New composites made of natural fiber polymers such as wasted date palm surface fiber (DPSF) and pineapple leaf fibers (PALFs) are developed in an attempt to lower the environmental impact worldwide and, at the same time, produce eco-friendly insulation materials. Composite samples of different compositions are obtained using wood adhesive as a binder. Seven samples are prepared: two for the loose natural polymers of PALF and DPSF, two for the composites bound by single materials of PALF and DPSF using wood adhesive as a binder, and three composites of both materials and the binder with different compositions. Sound absorption coefficients (SACs) are obtained for bound and hybrid composite samples for a wide range of frequencies. Flexural moment tests are determined for these composites. A thermogravimetric analysis test (TGA) and the moisture content are obtained for the natural polymers and composites. The results show that the average range of thermal conductivity coefficient is 0.042–0.06 W/(m K), 0.052–0.075 W/(m K), and 0.054–0.07 W/(m K) for the loose fiber polymers, bound composites, and hybrid composites, respectively. The bound composites of DPSF have a very good sound absorption coefficient (>0.5) for almost all frequencies greater than 300 Hz, followed by the hybrid composite ones for frequencies greater than 1000 Hz (SAC > 0.5). The loose fiber polymers of PALF are thermally stable up to 218 °C. Most bound and hybrid composites have a good flexure modulus (6.47–64.16 MPa) and flexure stress (0.43–1.67 Mpa). The loose fiber polymers and bound and hybrid composites have a low moisture content below 4%. These characteristics of the newly developed sustainable and biodegradable fiber polymers and their composites are considered promising thermal insulation and sound absorption materials in replacing synthetic and petrochemical insulation materials in buildings and other engineering applications.

Pineapple leaf fiber (PALF), striped sunflower seed fiber (SFSF), and watermelon seed (WMS) are considered natural waste polymer materials, which are biodegradable and sustainable. This study presents new novel thermal insulation and sound absorption materials using such waste as raw materials. PALF, SFSF, and WMS were used as loose, bound, and hybrid samples with different compositions to develop promising thermal insulation and sound-absorbing materials. Eleven sample boards were prepared: three were loose, three were bound, and five were hybrid between PALF with either SFSF or WMS. Wood adhesive was used as a binder for both the bound and hybrid sample boards. Laboratory scale sample boards of size 30 cm × 30 cm with variable thicknesses were prepared. The results show that the average thermal conductivity coefficient for the loose samples at the temperature range 20–80 °C is 0.04694 W/(m.K), 0.05611 W/(m.K), and 0.05976 W/m.K for PALF, SFSF, and WMS, respectively. Those for bound sample boards are 0.06344 W/(m.K), 0.07113 W/(m.K), and 0.08344 W/m.K for PALF, SFSF, and WMS, respectively. The hybrid ones between PALF and SFSF have 0.05921 W/m.K and 0.06845 W/(m.K) for two different compositions. The other hybrid between PALF and WMS has 0.06577 W/(m.K) and 0.07007 for two different compassions. The sound absorption coefficient for most of the bound and hybrid boards is above 0.5 and reaches higher values at some different frequencies. The thermogravimetric analysis for both SFSF and WMS shows that they are thermally stable up to 261 °C and 270 °C, respectively. The three-point bending moment test was also performed to test the mechanical properties of the bound and hybrid sample boards. It should be mentioned that using such waste materials as new sources of thermal insulation and sound absorption materials in buildings and other applications would lead the world to utilize the waste until zero agrowaste is reached, which will lower the environmental impact.

