inhibits intercellular space formation and, in consequence, inhibits vitellogenesis. Confocal and electron microscope examination showed that peptide injection causes changes in the morphology indicating death of follicular cells. We observed F-actin cytoskeleton disorganization, induction of caspase activity, changes in chromatin organization and autophagic vacuole formation. Moreover, the apical cytoplasm of follicular cells is filled with numerous free ribosomes, probably indicating a higher demand for protein biosynthesis, especially in preparation for autophagic vacuole formation. On the other hand, the process of polyribosomes formation is inhibited, indicating the contributing effect of this hormone. Conclusion: Neb-colloostatin induces atresia in the mealworm ovary. Degeneration of T. molitor follicles includes changes in morphology and viability of follicular cells, and oosorption as a consequence of these changes.