Synthesis of Eu3+- and Er3+/Yb3+-doped GdVO4 nanoparticles in reverse micelles and their multifunctional luminescence properties are presented. Using cyclohexane, Triton X-100, and n-pentanol as the oil, surfactant, and co-surfactant, respectively, crystalline nanoparticles with ~4 nm diameter are prepared at low temperatures. The particle size assessed using transmission electron microscopy is similar to the crystallite size obtained from X-ray diffraction measurements, suggesting that each particle comprises a single crystallite. Eu3+-doped GdVO4 nanoparticles emit red light through downconversion upon UV excitation. Er3+/Yb3+-doped GdVO4 nanoparticles exhibit several functions; apart from the downconversion of UV radiation into visible green light, they act as upconvertors, transforming near-infrared excitation (980 nm) into visible green light. The ratio of green emissions from 2H11/2 → 2I15/2 and 4S3/2 → 4I15/2 transitions is temperature dependent and can be used for nanoscale temperature sensing with near-infrared excitation. The relative sensor sensitivity is 1.11%K−1, which is among the highest sensitivities recorded for upconversion-luminescence-based thermometers.

The spectroscopic properties of different infrared-emitting neodymium-doped nanoparticles (LaF3:Nd3+, SrF2:Nd3+, NaGdF4: Nd3+, NaYF4: Nd3+, KYF4: Nd3+, GdVO4: Nd3+, and Nd:YAG) have been systematically analyzed. A comparison of the spectral shapes of both emission and absorption spectra is presented, from which the relevant role played by the host matrix is evidenced. The lack of a “universal” optimum system for infrared bioimaging is discussed, as the specific bioimaging application and the experimental setup for infrared imaging determine the neodymium-doped nanoparticle to be preferentially used in each case.

${\mathrm{Eu}}^{3+}$- and ${\mathrm{Dy}}^{3+}$-doped ${\mathrm{GdVO}}_4$ samples synthesized by a high-temperature solid-state method are investigated by fluorescence spectroscopy at 298–750 K. They demonstrate potential for development as thermographic phosphors because the experimental and theoretical temperature dependence of the intensity ratio of the two lines agrees well. Experimental lifetime measurements recorded at 10–750 K were fitted using three theoretical models: multiphonon relaxation, temperature quenching through the charge transfer (CT) region, and our modified CT model (TDCT), which considers the temperature dependence of CT energy. The TDCT model yields the best results with good agreement between experimental and fitted lifetime data.