The effect of tilt angle on free convection heat transfer is investigated experimentally inside a rectangular parallelepiped cavity filled with water. The cavity had the dimensions S × S × H (m³), where S was the inside length, and H was the inside height of the cavity. The lower surface was subject to constant heat flux, and the upper surface was cooled by a stream of ambient air. The free convection heat transfer data were generated using different uniform heat fluxes. Four tilt angles were considered: $0°, 30°, 60°, \mathrm{and} 90°$. The surface temperature measurements were collected 10 h after the experimental run to ensure that a steady-state was reached. It was noticeable that the free convection heat transfer strongly depended on the tilt angle and the modified Rayleigh numbers. The 3D results showed that the Nusselt number reached a maximum at 60° at a fixed modified Rayleigh number. An enhancement in the Nusselt number at any tilt angle was observed over that of a zero tilt angle, and the percent of enhancement was 7.92–62.38%, depending on the modified Rayleigh numbers and the tilt angle. It was also observed that as the modified Rayleigh number increased, the temperature uniformity on both the hot and cold surfaces was disturbed. Furthermore, an empirical correlation between the modified Rayleigh numbers and Nusselt numbers was obtained for each angle. Moreover, two overall general correlations are obtained to cover the four tilt angles (i.e., 0°, 30°, 60°, and 90°) and the modified Rayleigh numbers, which should be helpful for engineering applications.

A tremendous amount of waste black tea bags (BTBs) and date palm surface fibers (DPSFs), at the end of their life cycle, end up in landfills, leading to increased pollution and an increase in the negative impact on the environment. Therefore, this study aims to utilize these normally wasted materials efficiently by developing new composite materials for thermal insulation and sound absorption. Five insulation composite boards were developed, two were bound (BTB or DPSF with polyvinyl Acetate resin (PVA)) and three were hybrids (BTB, DPSF, and resin). In addition, the loose raw waste materials (BTB and DPSF) were tested separately with no binder. Thermal conductivity and sound absorption coefficients were determined for all boards. Thermal stability analysis was reported for the components of the tea bag (string, label, and bag) and one of the composite hybrid boards. Mechanical properties of the boards such as flexural strain, flexural stress, and flexural elastic modulus were determined for the bound and hybrid composites. The results showed that the thermal conductivity coefficients for all the hybrid composite sample boards are less than 0.07 at the ambient temperature of 24 °C and they were enhanced as the BTB ratio was reduced in the hybrid composite boards. The noise reduction coefficient for bound and all hybrid composite samples is greater than 0.37. The composite samples are thermally stable up to 291 °C. Most composite samples have a high flexure modulus between 4.3 MPa and 10.5 MPa. The tea bag raw materials and the composite samples have a low moisture content below 2.25%. These output results seem promising and encouraging using such developed sample boards as eco-friendly thermal insulation and sound absorption and competing with the synthetic ones developed from petrochemicals in building insulation. Moreover, returning these waste materials to circulation and producing new eco-friendly composites can reduce the number of landfills, the level of environmental pollution, and the use of synthetic materials made from fossil resources.

This experimental study provides a comprehensive investigation of natural convection heat transfer inside shallow square cuboid enclosures filled with aluminum oxide–water nanofluid at four different volume concentrations: 0.0%, 0.2%, 0.4%, and 0.8%. Two square cuboid enclosures were used with sizes 30 × 30 × H cm³, where H is the inside thickness of the enclosures. This led to two different enclosure aspect ratios (κ = H/30 = 0.033 and 0.066). Four inclination angles to the horizontal position of the enclosures were used: 0°, 30°, 60°, and 90°. The crucial thermophysical properties of the synthetic nanofluid were obtained. The thermal conductivity of the nanofluid was measured experimentally at various volume concentrations. Furthermore, the viscosity and density were also measured experimentally at temperatures ranging from 15 to 40 °C as a function of the volume concentration. The heat transfer data were generated by heating the lower surface of the enclosure using a uniform flexible heat flux heater. The opposite surface was cooled using an air fan. The results of the experimental physical parameter measurements show that the percent of maximum deviation in thermal conductivity with those in the literature were 6.61% at a 1.0% volume concentration. The deviation of dynamic viscosity was between 0.21% and 16.36% at 0.1% and 1% volume concentrations, respectively, and for density it was 0.29% at 40 °C and a 1% volume concentration. The results showed up to a 27% enhancement in the Nusselt number at an angle of 60° and a 0.4% volume concentration in the largest aspect ratio (κ = 0.066). However, for the low aspect ratio enclosure (κ = 0.033), there was no noticeable improvement in heat transfer at any combination of volume concentration and inclination angle. The results show that the inclination angle is a significant factor in natural convection only for large aspect ratio enclosures. Furthermore, for large aspect ratio, the Nusselt number increased until the angle approached 60°, then it decreased again.